FORD WSS-M1H901-A-2008 FABRIC LOGAN PATTERN WARP KNIT TO BE USED WITH FORD WSS-M99P1111-A 《LOGAN图案的经编针织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 02 06 N-STATUS No replacement named M. Dumitrescu 2003 04 22 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.9, 4 deleted 2002 05 10 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Pa

2、ge 1 of 2 FABRIC, LOGAN PATTERN, WARP KNIT WSS-M1H901-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a single Raschel 56 Gauge warp knitted, LOGAN PATTERN, polyester bodycloth of good quality and uniform composition 2. APPLICATION This specification was releas

3、ed originally for material used as an interior trim fabric for 2003 V229 WINDSTAR seat insert. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material supplier

4、s and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 161.4 wales/10 cm Courses 244 courses/10 cm 3.4.2 Fabric Weight, range, g/m2(FLTM BN 106-01) Face w/Back

5、coat 397 - 471 Laminated to 3 mm foam 472 - 576 ENGINEERING MATERIAL SPECIFICATIONWSS-M1H901-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 71% Polyester, 29% Polypropylene Backcoat Acrylic 3.6 YARN CONSTRUCTION (ASTM D 1244) Face 29% 16.7tex f36 (Polypropylene) Middle 47% 7.8 texf34 (Semi Dull Polyester) Back 24% 7.8tex f34 (Dull Polyester) 3.7 METHOD OF DYEING Piece Dye/Solution Dye 3.8 FINISHING OPERATIONS Knit, Dye, Dry, Nap, Heat set, Inspect