FORD WSS-M7C79-B-2011 CAVITY WAX CORROSION PROTECTION AUTOMOTIVE CAVITIES SOLVENT BASED 80% SOLIDS TO BE USED WITH FORD WSS-M99P1111-A 《防腐自动腔体溶剂的80%固体腔体蜡 与福特WSS-M99P1111-A 一起使用.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 00 2011 07 13 Activated New Specification U.Mueller, FOE Controlled document at www.MATS Copyright 2011, Ford Global Technologies, LLC Page 1 of 2 CAVITY WAX, CORROSION PROTECTION WSS-M7C79-B AUTOMOTIVE CAVITIES SOLVENT BASED, 80% SOLIDS

2、1. SCOPE The material defined by this specification is solvent based rust preventive compounds and contain an UV- marker. 2. APPLICATION This specification was originally released for cavity waxes sprayed into box sections below the floor panel (rocker panel, side and cross members, etc.), in the en

3、gine compartment and to lower areas of pillars, doors, hood and tailgate. They are applied to the vehicle body after the paint process, prior to final assembly. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Stand

4、ard Requirements for Production Materials (WSS-M99P1111-A). 3.2 MATERIAL PROPERTIES 3.2.1 Non Volatile Content 80% (+/-2%) (FLTM BI 102-01) 3.2.2 Rheology A flow diagram to identify the characteristic properties of the material shall be added to the Initial Sample Report, together with a list of the

5、 relevant test parameter (temperature, shear rate, time, etc.) and equipment details 3.2.3 Creeping Power (FLTM BJ 128-02, Method A) At 23C 20mm (+/-2mm) min At 60C 35mm (+/-2mm) min 3.2.4 Drying After drying the (Film thickness on test panels 35 +/- 5 m) material must be drip free. Drying Time (23

6、+/- 2 C for 5 minutes) ENGINEERING MATERIAL SPECIFICATION WSS-M7C79-B Controlled document at www.MATS Copyright 2011, Ford Global Technologies, LLC Page 2 of 2 3.2.5 Storage Stability 6 months at 32 C 3 months at 40 C General storage must be frost free. After the storage, the material shall not show

7、 separation or coagulation and must meet all specification requirements. 3.3 PERFORMANCE PROPERTIES Wax according to these specifications must meet all requirements of WSS-M21P35-A2. 3.4 REMOVAL The wax film must be removable from automotive topcoats and application facilities at any time without da

8、maging the painted surface. The supplier must recommend a suitable solvent/cleaner process in the Initial Sample Report. Relevant topcoat systems are: Body enamel, catalyzed repair enamel, plastic paint, repair paint materials. 4. GENERAL INFORMATION The information given below is provided for clari

9、fication and assistance in meeting the requirements of these specifications. 4.1 MATERIAL REFERENCE All related materials used for approval of cavity wax according to this specification, e.g. substrate, paint materials, solvents, etc. as well as the application parameter (Density at 23 C, Flash point, viscosity curves, film thickness, drying conditions and Flow rate at (FLTM BJ 128-01, apply 0.1ml droplets) shall be noted in the Initial Sample Report of the wax.