FORD WSS-M1H934-A-2003 FABRIC CUBICLE PATTERN PILE KNITTED UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A 《CUBICLE图案的不分层长毛绒针织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 10 09 Activated N. J. Komatsu Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 2 FABRIC, CUBICLE PATTERN, PILE KNITTED, WSS-M1H934-A UNLAMINATED 1. SCOPE The material defined by this specification i

2、s a 4 bar 28 gauge warp knitted, simulated velour, polyester bodycloth. 2. APPLICATION This specification was released originally for material used for as an interior trim fabric for 2003 Model Year. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirement

3、s of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, range (ASTM D 3887) Wales 144 w

4、ales/10 cm Courses 190 courses/10 cm 3.2.2 Fabric Weight, range 247 - 303 g/m2(FLTM BN 106-01) 3.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 110 dtex f47 (polyester, false twist) Middle & Back 76 dtex 24 (polyester, flat) ENGINEERING MATERIAL SPECIFICATI

5、ONWSS-M1H934-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 2 3.5 METHOD OF DYEING Piece dyed or as approved by Materials Engineering 3.6 FINISHING OPERATIONS As approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.