GME QK 000574-2014 Polypropylene EPDM-Blend (Issue 3 English German This standard may be applied only for current programs It is inactive for all future projects and without replacw .pdf

1、EUROPEENGINEERINGSTANDARDSMaterialSpecificationLIMITED USEQK 000574Polypropylene/EPDM-BlendNOTE: This standard may be applied only forcurrent programs. It is inactive for all futureprojects and without replacement.If this product should be used for a newproject, a Re-Certification according toGMW157

2、02 is required.Polypropylen/EPDM-BlendHINWEIS: Diese Spezifikation darf nur noch frlaufende Projekte angewendet werden und istfr alle zuknftigen Projekte ohne Ersatz ungl-tig.Falls dieses Produkt fr ein neues Projekt zumEinsatz kommen soll, ist eine Neu-Zertifizierungnach GMW15702 erforderlich. Copy

3、right 2014 General Motors Company All Rights ReservedOctober 2014 - Issue No. 3 Page 1 of 11 Release and Revisions 1 Freigabe und nderungenThis standard was first approved and released inJune 1989.Diese Vorschrift wurde erstmalig genehmigt undfreigegeben im Juni 1989.Issue /AusgabePublication Date /

4、AusgabedatumDescription (Organization) /Beschreibung (Organisation)3 OCT 2014 Limited Use Status (GME Cross Carline Specifications)ADAM OPEL AG - TEZ ILL Werkstoff-Entwicklung Material-Develooment Material-Development and Testing Techn. Lieferbedingungen fiir Werkstoffe ENGINEERING - MATERIAL SPECIF

5、ICATION QKOOO 574 Polypropyfen/EPDM-Blend Polypropylene/EPDM-Blend Werkstoff: Pdypropyien/EPDM-Blend (PP/EPDM). Material: Pdypropyiene/EPDM-blend (PP/EPDM). Vetwendung: Application: Handelsname: Trade Name: Lieferant: Supplier: Lieferform: Form of Delivery: SprftzgieDtype zur Herstellung technischer

6、 Teile mit hoher Schlagzahig- keit such in der Glte, z. B. Verkleidung-StoBfanger. Injection moulding type for manufacturing technical parts requiring high impact strength also at low temperatures, e. g. facia-bumper. Moplen SP 179 Montedison Deutschland GmbH, D - 6236 Eschborn Granulat Granules &us

7、fertigungs-Nr.: 2 Datum: Z/90 Ausgefertigt: Issue: Date: Prepared: $& w 4L Genehmigt: J k Seite 1 von 4 Approved: Page of Unbeschadet etwaiger durch den Abnehmer erfolgenden Stichprobenprufungen tragt der Lieferant die Verantwortung dafur, daf3 die gelieferte Ware die Opel-Zeichnungsvorschriften erf

8、ullt Ein Prufbericht mit zahlenmaBigen Ergebnissen aus Prufungen der Lieferung selbst ist bei jeder Bemusterung, Erstbelieferung und Aus- fijhrunasanderuna mitzuaeben. Despite spot checks possibly perfromed by Opel, it is the suppliers responsibility that the delivered parts are in line with the Ope

9、l dra- wings. Deliveries of samples, first off-tool parts and pat-t&whose performance has been changed, must be accompanied by a test report showing the test results in terms of figures. Opel Form. 66 174-l E WD 1 88 QK 000 574 Forderungen/Requirements a) zu dokumentierende Eigenschaften/values for

10、documentation Dichte Density 2 0,900 s/cm” DIN 53 479 Schmelzindex MFI 230/2,16 Melt Flow Index MFI 230/2,16 7 bis 9 g/l0 min DIN 53 735 Elastizittitsmodul aus dem 3-Punkt-Biegeversuch 1750 Modulus of Elasticity by the N/mm2 DIN 53 457 3-Point-Flexural Test Vicat Erweichungstemperatur Vicat Softenin

11、g Temperature DIN 53 460 VST/A/50 2 +132 “C VST/B/50 2 +50 “C Kerbschlagztihigkeit DIN 53 453 Notched Impact Strength Norm-Kleinstab/ bei/at +23”C o. Br./no breakage Standard small rod - 20C 17 kJ/m 2 IS0 179/2 c b) nur zur Information/only for information HWe Hardness (63&3) Shore D DIN 53 505 Zugf

12、estigkeit 2 17 N/mm2 )DIN 53 455, Tensile Strength )Probekorper 3 )Test piece 3 ReiBdehnung 1300 % )v/speed = Elongation at Break )50 mm/min Kerbschlagzahigkeit nach lzod ASTM D 256 lzod Notched Impact Strength bei/at +23”C 500 J/m 0C 150 J/m - 20C 100 J/m Schlagzahigkeit nach lzod lzod Impact Stren

13、gth ASTM D 256 bei/at - 20C o. Br./no breakage Formbestandigkeit in der WBrme, Temperature of Deflection under DIN 53 461 Load Verfahren/Method A 1 +45 “C Verfahren/Method B 2 +72 “C Umweltschutz nach QU 000 001 - Cadmium. Environmental Protection to QU 000 001 - Cadmium. Ausfertigungs-Nr.: 2 Datum:

14、 2/90 Seite 2 von 4 Issue: Date: Page of Ooel Form. 66 166-1 A4 WD 1 88 ADAM OPEL AG QK 000 574 Hinweis Weitere Informationen siehe QK 000 000. Reference For further information refer to QK 000 000. Bemerkung Alle Probekdrper werden im Spritzgiel3verfahren hergestellt. Note All test pieces shall be

15、manufactured by injection moulding. Abfallbeseitigung: Gruppe D, Opel-Betriebsrichtlinie 440 Waste Disposal: Group D, Opel-Plant Directive No. 440 I Ausfertigungs-Nr.: 2 I Datum: z/90 Issue: Date: I Ausgefertigt: Prepared: Opel Form. 66 166-l AA WD 1 88 ADAM OPEL AG QK 000 574 12.02.9(: OatUrn Date

16、-1 I Content revised according to new suppliers datas, rewritten Be2 Sym. was Issue 1, Date of Issue 6/89 lnhalt nach Lieferantenangaben ijberarbeitet, neu geschrieben war Ausfertigungs-Nr. 1, Datum 6/69 Beschreibung / Description Anderungen I Revisions - in Checked APP. Ausfertigungs-Nr.: Datum: OdFom.66166-1 C WD ADAM OPELAG