1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 12 09 N-STATUS No Replacement L. Schmalz, FNA / M. Montgomery, FOE2005 02 10 Activated N. J. Komatsu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, LAPAZA, WOVEN JACQUARD, WSS-M1H975-A UN
2、LAMINATED NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for the 2006 Model Year. 3. REQUIREMENTS In addition to the re
3、quirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC C
4、ONSTRUCTION 3.2.1 Fabric Count, +/- 10% tolerance (ASTM D 3775) Warp 360 ends/10 cm Weft 160 picks/10 cm 3.2.2 Fabric Weight, range. (FLTM BN 106-01) 275 g/m23.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 370 dtex f68 (false twist, round, semi-dull) Weft
5、540 dtex f144, (round air texturized, semi-dull) ENGINEERING MATERIAL SPECIFICATIONWSS-M1H975-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF DYEING Yarn dyed or as approved by Materials Engineering 3.6 FINISHING OPERATIONS As approved by Mat
6、erials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.