FORD WSS-M5H33-A-2015 FABRIC KNITTED FABRIC FIXED TINTED ROOF GLASS SUNSHADE 10% LIGHT TRANSMITTANCE TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 2 2015 05 19 N Status No replacement or future usage A. Wagenhaus, NA 2014 06 24 Editorial Corrected title M. Dumitrescu, NA 2008 06 04 Activated M. Dumitrescu, FNA; C. Kung, FNA Controlled document at www.MATS Copyright 2015, Ford Global

2、 Technologies, LLC Page 1 of 3 FABRIC, KNITTED FABRIC, FIXED TINTED ROOF WSS-M5H33-A GLASS SUNSHADE, 10% LIGHT TRANSMITTANCE NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a knitted polyester fabric. 2. APPLICATION This specification was released originally as a

3、 Sunshade fabric with up to 10% light transmittance for the S197 2009 Mustang Glass Roof and D471 2009 Flex Fixed Tinted Roof Glass. 3. REQUIREMENTS In addition to the requirements listed herein, this material shall meet the SDS requirements of Manual sunshade as applicable. When used on the intende

4、d application, the material must be capable of performing satisfactory under all production and service conditions. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3

5、.2 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Corporate Design master sample, or shall be as specified on engineering drawing 3.2 WEIGHT, g/m2, (FLTM BN 106-01) Fabric 135 +/- 10 3.3 THICKNESS, mm 0.37 +/- 0.03 (ASTM D 1777) 3.4 COMPOSITION (ASTM D 276/ASTM D

6、 629) Fabric 100% Polyester 3.5 FABRIC CONSTRUCTION 3.5.1 Stitch Count +/- 10% tolerance (ASTM D 3887) Wales 112 per 10 cm Courses 210 per 10 cm ENGINEERING MATERIAL SPECIFICATION WSS-M5H33-A Copyright 2015, Ford Global Technologies, LLC Page 2 of 3 3.5.2 Yarn construction (ASTM D 1244) Face 11.1 te

7、x f32 8.5 tex f24 Or as approved by Ford Materials Engineering 3.5.3 Method of Dyeing Piece Dye 3.5.4 Finishing Fluorocarbon or Polyurethane 3.6 STRENGTH PROPERTIES 3.6.1 Breaking Strength, N min (ASTM D 5034, grab method, 300 mm/min) Wales 200 N Courses 500 N 3.6.2 Retained Breaking strength after

8、Xenon exposure (FLTM BO 116-01, 451 kJ/m2) Wales 40% Courses 40% 3.7 RESISTANCE TO MILDEW No Mildew (7 days at 38 C and 98% RH) 3.8 WEAR PROPERTIES 3.8.1 Taber Abrasion 200 cycles (SAE J948 CS10 wheels, 500g load) No distortion or color change 3.8.2 Resistance to Scuffing 25 cycles (SAE J365, A head

9、) No distortion or color change 3.9 COLOR PROPERTIES 3.9.1 Resistance to Fade Rating 4 (SAE J1885, AATCC Procedure 1 488.8 kJ/m2) Or Resistance to Fade Rating 4 (FLTM BO 116-01, AATCC Procedure 1 977.6 kJ/m2) ENGINEERING MATERIAL SPECIFICATION WSS-M5H33-A Copyright 2015, Ford Global Technologies, LL

10、C Page 3 of 3 3.9.2 Heat Aging Rating 4 (7 days at 110 C, AATCC Procedure 1) 3.9.3 Soiling and Cleanability (FLTM BN 112-08, ISO 105-A02/AATCC Evaluation Procedure 2) After Cleaning, min Rating 4 3.10 ODOR, max Rating 3 (FLTM BO 131-03 or SAE J1351) 3.11 FOGGING (SAE J1756, 3 h at 100 C heating, 21 C cooling plate, post test conditioning 1h and 16 h) Fog number, min 70 Formation of clear film, droplets or crystals is cause for rejection. 3.12 FLAMMABILITY 100mm/min (SAE J369/ISO 3795)