1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2004 08 25 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 1 of 2 FABRIC, CAPTAIN II PATTERN, DOBBY WOVEN WSS-M1H874-B 1. SCOPE The material defined by this specification is a CAPTAIN
2、II pattern, flat Dobby woven bodycloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an insert of seat fabric for the 2004 Explorer Sport Track and 2004 Escape 3. REQUIREMENTS In addition to the requirements listed herein, the
3、 fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance
4、 (ASTM D 3775) Warp 165 ends/10 cm Fill 137 picks/10 cm 3.2.2 Fabric Weight, range (FLTM BN 106-01) Face Fabric w/ backcoat 361 - 400 g/m2Laminated to 3mm foam 515 - 570 g/m23.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 52% Polyester 48% Polyvinyl Chloride Backcoatin
5、g 25.4 g/m2Ethylene Vinyl Acetate ENGINEERING MATERIAL SPECIFICATIONWSS-M1H874-B Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp A. 33.3 tex f136 (polyester, air textured, semi-dull, package dyed) x 2 Fill W 359 tex (
6、55.6 tex polyester core coated with black solution dyed polyvinyl chloride) X 33.3 tex f136 (polyester, air textured, semi-dull package dyed) x 2 Y 243 tex (55.6 tex polyester core coated with black solution dyed polyvinyl chloride) 3.5 METHOD OF DYEING Package Dyed/ Solution Dyed 3.6 FINISHING OPERATIONS Wash, Dry, Backcoat, Inspect