FORD WSS-M2F210-A2-2012 FABRIC VINYL (PVC) COATED POLYESTER BACKED FLOOR MAT BINDING TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions Rev. 0 2012 06 25 Activated New specification L. Sinclair, NAControlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, VINYL (PVC) COATED, POLYESTER BACKED, WSS-M2F210-A2 FLOOR MAT BINDING 1. SCOPE The m

2、aterial defined by this specification is a polyester based fabric of uniform construction. 2. APPLICATION This specification was released originally for floor mat binding. 3. REQUIREMENTS In addition to the requirements listed herein, the material must also meet the requirements of WSS-M8P24-A/ Late

3、st, Performance, Floor Mat Edging. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Materials used in interior applications must meet the requirements outlined

4、in WSSM99P2222-C1/Latest, Performance, Vehicle Interior Environment Quality Material/Component Requirements. Data must be included in material submission package. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Warp 15 yarn/cm Fill 13 yarn/cm 3.2.2 Weight, +/- 10% toleranc

5、e (FLTM BN 106-01) Fabric 60 +/- 5 g/m2Coating 300 +/- 30 g/m2Total 360 +/- 35 g/m23.2.3 Thickness 0.55 +/- 15 mm 3.3 COMPOSITION (ASTM D 629) Fabric 100% Polyester Coating 100% PVC ENGINEERING MATERIAL SPECIFICATIONWSS-M2F210-A2 Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CON

6、STRUCTION (ASTM D 1244) Warp 100% spun polyester, 76x36 dtex Fill 100% spun polyester, 76x36 dtex 3.5 METHOD OF DYING Solution 4. GENERAL INFORMATION This information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions co

7、ncerning Engineering Material Specifications. 4.1 PHYSICAL PROPERTIES 4.4.1 Tensile Strength (ISO 1421) Warp 33 daN/5 cm Fill 30 daN/5 cm 4.4.2 Elongation (ISO 1421) Warp 124 % Fill 115% 4.4.3 Tear Strength (ISO 4674) Warp 1.0 daN Fill 0.8 daN 4.4.4 Stretch and Set (SAE J855) Warp 35 % Fill 30 % 4.4.5 Adhesion (PVC to Fabric) 7.5 daN/5 cm (ISO 2411) 5. SUMMARY OF REVISIONS