FORD WSS-M4D822-B1-2016 POLYAMIDE (PA) 6 HEAT STABILIZED 40% GLASS FIBER MINERAL MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 01 2016 04 20 Revision See Summary of Revisions R. Harris, NA 2014 10 21 Released R. Harris, NA Controlled document at www.MATS Copyright 2016, Ford Global Technologies, LLC Page 1 of 6 POLYAMIDE (PA) 6, HEAT STABILIZED 40% GLASS WSS-M4D8

2、22-B1 FIBER/MINERAL MOLDING COMPOUND POLYAMIDE (PA) 6, HEAT STABILIZED 40% GLASS WRS-M4D822-B2 FIBER/MINERAL MOLDING COMPOUND, 25% PCR AND/OR PIR RECYCLED RESIN CONTENT 1. SCOPE The material defined by these specifications are heat stabilized with approximately 15% glass fiber and 25% mineral, reinf

3、orced polyamide 6 molding compounds. 2. APPLICATION This specification was released originally for material used in underhood applications. . 2.1 LIMITATIONS This material absorbs and retains moisture. Part design and tolerances must accommodate changes in part dimensions and physical properties due

4、 to moisture absorption or loss in the service/assembly environment. This material does not contain UV stabilizers, long term exposure to direct sunlight will cause chalking or loss of gloss. This material is not suitable to long term exposure to engine coolant, or direct exposure to strong acids or

5、 bases. It is not suitable for use above 150 C. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.1.1 Many 4D resin specifications prior to 2011, ide

6、ntified certain requirements with the symbol (s), which indicated that the mean and +/- 3 sigma values were to be reported. The specification minimum, maximum or range was established using 3 sigma data. For 2011 and beyond, refer to Table 1 for number of samples required for each test. 3.1.2 WSS-M4

7、D822-B1 is based on virgin materials. 3.1.3 WRS-M4D822-B2 must contain 25% Post Consumer Recycled (PCR) and/or Post Industrial Recycled (PIR) content as defined by WRS-M99P42-A1. The remaining portion of the material can come from virgin sources. The 25% must match the 25% PCR/PIR CONTENT in the tit

8、le of the specification. 3.1.4 The use of regrind is permitted, for economic / environmental reasons, with compliance as indicated in Ford Engineering CAD and Drafting Standard E-4. Part manufacturers using this specification must complete DV and PV testing with the allowable amount of ENGINEERING M

9、ATERIAL SPECIFICATION WSS-M4D822-B1/ WRS-M4D822-B2 Copyright 2016, Ford Global Technologies, LLC Page 2 of 6 regrind and the maximum allowable regrind content must be specified on the engineering drawing. Any changes to what is specified on the drawing (no specification implies zero regrind) must be

10、 approved by Materials and PD Engineering through the formal Ford Motor process (SREA). 3.1.5 Dry as molded: All test values indicated herein are based on material and specimens with moisture content not exceeding 0.2% except where noted (Moisture Conditioned, see paragraph 3.1.5) (test according to

11、 ISO 15512 Method B/ASTM D 6869). All test materials have to be sealed in moisture-proof containers and stored at 23 +/- 2 C for at least 24 h immediately after processing. If the moisture content exceeds 0.2%, conditioning the material for a minimum of 16 h at 40 50 C at a reduced pressure below 13

12、3 kPa. Conduct tests in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5% relative humidity. Individual specimens shall not be removed from closed containers until immediately before testing. 3.1.6 Moisture Conditioned: The specimens shall be conditioned to a moisture content of 1.0 to 2.0 wt% moi

13、sture then place the specimens in standard atmosphere of 23 +/- 2 C and 50 +/- 5% relative humidity for at least 1 h before testing (according to ISO 1110). Moisture content shall be reported to verify the moisture level. . 3.1.7 Performance Criteria: Parts using these specifications must comply wit

14、h all the requirements of WSS-M15P50-B/Latest and fulfill applicable SDS/CDS requirements. 3.1.8 As specified in WSS-M99P1111-A, paragraph 3.2, Ford Materials Engineering may request a Control Plan and Certificate of Analysis (CoA) containing lot testing requirements which must include, but are not

15、limited to: Filler Content Impact Strength, Notched Charpy at 23C Tensile Modulus 3.2 SAMPLE PREPARATION Unless otherwise specified all tests shall be carried out on injection molded, one-end gated test specimens. The test specimens A and D shall be molded using molding conditions defined in ISO 187

16、4-2. See Table 1 for the number of specimens required. Specimens shall be as follows: Specimen A 150 minimum x 10 x 4.0 +/- 0.2 mm (ISO 527-2, Specimen Type 1A) Specimen B 355 x 100 x 1.0 +/- 0.1 mm (ISO 3795) Specimen C 145 x 60 x 3.2 +/- 0.2 mm Specimen D Center of Specimen A. 80 x 10 x 4.0 +/- 0.

