FORD WSS-M4D777-A8-2006 THERMOPLASTIC POLYOLEFIN ELASTOMER (TEO) HIGH COLD IMPACT EXTRUSION MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《热塑性聚烯径(TEO)弹性体高冷冲挤压成型料 与标准FORD .pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 07 28 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 5 THERMOPLASTIC POLYOLEFIN ELASTOMER (TEO) WSS-M4D777-A8 HIGH COLD IMPACT EXTRUSION MOLDING COMPOUND 1. SCOPE The materi

2、al defined by this specification is a thermoplastic polyolefin elastomer (TEO) extrusion molding compound with high cold impact resistance and low burn rates. 2. APPLICATION This specification was released originally for material used for airbag covers, non-visible to customer. 3. REQUIREMENTS Mater

3、ial specification requirements are to be used for initial qualification of materials. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 All requirements of this

4、specification, identified by symbol (s), shall be met with data representing 3 sigma values. 3.2 MOLDING COMPOUND (s) 3.2.1 Melt Flow Rate 0.4 - 1.1 g/10 minutes (ISO 1133, 230 C, 2.16 kg) 3.3 MOLDED TEST SPECIMEN 3.3.1 Preparation of Test Specimens Unless otherwise specified all tests shall be carr

5、ied out on injection molded one-end gated test specimens. The following dimensions are required: A. 150 min x 10 x 4.0 +/- 0.2 mm (Tensile Bar, ISO 3167) B. 120 x 10 x 4.0 +/- 0.2 mm Specimens with shorter dimensions shall be cut from the center portion of the test specimen A and/or B. The specimens

6、 shall be prepared according to ISO 294. No annealing allowed. 3.3.2 Density 0.87- 0.9 g/cm3(ISO 1183, Method A) ENGINEERING MATERIAL SPECIFICATIONWSS-M4D777-A8 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 5 3.3.3 Hardness, Durometer D 40-55 (ISO 868, 15 s

7、dwell) (s) 3.3.4 Tensile Strength at Max Load, min 10 MPa (ISO R 527, 150 minimum x 10 x 4.0 +/- 0.2 mm specimen, 50 mm/min test speed) (s) 3.3.4.1 Elongation at Break, min 350% (Test Method according to para 3.5.4) (s) 3.3.5 Flexural Modulus, min 250 MPa (ISO 178, 80 x 10 x 4.0 +/- 0.2 mm specimen,

8、 2 mm/min test speed, 64 mm support span) 3.3.6 Shear Modulus at 23 C 133 MPa (ASTM D 4065, forced constant amplitude, fixed frequency of 1 Hz +/- 15%, strain level below 1%. Specimen approx. 60 x 10 x 4.0 +/- 0.2 mm cut from the center of specimen A. Specimen length between clamps 35 - 40 mm. Soak

9、time at each temperature interval - 3 minutes minimum) Additionally, a Shear Modulus versus Temperature curve shall be plotted for -50 to +140 C temperature range, at 5 C minimum intervals. The plotted curve must be within tolerance range shown on page 5. (s) 3.3.7 Impact Strength, Izod, min (ISO 18

10、0/1A, 80 x 10 x 4.0 +/- 0.2 mm specimen, 10 specimens for each test) 3.3.7.1 At 23 +/- 2 C 35kJ/m23.3.7.2 At -40 +/- 1 C 45 kJ/m23.3.7.3 At -20 +/- 2 C 55 kJ/m2The test specimens must be conditioned for minimum of 6 h at the above specified temperature prior to impact test. Low temperature testing s

11、hall be done within the cold box. (s) 3.3.8 Heat Deflection Temperature, min (ISO 75, 120 x 10 x 4.0 +/- 0.2 mm specimen, edgewise, 0.32 +/- 0.01 mm deflection) 3.3.8.1 At 1.80 Mpa 37 C ENGINEERING MATERIAL SPECIFICATIONWSS-M4D777-A8 Printed copies are uncontrolled Copyright 2006, Ford Global Techno

12、logies, LLC Page 3 of 5 3.3.8.2 At 0.45 Mpa 50 C All specimens dry as molded. If not tested immediately after molding, specimens must be stored in a sealed, moisture-proof container filled with silica gel. 3.3.9 Heat Aging Performance (ISO 188, except 150 +/- 50 air changes/h, 1000 h at 150 +/- 2 C.

13、 Unaged property values shall be determined at the time of the aged properties determination) 3.3.9.1 Tensile Strength at Yield Change +/- 25% (Test Method per para 3.5.4) 3.3.9.2 Impact Strength, Izod Change, max -25% (Test Method per para 3.5.7.1, specimens to be notched before heat aging) 3.4 FOG

14、GING (SAE J1756, 3 h at 100 C heating, 21 C cooling plate, post test conditioning 1 h and 16 h) Fog Number, min 80 Formation of clear film, droplets or crystals is cause for rejection. 3.5 FLAMMABILITY (ISO 3795) Burn Rate, max 100 mm/minute The specimen size required for material approval is 355 x

15、100 x 1.0 +/- 0.1 mm with a smooth surface. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 COEFFICIENT OF LINEAR THERMAL EXPANSION 5.0 - 7.5 x 10-5/C (ASTM E 831 (TMA), temperature range -30 to +1

16、00 C) 4.2 MOLD SHRINKAGE (ISO 2577, approx. 150 x 100 x 3.2 +/- 0.2 mm injection molded specimen) 4.2.1 Molding Shrinkage . After 48 h at 23 +/- 2 C 0.7-1.0% ENGINEERING MATERIAL SPECIFICATIONWSS-M4D777-A8 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 4 of 5 4.2.2 Post Shrinkage (Separate specimens required for each test) . After 48 h at 80 C 0.2 - 0.3% . After 30 min at 120 C 0.0 - 0.4% 4.3 RECYCLING CODE PP+EPDM ENGINEERING MATERIAL SPECIFICATIONWSS-M4D777-A8 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 5 of 5