FORD WSS-M4D836-B1-2012 ABS ELECTROPLATING GRADE MOLDING COMPOUND EXTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 1 2012 09 24 Revised Editorial correction to Melt Flow rate. S. Zhang, APA 2012 05 14 Activated C. McComb, NA Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 6 ABS, ELECTROPLATING GRADE MOLDING COM

2、POUND, EXTERIOR WSS-M4D836-B1 ABS, ELECTROPLATING GRADE MOLDING COMPOUND, INTERIOR WSS-M4D836-B2 1. SCOPE The material defined by this specification is an electroplating grade of molding compound based on acrylonitrile/butadiene/styrene (ABS). 2. APPLICATION WSS-M4D836-B1 - This specification was re

3、leased originally for material used in electroplated or painted badges, grilles, and exterior lighting chrome trim. WSS-M4D836-B2 This specification was released originally for material used in electroplated interior trim such as rings and knobs. 2.1 LIMITATIONS This material does not contain UV sta

4、bilizers, long term exposure to direct sunlight will cause chalking and loss of gloss. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.1.1 Many 4D

5、resin specifications prior to 2011, identified certain requirements with the symbol (s), which indicated that the mean and +/- 3 sigma values were to be reported. The specification minimum, maximum or range was established using 3 sigma data. For 2011 and beyond, refer to Table 1 for number of sampl

6、es required for each test to establish specification limits. 3.1.2 The use of regrind is permitted, for economic / environmental reasons, with compliance as indicated in Ford Engineering CAD and Drafting Standard E-4. 3.1.3 For WSS-MD836-B2 only: Materials used in interior applications must meet the

7、 requirements outlined in WSS-M99P2222-C1/Latest, Performance, Vehicle Interior Environment Quality Material/Component Requirements. Data must be included in material submission package. 3.1.4 Performance Criteria: Parts using this specification shall meet the appropriate performance specifications:

8、 Plated applications: WSS-M1P83-D1/D2/D3 or latest. Interior painted applications: WSS-M2P188-A1 or latest Exterior painted applications: WSS-M2P180-D or latest. A primer may be required to reduce appearance defects such as blushing. ENGINEERING MATERIAL SPECIFICATION WSS-M4D836-B1/B2 Copyright 2012

9、, Ford Global Technologies, LLC Page 2 of 6 3.2 SAMPLE PREPARATION Unless otherwise specified all tests shall be carried out on injection molded, one-end gated test specimens. The test specimens A and D shall be molded using molding conditions defined in ISO 2580-2. No annealing is allowed. See Tabl

10、e 1 for the number of specimens required. Specimens shall be as follows: Specimen A 150 minimum x 10 x 4.0 +/- 0.2 mm (ISO 527-2, Specimen Type 1A) Specimen B 355 x 100 x 2.0 +/- 0.1 mm (ISO 3795) Specimen C 145 x 60 x 3.2 +/- 0.2 mm Specimen D Center of Specimen A. 80 x 10 x 4.0 +/- 0.2 mm Specimen

11、 E 100 mm diameter x 3.2 mm Specimen F 80 mm diameter x 3.2 mm Specimen G 90 mm x 200 mm Specimen H 50 +/- 1 mm diameter x 3.2 +/- 0.2 mm Specimen I 100 mm x 150 mm, min 3.3 MATERIAL PROPERTIES 3.3.1 Density 1.02 - 1.1 g/cm3(ISO 1183, Method A) 3.3.2 Tensile Strength at Yield 35 MPa min (ISO 527-1 F

12、low 6.4 10.5 E-5 mm/mm/C 3.4.1.1 Mold Shrinkage (For specific method, sample size, contact materials engineering) Flow Cross Flow 0.4 - 0.8 0.4 - 0.8 % % 3.4.3 Poissons ratio 0.35 3.4.4.1 Impact Strength, Notched Izod; At 23 +/- 2 C 11-28 kJ/m23.4.4.2 Impact Strength, Notched Izod; At -40 +/- 2 C 4

13、- 15 kJ/m25. SUMMARY OF REVISIONS 2012 09 24 Revised to clarify Melt Flow requirement as a minimum. ENGINEERING MATERIAL SPECIFICATION WSS-M4D836-B1/B2 Copyright 2012, Ford Global Technologies, LLC Page 6 of 6 4.2 MATERIAL IDENTIFICATION FOR RECYCLING PURPOSES ABS (ISO 1043/11469) Table 1: Minimum S

14、ample Size Initial Approval New Manufacturing Location for Previously Approved Material Para. Test Minimum Lots Specimens per Lot Total Test Specimens Lots Specimens per lot Total Test Specimens 3.1 WSS-M99P1111-A 3.1.4 WSS-M99P2222-C1 Total Carbon, Hazardous Substances, Formaldehyde, Acraldehyde, A

15、cetaldehyde (See below for odor and fogging) 1 1 1 per test 3.3.1 Density 1 3 3 3.3.2 Tensile Strength at Yield* 3 5 15 1 5 5 3.3.3 Elongation at Yield* 3 5 15 1 5 5 3.3.4 Tensile Modulus 1 10 10 3.3.5 Flexural Modulus* 3 10 30 1 10 10 3.3.6 Impact Strength Notched Charpy (per condition)* 3 10 30 1

16、10 10 3.3.7 Heat Deflection Temperature* 3 2 6 1 2 2 3.3.8 Vicat Softening Temperature* 3 2 6 1 2 2 3.3.9 Heat Aging Performance 3.3.9.1 Tensile Strength at Yield Change 1 5 5 3.3.9.2 Impact Strength, Notched Charpy Change 1 10 10 3.3.10 Flammability 1 5 5 3.3.11 Odor, B2 only 1 9 9 3.3.12 Fogging P

17、hotometric, B2 only 1 3 3 3.3.13 Fogging Gravimetric, B2 only 1 3 3 3.3.14 Melt Flow Rate* 3 1 3 1 1 1 3.4.1 Coefficient of Linear Thermal Expansion (per condition) 1 3 3 3.4.2 Mold Shrinkage 1 5 5 3.4.3 Poissons Ratio 1 2 2 3.4.5 Curves - FTIR - TGA - DSC - CLTE Engineering Stress/Strain at 23 C 1 1 1 per test * For these requirements the 3 sigma value from the raw data is used to meet the requirements.