FORD WSS-M4P13-A-2014 ANODIZED ALUMINUM PERFORMANCE DECORATIVE EXTERIOR TRIM TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 2 2014 06 12 Editorial Corrected suffix 2014 06 10 Updated See Summary of Revisions G. Eaton, NA 2011 10 10 Activated G. Eaton, FNA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 6ANODIZED ALUMINU

2、M PERFORMANCE, DECORATIVE EXTERIOR TRIM WSS-M4P13-A 1. SCOPE This specification defines the minimum durability and performance requirements of anodized aluminum for bright decorative trim components. 2. APPLICATION This performance specification was released originally for anodized aluminum outer be

3、lt moldings. 2.1 LIMITATIONS Any cleaning agent containing a combination of ethoxylated C12-15 fatty acid and sodium metasillicate should not be used to clean this material (example: Motorcraft Multipurpose Cleaner). Surface attack will occur leaving a chalky substance on the surface. 3. REQUIREMENT

4、S 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 ANODIZED ALUMINUM PERFORMANCE MANAGEMENT All materials evaluated under this performance specification must have

5、 Supplement A completed and signed by Ford Materials Engineering, the material/coatings supplier, and the Tier One supplier. The Supplement A and specification data will be stored in the Ford Materials Database (FMD). If the aluminum is being applied to an outer belt molding, compatibility of the an

6、odized aluminum with seal material (s) is the responsibility of the Tier One supplier. The Tier One supplier shall have the seal tested against the applicable performance specification requirements. Table 2.0 describes the construction of the anodized aluminum, and must be submitted with Supplement

7、A. (Reference Supplement A). The Tier One supplier is responsible for including Table 2.0 and this performance specification on the part drawing. 3.3 FINISHED PARTS Testing must be conducted at Design Verification (DV) and Product Validation (PV) per Table 1.0 (including Supplement A), unless otherw

8、ise agreed to by Materials Engineering, and on actual production parts or a section of the part whenever possible. Where part dimensions limit testing equipment access, representative test samples may be substituted. PV Testing must be conducted on actual production processed parts. No change in mat

9、erial, facility, or processing is permitted without written approval from Ford Materials Engineering Activity, via SREA. ENGINEERING MATERIAL SPECIFICATION WSS-M4P13-A Copyright 2014, Ford Global Technologies, LLC Page 2 of 6 All test values are based on parts conditioned in a controlled atmosphere

10、of 23 +/- 2 C and 50% R.H. for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. 3.4 APPEARANCE: COLOR, FINISH, SURFACE (FLTM BI 109-01) The color, gloss, and finish of the anodized aluminum part shall be specified on the engineering drawing and be

11、uniform along the entire length of the assembly. The surface shall be free of blisters, voids and scratches. 3.5 RESISTANCE PROPERTIES Paragraph 3.5.1 Corrosion Resistance, shall be tested on whole parts or sections of assemblies and must include all materials and interfacing parts (i.e. mating part

12、s). Separate specimens are required for each test. The parts after being subjected to the tests listed below shall conform to the following requirements in addition to the ones listed: (a) No cracking, chalking, crazing, iridescence, bloom, milkiness, separation, loss of adhesion (coating), or loss

13、of embossment allowed (as defined in ASTM D1566). (b) No visible corrosion or blistering is permitted. 3.5.1 Corrosion Resistance (CETP 00.00-L-467) Moderate Visibility - 6 weeks exposure No Visible Change High Visibility 9 weeks exposure No Visible Change Design with Crevices 12 weeks exposure No V

14、isible Change or Loss of Functionality 3.5.2 Fluid Resistance Rating 5 min (FLTM BI 168-01, Method B, No Visible Change ISO 105-A02/AATCC Evaluation Procedure 1) Test Fluids: Gasoline Diesel Coolant Engine Oil DI Water Windshield Washer Fluid Motorcraft Bug and Tar Remover Glass Cleaner IPA ENGINEER

