FORD WSS-M4D865-B8-2014 POLYPROPYLENE (PP) 30% LONG GLASS FIBER REINFORCED STRUCTURAL NON UV-STABLE TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 2 2014 11 07 Editorial Editorial See Summary of Revisions L. Soreide, NA 2013 05 13 Revised Editorial See Summary of Revisions G. Eaton, NA 2012 06 08 Activated New specification Georgette Eaton, NA Controlled document at www.MATS Copyri

2、ght 2014, Ford Global Technologies, LLC Page 1 of 5 POLYPROPYLENE (PP) WSS-M4D865-B8 30% LONG GLASS FIBER REINFORCED, STRUCTURAL, NON UV-STABLE 1. SCOPE The material defined by this specification is an injection molding compound composed of a polypropylene matrix, with 30% by weight long glass fiber

3、 reinforcement with typical fiber length between 9-16 mm. 2. APPLICATION This specification was released originally for material used for door module structures. 2.1 LIMITATIONS This material does not contain UV stabilizers, long term exposure to direct sunlight will cause chalking and loss of gloss

4、. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 This specification is based on virgin materials. Materials with post-consumer, post industria

5、l, or repolymerised recycled materials as defined by WRS-M99P42-A1 are preferred and should be used whenever feasible. 3.1.2 The use of regrind is permitted, for economic / environmental reasons, with compliance as indicated in Ford Engineering CAD and Drafting Standard E-4. 3.1.3 Performance Criter

6、ia: Parts using this specification shall meet the appropriate system design specifications (SDS) requirements 3.1.4 Processing Criteria: Proper processing parameters and equipment should be used to preserve maximum fiber length in molded parts as specified and measured by the raw material supplier.

7、Raw material supplier must be involved upfront for mold flow, CAE, and tooling design and should be present at all molding trial. WSS-M99D514-A1 is to be used for thermoplastic compounds using long glass fiber masterbatch pellets. WSS-M99D514-A2 is to be used for thermplastic compounds using Direct

8、Long glass Fiber Technology (DLFT) or Injection Molding Compounding (IMC). ENGINEERING MATERIAL SPECIFICATION WSS-M4D865-B8 Copyright 2014, Ford Global Technologies, LLC Page 2 of 5 3.2 SAMPLE PREPARATION Unless otherwise specified all tests shall be carried out on injection molded, one-end gated te

9、st specimens. The test specimens A and D shall be molded using molding conditions defined in ISO 1873-2. No annealing is allowed. See Table 1 for the number of samples required. Specimens shall be as follows: Specimen A 150 minimum x 10 x 4.0 +/- 0.2 mm (ISO 527-2, Specimen Type 1A) Specimen B 355 x

10、 100 x 1.0 +/- 0.1 mm (ISO 3795) Specimen C 145 x 60 x 3.2 +/- 0.2 mm Specimen D Center of Specimen A. 80 x 10 x 4.0 +/- 0.2 mm Specimen E 100 mm diameter x 3.2 mm Specimen F 80 mm diameter x 3.2 mm Specimen G 90 mm x 200 mm Specimen H 50 +/- 1 mm diameter x 3.2 +/- 0.2 mm Specimen I 100 mm x 150 mm

11、, min 3.3 MATERIAL PROPERTIES 3.3.1 Filler Content 28% - 33% (ISO 3451-1, Method A, 1h at 650 +/- 25C, test portion, 2 2.5g) 3.3.2 Density 1.10 1.15 g/cm3 (ISO 1183, Method A) 3.3.3 Tensile Strength at Break 79 MPa min (ISO 527-1 At 23 +/- 2 C 26 kJ/m2 3.4.3.2 Impact Strength, Notched Izod; At -40 +

12、/- 2 C 27 kJ/m2 3.4.4 Poissons Ratio 0.34 N/A 4.2 MATERIAL IDENTIFICATION FOR RECYCLING PURPOSES PP-GLF30 (ISO 1043/ISO 11469) ENGINEERING MATERIAL SPECIFICATION WSS-M4D865-B8 Copyright 2014, Ford Global Technologies, LLC Page 5 of 5 Table 1: Minimum Sample Size Initial Approval New Manufacturing Lo

13、cation for Previously Approved Material Para. Test Minimum Lots Specimens per lot Total Test Specimens Lots Specimens per lot Total Test Specimens 3.1 WSS-M99P1111-A 3.1.2 WSS-M99P2222-C1/Latest Total Carbon, Hazardous Substances, Formaldehyde, Acraldehyde, Acetaldehyde (See below for odor and foggi

14、ng) 1 1 1 per test 3.3.1 Filler Content* 3 1 3 1 1 1 3.3.2 Density 1 3 3 3.3.3 Tensile Strength at Break* 3 5 15 1 5 5 3.3.4 Tensile Modulus 1 10 10 3.3.5 Flexural Modulus* 3 10 30 1 10 10 3.3.6 Impact Strength, Notched Charpy (per condition)* 3 10 30 1 10 10 3.3.7 Heat Deflection Temperature* 3 2 6

15、 1 2 2 3.3.8 Heat Aging Performance 3.3.8.1 Tensile Strength at Break Change 1 5 5 3.3.8.2 Impact Strength, Notched Charpy Change 1 10 10 3.3.9 Flammability 1 5 5 3.4.1 Molding Shrinkage 1 5 5 1 5 5 3.4.2 Coefficient of Linear Thermal Expansion (per condition) 1 3 3 3.4.3 Impact Strength Notched Izo

16、d (per condition) 1 10 10 3.4.4 Poissons Ratio 1 2 2 3.4.5 Curves - FTIR - TGA - DSC - CLTE - Stress/Strain Curves 1 1 1 per test *For these requirements the 3 sigma value from the raw data is used to meet the requirements. Individual data points shall be reported. 5. SUMMARY OF REVISIONS 11/7/2014 Corrected recycling code 5/13/2013 Editorial Change Removed fiber length from title and changed the length in the scope from 9-13 mm to 9-16 mm