FORD WSS-M1H868-A-2003 FABRIC SOLE PATTERN KNIT TO BE USED WITH FORD WSS-M99P1111-A 《SOLE图案的针织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 04 16 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.11, 3.12, 4 deleted 2001 08 08 Activated M. Dumitrescu Printed copies are uncontrolled Page 1 of 3 Copyright 2003, Ford Global Technologies, Inc. F

2、ABRIC, SOLE PATTERN, KNIT WSS-M1H868-A 1. SCOPE The material defined by this specification is a Double Needle Bar Sole pattern knit body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for the 2003

3、Tribute High Series seat insert. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. Material specification requirements are to be used for initial qualification of materials. 3.0 STANDARD REQUIREMENTS FOR PRODUCTIO

4、N MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5 % tolerance (ASTM D 3887) Wales 98.4 wales/10 cm Courses 138.0 courses/10 cm 3.4.2 Fabric Weight, range, g

5、/m2(FLTM BN 106-01) Laminated* Face w/no Backcoat 533 - 652 418 - 510 *At 3 mm foam thickness ENGINEERING MATERIAL SPECIFICATION WSS-M1H868-A Page 2 of 3 Copyright 2003, Ford Global Technologies, Inc. 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100 % Polyester 3.6 Y

6、ARN CONSTRUCTION (ASTM D 1244) Face A. 16.7 tex f50 (2 ply Bright/dull Polyester) B. 11.1 tex f100 (2 ply dull Polyester) Middle Face 11.1 tex f34 (solution dyed Polyester) Back 11.1 tex f34 (solution dyed Polyester) 3.7 METHOD OF DYEING Piece Dye/ Solution dye 3.8 FINISHING OPERATIONS Knit, Slit, D

7、ye, Dry, Heatset, Inspect 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. ENGINEERING MATERIAL SPECIFICATION WSS-M1H868-A Page 3 of 3 Copyright 2003, Ford Global Technologies, Inc. 3.10 STRETCH & SET, %, range

8、 (SAE J855) Fabrics outside this range may be accepted provided they have been approved jointly by the Materials Engineering activity and the affected Design Engineering and Development activity. Wales Courses Stretch, range 6 - 30 10 - 35 Set, max* 12 14 * At no time shall the set exceed 40 % of th

9、e measured stretch unless approved jointly by the Materials Engineering activity and the affected Design Engineering and Development activity. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.