15、ING MATERIAL SPECIFICATION WSS-M4P13-A Copyright 2014, Ford Global Technologies, LLC Page 3 of 6 3.5.3 Alkalinity Resistance, pH 13 Rating 4 min (ISO 105-A02/AATCC Evaluation Procedure 1) Alkaline Test Solution: Na3P04 2 g/l NaCl 200 mg/l NaOH Add until pH=13 Deionized water is used to dilute the so

16、lution Method: Partially immerse each sample in the specified solution for 10 minutes at 23 +/-2 C. After 10 minutes remove the samples from the solution, rinse with water, and wipe dry with a non-treated cotton cloth. Note any visible change. 3.5.4 Resistance to Exterior Weathering Applicable to co

17、mponents with organic coatings/sealing technologies only. Is not required for components utilizing inorganic anodize sealing technologies. (ISO 105-A02/AATCC Evaluation Procedure 1) 3.5.4.1 Accelerated Weathering Rating 4 min (SAE J2527 Atlas Water Cooled, Rotary Drum Xenon-Arc Apparatus only. Modif

18、ied Type “S“ borosilicate inner and outer filters, 0.55 W/m2 radiant exposure monitored at 340 nm. 3000 h exposure) 3.5.4.2 Natural Weathering Rating 4 min New Technology Only 1 & 2 year required (SAE J1976, Procedure A) 3.5.5 Mar Resistance 70% Gloss retention (FLTM BI 161-01) No visual Mar at all

19、angles 3.5.6 Acid Dissolution Test 6.0 max (FLTM BQ 007-02) ENGINEERING MATERIAL SPECIFICATION WSS-M4P13-A Copyright 2014, Ford Global Technologies, LLC Page 4 of 6 TABLE 1.0: DV/PV Requirements Sample size/color (if applicable) To be done at DV testing To be done at PV testing 3.5.1 Corrosion Resis

20、tance 3 X X* 3.5.2 Fluid Resistance 1 per fluid X X* 3.5.3 Alkalinity Resistance 3 X X* 3.5.4 Resistance to Exterior Weathering 1 X X* 3.5.5 Resistance to Marring 1 X X* 3.5.6 Acid Dissolution 1 X X* X = required PV testing must be conducted on actual production processed parts. * = Testing only nee

21、ds to be completed if there is any change in the material or process that was tested at DV. Must be agreed to by Ford Materials Engineering. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for

22、 questions concerning Engineering Material Specifications. 5. SUMMARY OF REVISIONS 2014 06 10 3.5.3 Alkalinity resistance changed requirement from a rating 5 to a rating 4 min. 3.5.4 Revised exterior weathering method to only be applicable to aluminum with organic coatings/sealing technologies. 3.5.

23、5 Standardized mar resistance test title and requirement. Table 1.0 Added all tests to DV testing, corrected table typo from 2 to 1 Changed title Formatting and verbiage throughout document ENGINEERING MATERIAL SPECIFICATION WSS-M4P13-A Copyright 2014, Ford Global Technologies, LLC Page 5 of 6 SUPPL

24、EMENT A Ford part name, program (s), and part # to which this material is applied: Location (s) / Product Description on vehicle for application: Tier One Supplier Report number: Tier One Contact person (name/title/phone/e-mail): Product Construction Base Alloy _ Anodized Thickness _ Sealing Technol

25、ogy _ Coating Technology (if applicable) _ ENGINEERING MATERIAL SPECIFICATION WSS-M4P13-A Copyright 2014, Ford Global Technologies, LLC Page 6 of 6 Table 2.0 Part Location Tier 1 Supplier/ Product Code Construction Materials, Product Codes, and Suppliers Signed & Dated: TIER ONE SUPPLIER ANODIZED ALUMINUM SUPPLIER MATERIALS ENGINEER COATING SUPPLIER (IF APPLICABLE)