FORD WSS-M5H35-A-2014 FABRIC KNITTED FABRIC SIDE DOOR WINDOW SUNSHADE GLASS 30% LIGHT TRANSMITTANCE TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 01 2014 06 24 Editorial Corrected title M. Dumitrescu, NA 2009 02 18 Activated M. Dumitrescu, FNA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 3 FABRIC, KNITTED FABRIC SIDE DOOR WINDOW SUNSHADE W

2、SS-M5H35-A GLASS, 30% LIGHT TRANSMITTANCE 1. SCOPE The material defined by this specification is a knitted polyester fabric. 2. APPLICATION This specification was released originally as a Sunshade fabric with 30% light transmittance for D472 2011 DOOR WINDOW GLASS. 3. REQUIREMENTS In addition to the

3、 requirements listed herein, this material shall meet the SDS requirements of Manual Sunshade Assembly as applicable. When used on the intended application, the material must be capable of performing satisfactory under all production and service conditions. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION M

4、ATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Corporate Design master sample, or shall be as specified on engineering

5、 drawing 3.3 WEIGHT, g/m2, (FLTM BN 106-01) Fabric 122 +/- 10 3.4 THICKNESS, mm 0.37 +/- 0.03 (ASTM D 1777) 3.5 COMPOSITION (ASTM D 276/ASTM D 629) Fabric 100% Polyester ENGINEERING MATERIAL SPECIFICATION WSS-M5H35-A Copyright 2014, Ford Global Technologies, LLC Page 2 of 3 3.6 FABRIC CONSTRUCTION 3

6、.6.1 Stitch Count +/- 5% tolerance (ASTM D 3887) Wales 120 per 10 cm Courses 260 per 10 cm 3.6.2 Yarn construction (ASTM D 1244) Face 5 tex f24 5 tex f24 5 tex f24 Or as approved by Ford Materials Engineer and specified on Approved source List 3.6.3 Method of Dyeing solution dye 3.7 STRENGTH PROPERT

7、IES 3.7.1 Breaking Strength, N min (ASTM D 5034, grab method, 300 mm/min) Wales 200 N Courses 500 N 3.7.2 Retained Breaking strength after Xenon exposure (FLTM BO 116-01, 451 kJ/m2) Wales 30% Courses 30% 3.8 RESISTANCE TO MILDEW No Mildew (7 days at 38 C and 98% RH) 3.9 WEAR PROPERTIES 3.9.1 Taber A

8、brasion 200 cycles (SAE J948 CS10 wheels, 500g load) No distortion or color change 3.9.2 Resistance to Scuffing 25 cycles (SAE J365, A head) No distortion or color change 3.10 COLOR PROPERTIES 3.10.1 Resistance to Fade Rating 4 (SAE J2412, AATCC Procedure 1 488.8 kJ/m2) or Resistance to Fade Rating

9、4 (FLTM BO 116-01, AATCC Procedure 1 977.6 kJ/m2) ENGINEERING MATERIAL SPECIFICATION WSS-M5H35-A Copyright 2014, Ford Global Technologies, LLC Page 3 of 3 3.10.2 Heat Aging Rating 4 (7 days at 110 C, AATCC Procedure 1) 3.10.3 Soiling and Cleanability (FLTM BN 112-08, ISO 105-A02/AATCC Evaluation Pro

10、cedure 1) After Cleaning, min Rating 3 3.11 ODOR, max (FLTM BO 131-03) Rating 3 3.12 FOGGING (SAE J1756, 3 h at 100 C heating, 21 C cooling plate, post test conditioning 16 h) Fog number, min 70 Formation of clear film, droplets or crystals is cause for rejection. 3.13 FLAMMABILITY 100mm/min (SAE J369/ISO 3795)