17、2 mm Specimen E 100 mm diameter x 3.2 mm Specimen F 80 mm diameter x 3.2 mm Specimen G 90 mm x 200 mm Specimen H 50 +/- 1 mm diameter x 3.2 +/- 0.2 mm Specimen I 100 mm x 150 mm, min ENGINEERING MATERIAL SPECIFICATION WSS-M4D822-B1/ WRS-M4D822-B2 Copyright 2016, Ford Global Technologies, LLC Page 3

18、of 6 3.3 MATERIAL PROPERTIES 3.3.1 Melt Temperature 210 - 225 C (ISO 11357, 10 C/min heating rate) 3.3.2 Determination of Ash Glass: 13 - 17% (ISO 3451-4, test temperature 600 Mineral: 23 - 27% +/- 25 C, test portion 2.0 to 2.5 g) 3.3.3 Density 1.42 1.50 g/cm3 (ISO 1183, Method A) 3.3.4 Tensile Stre

19、ngth at Break 100 MPa min (ISO 527-1 and ISO 527-2, Specimen A, 5 mm/minute test speed) 3.3.5 Tensile Modulus 6 GPa min (ISO 527-1 and ISO 527-2, Specimen A, 1 mm/minute test speed) 3.3.6 Impact Strength, Notched Charpy (ISO 179-1/2, Specimen D) 3.3.6.1 At 23 +/- 2 C 3.0 kJ/m2 min Report Break Type3

20、.3.6.2 At -40 +/- 2 C 2.0 kJ/m2 min Report Break Type The test specimen must be conditioned for minimum of 6 hours at the above specified temperature prior to impact test. Low temperature testing shall be done within the cold chamber, if not possible, test may be conducted outside, but within 5 seco

21、nds. 3.3.7 Heat Deflection Temperature 187 C min (ISO 75-1 and ISO 75-2, Specimen D, flatwise, 0.34 +/- 0.1 mm deflection, at 1.80 MPa) 3.3.8 Heat Aging Performance (ISO 188, except 150 +/- 50 air changes/h, 1000 h at 140 +/- 2 C. After heat aging test specimens are to be conditioned in a desiccator

22、 for 3 - 5 h at 23 +/- 2 C. Unaged property values shall be determined at the time of the aged properties determination) 3.3.8.1 Impact Strength, Notched Charpy, Change +/- 25% max (Test Method per para 3.3.6.1, specimens to be notched before Heat Aging) 3.3.9 Flammability (ISO 3795/SAE J369, Specim

23、en B, smooth surface) Burn Rate 100 mm/minute max ENGINEERING MATERIAL SPECIFICATION WSS-M4D822-B1/ WRS-M4D822-B2 Copyright 2016, Ford Global Technologies, LLC Page 4 of 6 3.4 MATERIAL PROPERTIES REPORT ONLY Values are retained in Ford Materials Database . 3.4.1 Molding Shrinkage (Report method used

24、, sample size and value) After 48 h at 23 +/- 2 C Flow Report Value, % Cross Flow Report Value, % 3.4.2 Coefficient of Linear Thermal Expansion (ISO 11359-2), -30 +/- 2 C to 60 +/- 2 C Flow Report Value, E-5 mm/mm/ C Cross Flow Report Value, E-5 mm/mm/ C 60 +/- 2 C to 120 +/- 2 C Flow Report Value,

25、E-5 mm/mm/ C Cross Flow Report Value, E-5 mm/mm/ C 3.4.3 Water Absorption Report Value, % (ISO 62, 24 h immersion, Specimen H) 3.4.4 Heat Deflection Temperature (ISO 75-1 and ISO 75-2, Specimen D, flatwise, 0.34 +/- 0.1 mm deflection, at 0.45 Mpa) Report Value. C 3.4.5 Poissons Ratio Report Ratio (I

26、SO 527-1 and ISO 527-2, Specimen A, 1 mm/minute test speed) 3.4.6 Moisture Conditioned 3.4.6.1 Moisture Content Report Value wt% (ISO 15512, Karl Fisher, or ASTM D756-93 weight change method) Note: Moisture content must be between 1.0 2.0 wt.% before testing para 3.4.6.2, 3.4.6.3, 3.4.6.4, and 3.4.6

