FORD WSS-M1H891-A-2008 FABRIC BRICK PATTERN WARP KNIT TO BE USED WITH FORD WSS-M99P1111-A 《砖块（Brick）图案的经编针织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 12 17 N-STATUS No Replacement B. Haggart, FNA 2003 04 22 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.9, 4 deleted 2002 04 22 Activated M. DumitrescuPrinted copies are uncontrolled Page 1 of 2 Copyr

2、ight 2008, Ford Global Technologies, Inc. FABRIC, BRICK PATTERN, WARP KNIT WSS-M1H891-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a BRICK PATTERN, a 28 Gauge, TRICOT knit, body cloth of good quality and uniform composition. 2. APPLICATION This specification

3、 was released originally for material used as an interior trim fabric for 2004 XL/XLT/EDGE Ranger seat insert. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS M

4、aterial suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5 % tolerance (ASTM D 3887) Wales 132 wales/10 cm Courses 146 courses/ 10 cm 3.4.2 Fabric Weight, range, g/m2 (FLTM BN 10

5、6-01) Laminated * Face w/Backcoat 557 - 614 444-489 * 3 mm foam thickness ENGINEERING MATERIAL SPECIFICATION WSS-M1H891-A Page 2 of 2 Copyright 2008, Ford Global Technologies, Inc. 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoat Acrylic 3.6 YARN CONSTRUCTION (ASTM D 1244) Face Middle Face 16.7 tex f34 (Sol dye Polyester) Middle Back 16.7 tex f34 (Sol dye Polyester) Back 16.7 tex f50 (Natural Polyester) 3.7 METHOD OF DYEING Piece Dye 3.8 FINISHING OPERATIONS Knit, Setmake, Dye, Backcoat, Heat set Inspect