FORD WSS-M2D505-A6-2003 THERMOPLASTIC ELASTOMER POLYOLEFIN EP RUBBER MODIFIED (TEO) 55 DUROMETER D HARDNESS EXTERIOR APPLICATIONS TO BE USED WITH FORD WSS-M99P1111-A 《汽车外部用硬度为55 .pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 12 15 Activated B HennesseyPrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 3 THERMOPLASTIC ELASTOMER, POLYOLEFIN EP RUBBER WSS-M2D505-A6 MODIFIED (TEO), 55 DUROMETER D HARDNESS, EXTERIOR APPLICATIO

2、NS 1. SCOPE The material defined by this specification is a U.V. stabilized thermoplastic polyolefin EPDM rubber modified (TEO). The material can be processed by conventional thermoplastic molding techniques such as injection and/or extrusion molding. 2. APPLICATION The specification was released or

3、iginally for material used for roof profile skin. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 DYNAMIC MECHANICAL ANALYSIS (ASTM D 4065) Ford

4、Motor Company, at its option, may establish shear modulus/damping vs. temperature curves plotted for - 50 to + 170 C temperature range for material/parts supplied to this specification. The shear modulus and damping curves established for initial approval shall constitute the reference standard and

5、shall be kept on file at the designated material laboratory. All samples shall produce shear modulus and damping curves that correspond to the reference standard when tested under the same conditions. 3.3 MATERIAL TESTING 3.3.1 Preparation of Test Specimens Whenever possible, all test specimens shal

6、l be die-cut from the finished parts. When not feasible, molded specimens are manufactured from the same material and with equivalent cure to the molded parts are recommended. The molded specimens respect the dimensions required by the specific test. 3.4 ORIGINAL PROPERTIES 3.4.1 Density, +/- 0.05 g

7、/cm30.9 (ISO 1183, Method A) ENGINEERING MATERIAL SPECIFICATIONWSS-M2D505-A6Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 3 3.4.2 Hardness, Durometer A 54 +/- 5 points (ISO 868, 15 second dwell) 3.4.3 Tensile Strength, MPa, min (ISO 527, type 2/ 50 mm/min)

8、molded specimen I. Parallel to Flow 20 3.4.3.1 Elongation at Break, min (Test method according to para 3.4.3) I. Parallel to Flow 30% 3.4.4 Tear Strength, min (ISO 34, specimen angular type) injected specimens 3.4.4.1 Parallel to Flow 130 kN/m 3.4.5 Brittleness Point, max - 40 C (ISO 812, Type B spe

9、cimen/ ASTM D 2137, Method A) 3.4.6 Ozone Resistance, max 0 Rating (FLTM BP 101-01, Procedure A) 3.4.7 Migration Staining Rating 4 (FLTM BN 103-01, ISO 105-A02/ AATCC Evaluation Procedure 2) 3.5 HEAT AGING (ISO 188, 150 +/- 50 air change/h, 1000 h at 125 +/- 2 C) 3.5.1 Hardness Change, +/- 5 3.5.2 T

10、ensile Strength Change, max - 30% 3.5.3 Elongation Change, max - 30% 3.5.4 Visual Evaluation No surface tackiness or cracks when folded flat against self. 3.6 FLAMMABILITY (ISO 3795) Burn Rate, max 100 mm/minute ENGINEERING MATERIAL SPECIFICATIONWSS-M2D505-A6Printed copies are uncontrolled Copyright

11、 2003, Ford Global Technologies, Inc. Page 3 of 3 3.7 WEATHERING RESISTANCE After exposure in accordance with 3.7.1, 3.7.2 and 3.7.3 the material shall show no color change in excess of specified Gray Scale rating (AATCC Evaluation Procedure 1/ ISO 105-A02). In addition, there shall be no cracking,

12、crazing or other deterioration. A slight loss of gloss or chalking will be allowed provided an acceptable appearance can be achieved by washing and/or polishing with Ford car polish (auto wax) after the outdoor exposure, by permission of the affected Product Development Materials Activity. All initi

13、al approval will be based on the preliminary Weatherometer exposure, pending Florida and Arizona exposure results for final approval. 3.7.1 Xenon Arc Weatherometer Exterior Rating 4 (SAE J1960, 2500 kJ/m2exposure minimum, specimen size: 60 x 60 minimum x 2.0 +/- 0.1 mm thick, smooth surface, low glo

14、ss injection molded specimen) 3.7.2 Weathering Rating 4 12 months Florida 12 months Arizona Exterior (SAE J1976, 5 south, direct weathering inland, specimen size: 60 x 60 minimum x 2.0 +/- 0.1 mm thick, smooth surface, low gloss injection molded specimen) 3.7.3 Weathering Rating 3-4 24 months Florid

15、a 24 months Arizona Exterior (SAE J1976, 5 south, direct weathering inland, specimen size: 60 x 60 minimum x 2.0 +/- 0.1 mm thick, smooth surface, low gloss injection molded specimen) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 RECYCLING CODE TEO