27、.5. 3.4.6.2 Tensile Strength at Break Report Value, MPa (ISO 527-1 and ISO 527-2, Specimen A, 5 mm/minute test speed, 23 +/- 2 C) 3.4.6.3 Tensile Modulus Report Value, GPa (ISO 527-1 and ISO 527-2, Specimen A, 1 mm/minute test speed) 3.4.6.4 Impact Strength, Notched Charpy Report Value, kJ/m2 (ISO 1

28、79-1/1eA, Specimen D, 23 +/- 2 C) Report Break Type 3.4.6.5 Flexural Modulus Report Value, GPa(ISO 178, Specimen D, 64 mm support span, 2 mm/minute test speed) ENGINEERING MATERIAL SPECIFICATION WSS-M4D822-B1/ WRS-M4D822-B2 Copyright 2016, Ford Global Technologies, LLC Page 5 of 6 3.4.7 Supplemental

29、 Information The following curves are to be submitted with the data packages: FTIR TGA DSC CLTE (3 curves per directions, flow and cross flow) Engineering Stress/Strain at 23 +/- 2 C and -40 +/- 2 C 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in me

30、eting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 TYPICAL PROPERTIES USING METHODS IN SECTION 3.4 Para. Test Typical Value Units 3.4.1 Molding Shrinkage (After 48 h at 23 +/- 2 C) (For specific method and sample size, contact Mat

31、erials Engineering) Flow Cross Flow 0.4 0.7 % % 3.4.2 Coefficient of Linear Thermal Expansion -30 to 60oC Flow Cross Flow 60 to 120oC Flow Cross Flow 3.0 7.2 2.8 12.8 E-5 mm/mm/ C E-5 mm/mm/ C E-5 mm/mm/ C E-5 mm/mm/ C 3.4.3 Water Absorption 0.8 % 3.4.4 Heat Deflection, at 0.45 MPa, minimum 214 C 3.

32、4.6 Poissons Ratio 0.4 N/A 3.4.7.1 Moisture Content 2.2 % 3.4.7.2 Moisture Conditioned Tensile Strength at Break 66 MPa 3.4.7.2 Moisture Conditioned Tensile Modulus 4.02 GPa 3.4.7.3 Moisture Conditioned Notched Charpy Impact 7 kJ/m2 3.4.7.4 Moisture Conditioned Flexural Modulus 3.9 GPa 4.2 GENERIC I

33、DENTIFICATION AND MARKING OF PLASTIC PRODUCTS PA6-(GF+M)40 (ISO 1043/11469) ENGINEERING MATERIAL SPECIFICATION WSS-M4D822-B1/ WRS-M4D822-B2 Copyright 2016, Ford Global Technologies, LLC Page 6 of 6 Table 1: Minimum Sample Size Initial Approval New Manufacturing Location for Previously Approved Mater

34、ial Para. Test Lots Specimens per Lot Total Test Specimens Lots Specimens per lot Total Test Specimens 3.1 WSS-M99P1111-A 3.1.7 WSS-M15P50-B/Latest Reference Performance Specification 3.3.1 Determination of Ash 3 1 3 1 1 1 3.3.2 Melt Temperature 3 1 3 3.3.3 Density 1 3 3 3.3.4 Tensile Strength at Br

35、eak* 3 5 15 1 5 5 3.3.5 Tensile Modulus* 3 10 30 1 10 10 3.3.6 Impact Strength Notched Charpy (per condition)* 3 10 30 1 10 10 3.3.7 Heat Deflection Temperature* 3 2 6 1 2 2 3.3.8 Heat Aging Performance 3.3.8.1 Impact Strength, Notched Charpy, Change 1 10 10 3.3.9 Flammability 1 5 5 3.4.1 Mold Shrin

36、kage 1 5 5 1 5 5 3.4.2 Coefficient of Linear Thermal Expansion (per condition) 1 3 3 3.4.3 Water Absorption 1 3 3 3.4.5 Heat Deflection Temperature, 0.45 MPa 1 2 2 3.4.6 Poissons Ratio 1 2 2 1 2 2 3.4.7.1 Moisture Content 1 1 1 3.4.7.2 Moisture Conditioned Tensile Strength at Break 3 5 15 1 5 5 3.4.

37、7.3 Moisture Conditioned Tensile Modulus 1 10 10 3.4.7.4 Moisture Conditioned Notched Charpy Impact 3 10 30 1 10 10 3.4.7.5 Moisture Conditioned Flexural Modulus 1 10 30 3.4.8 Curves - FTIR - TGA - DSC - CLTE - Stress/Strain ( 23 C and -40 C) 1 1 1 per test *3 Sigma statistical data is required for the noted tests. Individual data points shall be reported. 5. SUMMARY OF REVISIONS 2016 04 20 Changed Melt Temperature from 210-219C back to WSK-M4D822-A range of 210-225 C