FORD WSS-M3H105-A11-2002 CARPET POLYESTER FLAT NEEDLED HEAT ACTIVATED WITH POLYETHYLENE BACKING TO BE USED WITH FORD WSS-M99P1111-A 《聚乙烯背衬的热活化型扁平针刺聚酯地毯 与标准FORD WSS-M99P1111-A一起使.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2002 12 05 Revised Rev para 3.6.2 L. Soreide 2002 10 31 Activated L. Soreide Printed copies are uncontrolled Page 1 of 2 Copyright 2002, Ford Global Technologies, Inc. CARPET, POLYESTER, FLAT NEEDLED, WSS-M3

2、H105-A11 HEAT ACTIVATED WITH POLYETHYLENE BACKING 1. SCOPE The materials defined by this specification are flat needled, polyester, non-woven carpets of good quality and uniform composition. The face fiber is 100 % recycled post consumer polyester. Heat activated binder polyester with polyethylene e

3、xtrusion forms the backing. 2. APPLICATION This specification was originally released for material used as trunk covering material for the 2000 Focus C-170. 3. REQUIREMENTS In addition to the requirements listed herein, the end-item carpet assembly (molded or otherwise fabricated), shall meet all re

4、quirements of the WSS-M15P32-C performance specification. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 SAMPLE SELECTION All evaluations shall be conducted on

5、test specimens taken from finished roll goods prior to any subsequent operations, such as reheating or molding. 3.3 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Design Center master sample, or shall be as specified on the engineering drawing. 3.4 COMPOSITION (A

6、STM D 629) Fiber 100% Polyester Backing Polyethylene-LDPE ENGINEERING MATERIAL SPECIFICATION WSS-M3H105-A11 Page 2 of 2 Copyright 2002, Ford Global Technologies, Inc. 3.5 METHOD OF DYEING Solution dyed or equivalent 3.6 CONSTRUCTION 3.6.1 Fiber Size and Description 5 dtex/18 dtex (ASTM D 1244) (Poly

7、ester) 3.6.2 Thickness, range, mm 1.15 - 2.15 (ASTM D 1777) 3.7 WEIGHT, min* (FLTM BN 106-01) Pile Fiber 180 - 260 g/m2Backcoating 90 - 130 g/m2Total 270 - 390 g/m2*Or as specified on Engineering drawing 3.8 PHYSICAL PROPERTIES 3.8.1 Shrinkage, max. 1.5% (FLTM BN 105-01) 3.8.2 Breaking Strength, target (ASTM D 5034, Grab Method, 305 mm/minute jaw speed) MD 445 N AMD 575 N