1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2004 04 23 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 1 of 2 VINYL, FILM, EDGE BINDING GRADE WSS-M2F199-A 1. SCOPE The material defined by this specification is a vinyl or vinyl c

2、opolymer unsupported film. 2. APPLICATION This specification was released originally for material used as sewn edge binding for C170 Security Shade 3. REQUIREMENTS In addition to the requirements listed herein, the vinyl film shall meet the requirements of WSS-M8P3-D1. 3.1 STANDARD REQUIREMENTS FOR

3、PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A) 3.2 APPEARANCE (FLTM BI 109-01) The color, pattern, gloss level and finish shall match the approved Corporate Design master sample, or shall be as s

4、pecified on engineering drawing. 3.3 DIMENSIONS (ASTM D 374, Method C) Thickness, mm 0.69 - 0.94 3.4 WEIGHT, g/m2, +/- 10% 705 (ASTM D 751) 3.5 BREAKING STRENGTH, MPa, min 6.0 (ISO 37, type 1 dumb-bell/ASTM D 412, Method A, Die C) 3.6 RESISTANCE TO TEAR, N/mm, min 26 (ASTM D 1004, Method B, Procedur

5、e Al) 3.7 DIMENSIONAL STABILITY, max change (SAE J883) Room Temperature +/- 3% MD, AMD Oven Aged +/- 3% MD, AMD ENGINEERING MATERIAL SPECIFICATIONWSS-M2F199-A Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 2 of 2 3.8 STRETCH AND SET, % RANGE Stretch Set (SAE J855) MD 50 8 AMD 60 5 3.9 FLAMMABILITY, max 100 mm/minute (ISO 3795/SAE J369) 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 RECYCLING CODE PVC