1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 03 18 Revised Yarn construction para 3.4 revised to show resultant thickness N. J. Komatsu2004 07 13 Activated N. J. Komatsu Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 FABRIC, FLOE PATTERN, W
2、OVEN JACQUARD, WSS-M1H952-A UNLAMINATED 1. SCOPE The material defined by this specification is a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for use in the 2006 Model Year. 3. REQUIREMENTS In addition to
3、 the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 F
4、ABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10% tolerance (ASTM D 3775) Warp 250 ends/10 cm Weft 140 picks/10 cm 3.2.2 Fabric Weight, +/- 15% tolerance (FLTM BN 106-01) 365 g/m23.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 589-651 dtex f137-152 (air textu
5、rized, Semi-dull) ENGINEERING MATERIAL SPECIFICATIONWSS-M1H952-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 Weft 684-756 dtex f186-196 (air texturized, bright) 1092-1270 dtex f260-288 (air texturized, bright) 3.5 METHOD OF DYEING Yarn dyed or as approved
6、 by Materials Engineering 3.6 FINISHED OPERATIONS As approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.