FORD WSS-M3H145-A-2014 CARPET POLYESTER NONWOVEN RANDOM VELOUR NEEDLED LATEX BACKCOATED PEMBROKE PATTERN 745 g m2 (22 oz) TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 1 2014 03 13 Editorial Added Carpet Name L. Sinclair, NA 2010 10 22 Activated L. Sinclair, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 3 CARPET, POLYESTER, NONWOVEN, RANDOM VELOUR, WSS-M3H14

2、5-A NEEDLED, LATEX BACKCOATED, PEMBROKE PATTERN 745 g/m2 (22 oz) 1. SCOPE The materials defined by these specifications are random velour, needled, nonwoven carpets of good quality and uniform composition backcoated with a synthetic latex. 2. APPLICATION This specification was released originally fo

3、r floor carpet applications on B and C car platforms as part of the GCBP strategy. 3. REQUIREMENTS In addition to the requirements listed herein, the end-item floor carpet shall be tested to WSS-M8P16-B and any additional SDS requirements. The details for each of the suppliers specific construction

4、shall be documented in the supplement attached and uploaded into the FMD (Ford Materials Database). 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Vehicle Int

5、erior Environment Quality Materials/Component Performance Requirements Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-B1/latest. Data must be included in material submission package. 3.2 SAMPLE SELECTION All evaluations shall be conducted on test specimen

6、s taken from finished floor assemblies. 3.3 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Design Center master sample, or shall be as specified on the engineering drawing. 3.4 COMPOSITION 3.4.1 Face Fiber 100% Recycled Polyester (ASTM D276) Staple Fiber 3.4.2 Ba

7、ck Coating Latex (ASTM D276) ENGINEERING MATERIAL SPECIFICATION WSS-M3H145-A Copyright 2014, Ford Global Technologies, LLC Page 2 of 3 3.5 CONSTRUCTION 3.5.1 Face Fiber 12 denier (ASTM D 1244) 3.6 THICKNESS 3.6.1 Face Fiber Height 5.0 +/- 1.0 mm (ISO 1765) 3.6.2 Backcoating 1.0 +/- 0.1 mm (ISO 1765)

8、 The back coating shall thoroughly saturate the base of the carpet to ensure adequate fiber lock. Penetration of the back coating through to the face shall be controlled to provide the required resistance to abrasion and fiber loss, but it shall not be visible on the face of the carpet. 3.7 WEIGHT 3

9、.7.1 Face Fiber 729-780 g/m2 (ASTM D5848) (21.5-23 oz) 3.7.2 Back Coating 100 +/- 10 g/m2 (ASTM D5848) (3 +/- 0.3 oz) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 DRAWING CALL OUT The following

10、shall be called out on the Engineering drawing to correctly designate the approved material. WSS-M3H145-A Supplier Name and Product Code WSS-M8P16-B 5. SUMMARY OF REVISIONS ENGINEERING MATERIAL SPECIFICATION WSS-M3H145-A Copyright 2014, Ford Global Technologies, LLC Page 3 of 3 Non Woven Carpet Cons

11、truction Supplement Supplier _Supplier Contact Name_ Number _ Product/ Style Name _ Material Specification _ Performance Specification _ Supplier Product Code _ Manufacturing Location _ Supplier Lab Number _ Supplier Lab Date _ Composition Type Supplier Face Fiber ASTM D276 _ _ Binder Fiber ASTM D27

12、6 _ _ Fabric Backing ASTM D276 _ _ Pre Coat ASTM D276 _ _ Primary Backing ASTM D276 _ _ Secondary Backing ASTM D276 _ _ Construction Solution or piece dyed (circle one) Denier _ Face Fiber Thickness ISO 1765 _+/- _ mm Binder Fiber Thickness ISO 1765 _+/- _ mm Pre Coating Thickness ISO 1765 _+/- _ mm

13、 Primary Thickness ISO 1765 _+/- _ mm Secondary Thickness ISO 1765 _+/- _ mm Mass per Unit Area Weight Face Fiber ASTM D5848 _+/- _ g/m2 Binder Fiber ASTM D5848 _+/- _ g/m2 Pre Coating ASTM D5848 _+/- _ g/m2 Primary Backing ASTM D5848 _+/- _ g/m2 Secondary Backing ASTM D5848 _+/- _ g/m2 Materials Engineering Signature _Date _ Comments _ Rolled Goods _ Molded Product _