FORD WSS-M8A19-A5-2008 BEARINGS ALUMINUM SILICON STEEL BACKED TO BE USED WITH FORD WSS-M99P1111-A 《轴承 铝硅钢靠背(协同FORDWSS-M99P1111-A一起使用)》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Ver. 1 2008 06 25 Activated O. Garcia, FNA Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 BEARINGS, ALUMINUM SILICON STEEL BACKED WSS-M8A19-A5 1. SCOPE The materials defined by these specifications a

2、re aluminum-silicon bearing alloys bonded to a low carbon steel backing. 2. APPLICATION This specification was released originally for material used in the manufacturer of bearings and bushing for automotive applications. Uses include crank main, connecting rod, balance shaft and thrust washer beari

3、ngs and bushings of medium load. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 CONSTRUCTION The functional layer shall be cast or sintered into

4、 a wrought strip and roll-bonded onto a prepared steel backing (bonding coatings of nickel or aluminum up to 75 micrometers thickness allowed). 3.3 CHEMICAL COMPOSITION (weight %) 3.3.1 Steel Backing Cold rolled carbon steel (0.03 0.25% carbon) ENGINEERING MATERIAL SPECIFICATION WSS-M8A19-A5 Printed

5、 copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC. Page 2 of 2 3.3.2 Functional Layer Tin 8.0 10.8 Copper 0.7 0.9 Iron 0.7 max Silicon 2.2 2.8 Chromium .15 - .25 Lead 0.1 max Manganese - Total Others 0.50 max Aluminum Balance 3.4 ADHESIVE The bond between the bearing layer and t

6、he steel backing must withstand the following test: A sharp chisel with a cutting width of 10 mm minimum and a cutting angle of 40 - 50 will be forced at an angel of 30 - 60 between the bearing layer and the steel backing. The cutting motion of the chisel is in a direction which tends to pull the be

7、aring layer away from the backing. The bearing layer must not flake or spall. 3.5 HARDNESS (The average of 5 determinations Minimum on the bimetal strip) (ASTM E 92/ASTM E 10) HV 49 minimum Or HB 45 minimum Note: The maximum hardness will be part of the Control Plan, and shall be stated on Engineeri

8、ng Drawing following sample manufacture. 3.6 MICROSTRUCTURE The functional layer consists of a uniform distribution of silicon particles in an aluminum rich solid solution matrix, and shall be bonded to the steel backing with no bonding or interface defects when viewed at 100 times magnification. No

9、 silicon particle shall have any dimension greater then 15 microns. A1/A2 shall have lead constituents in the aluminum rich solid solution matrix, while A3/A4 shall have no lead constituents. 3.7 MECHANICAL PROPERTIES The mechanical properties of the steel backing shall be controlled directly or indirectly (e.g. hardness) as part of the control plan to ensure consistent installation and functional characteristics.