1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 07 19 Activated N. J. Komatsu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, SEED PATTERN, WOVEN JACQUARD, UNLAMINATED WSS-M1H999-A 1. SCOPE The material defined by this specification is
2、a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for use in the 2006 Model Year. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. In addition to the
3、 requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRI
4、C CONSTRUCTION 3.2.1 Fabric Count, +/- 10% tolerance (ASTM D 3775) Warp 240 ends/10 cm Weft 180 picks/10 cm 3.2.2 Fabric Weight, range 325 - 365 g/m23.3 METHOD OF DYEING Yarn dyed or as approved by (FLTM BN 106-01) Materials Engineering 3.4 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.5 YARN CON
5、STRUCTION (ASTM D 1244) Warp 660 dtex f 141 (air texturized, semi-dull) Weft 825 dtex f188 (air texturized, semi-dull) ENGINEERING MATERIAL SPECIFICATIONWSS-M1H999-APrinted copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.6 METHOD OF DYEING Yarn dyed or as approved
6、 by Materials Engineering 3.7 FINISHED OPERATIONS As approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.