FORD WSS-M3P30-A2-2003 PHOSPHATE BASE BONDED PTFE RESIN MOLYBDENUM DISULFIDE COATING TO BE USED WITH FORD WSS-M99P1111-A 《磷酸盐基粘合的聚四氟乙烯（PTFE）树脂二硫化钼涂料 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 08 28 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.10, 3.12 1996 11 15 Activated D. Frederick Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 2 PHOSPHATE BASE, BONDED PTFE RESIN, MOLYBDENUM WSS-M3P3

2、0-A2 DISULFIDE COATING 1. SCOPE This specification defines the performance levels for a proprietary torque tension repeatability coating with moderate corrosion resistance. Coating consists of a zinc phosphate base with a resin-bonded, heat-cured, molybdenum disulfide and fluoropolymer lubricant pac

3、kage. 2. APPLICATION Initial application is two-piece wheel nuts for hub-piloted wheels, where torque-tension repeatability over many uses is primary desired characteristic. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the C

4、ompanys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 PHOSPHATE SUBSTRATE The zinc phosphate shall have a smooth compact macrocrystalline structure which forms a dense, uniform coating. 3.4 COATING THICKNESS A specific top coat thickness is not specified. The minimum thickness

5、 shall be sufficient to meet the required torque-tension and corrosion resistance requirements. 3.5 OIL SEALER A water base corrosion inhibitor shall be applied as a sealer as the final processing step. Parts need not be completely dry to the touch, however, parts shall not be excessively oily. 3.6

6、APPEARANCE The coating shall be a uniform semi-gloss black, free of blister. 3.7 CORROSION RESISTANCE 72 (SAE/USCAR-1) 3.8 GASOLINE IMMERSION(ASTM D 471) Finished metal parts shall show no evidence of coating failure or loss of adhesion after immersion in reference fuel “B“ at room temperature. ENGI

7、NEERING MATERIAL SPECIFICATIONWSS-M3P30-A2Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 2 3.9 OIL IMMERSION 72 (ASTM D 471) Finished parts shall show no evidence of coating failure or loss of adhesion after immersion in IRM 903* at room temperature. * Replacement oil for ASTM D 471, Oil #3. 3.11 TORQUE TENSION REPEATABILITY Must meet requirements (SAE J1965)