GMKOREA EDS-T-7041-2008 THE TEST METHOD OF INSTRUMENT PANEL.pdf

1、GM DAEWOO Auto & Technology EDS Engineering, GM DAEWOO Auto & Technology Standards THE TEST METHOD OF INSTRUMENT PANEL Do Not Use on New Programs. Being Replaced by GMW14117&GMW14444 EDS-T-7041 ISSUED DATE: 1997. 01. 16 REVISED DATE: 2008. 10. 15 VERSION: 4 (Superceded) EDS-T-7041THE TEST METHOD OF

2、INSTRUMENT PANEL PAGE: 1/5 ISSUED DATE: 1997. 01. 16 REVISED DATE: 2008. 10. 15 VERSION: 4 GM DAEWOO Auto & Technology Note: This standard may be applied only for current project (incl. T255 Program). It is Superceded for all future projects and replaced by GMW14117 & GMW14444. 1. PURPOSE This speci

3、fication determines test methods and requirements of instrument panel.(hereafter I/P) 2. SCOPE This standard is applied to test of instrument panel used for GMDAT-manufactured vehicle (passenger car, multipurpose car, truck and bus, etc.) 3. TYPE Table 1. I/P Type Type Division Description Type 1 Fu

4、ll pad Foaming and skin material covered on plastics or steel core. Type 2 Padless (organic-coated) Organic coated plastics, without foaming and skin material Type 3 Padless Only plastics, without foaming and skin material 4. APPROVAL The instrument panel released to this specification shall be the

5、same as the approved products. If any changes happen to the approved specimen, GMDAT Technical centers approval is needed. But, test samples for DVP(Design Verification Plan) can be discussed separately. 5. REQUIREMENT 5.1. General requirement Unless otherwise specified in drawings or material speci

6、fications, released parts shall be used without any precondition. But, type 2 shall be tested 72 hrs after coating and drying. 5.2. Detailed requirement By conducting the tests to the clause 6, the detailed requirements in the Table 2, 3 shall be satisfied. Table 2. Detail requirement (Type 2) Requi

7、rements Test Items Test Methods Type 1 Type 2 Type 3 RemarksAdhesion EDS-T-7780-B - No minimum 90% of peel - Scratch resistance EDS-T-7758(4N) - No scratch on coating layers - Dry film thickness - Written in DWG EDS-T-7041THE TEST METHOD OF INSTRUMENT PANEL PAGE: 2/5 ISSUED DATE: 1997. 01. 16 REVISE

8、D DATE: 2008. 10. 15 VERSION: 4 GM DAEWOO Auto & Technology Table 3. Detailed requirement (Type 1, 2, 3) Requirements Test Items Test Methods Type 1 Type 2 Type 3 Remarks Temperature resistance 6.2 - No foam, wrinkle, color and surface change and cracks - Any size changes shall not adversely affect

9、the serviceability of the part Min. 4 grade of gray scale Min. 4 grade of gray scale Min. 4 grade of gray scale Resistance to heat aging - color change - other changes 6.3 No foam, winkle, gloss loss and cracks I/P of type 1 shall be tested with forming material attached on the rear side. Min. 4 gra

10、de of gray scale Min. 4 grade of gray scale Min. 4 grade of gray scale Light resistance - color change - other changes 6.4 No melting of organic component, blackening and gloss loss. Chemical resistance - grease - engine oil - antifreeze liquid - liquid soap - leather wax 6.5 No softening, swelling,

11、 color change - 5.3. Additional requirement Additional requirement other than clause 5 shall be specified in related drawings. 6. TEST METHODS 6.1. General requirement 6.1.1. Standard conditions of lab. Standard temperature and humidity shall be 232, 505%. But, the lab is not in standard conditions,

12、 record the test temperature and humidity. 6.1.2. Pretreatment Test samples shall be stored minimum 72 hrs since their production, and proper pretreatment shall be done according to the detailed test method. 6.1.3. Sample quantity According to test methods, completed products or a part of the produc

13、ts shall be used for a test sample. Minimum 3 pieces are needed for approval test and minimum 1 piece each for quality examination and incoming inspection. 6.2. Temperature resistance 6.2.1. Test apparatus (1) Forced air circulation oven which can keep required temperature at 2.5 K. EDS-T-7041THE TE

14、ST METHOD OF INSTRUMENT PANEL PAGE: 3/5 ISSUED DATE: 1997. 01. 16 REVISED DATE: 2008. 10. 15 VERSION: 4 GM DAEWOO Auto & Technology (2) Cold chamber which can keep temperature down at -40. (3) Hot chamber unit(infrared radiation irradiated chamber) which temperature is controllable from a room tempe

15、rature up to 150. 6.2.2. Test shall be conducted on completed products and test conditions are as follows: (1) Type 1 of I/P After placing I/P in the infrared rays test chamber at 120 of surface temperature and 90 of atmosphere temperature for 4 hrs, cool it to the room temperature and repeat this p

16、rocess three times. Conduct the following test : 4095% RH24 hrs -4024 hrs 9024 hrs. (2) Type 2, 3 of I/P After placing I/P in the infrared rays test chamber at 115 of surface temperature and 85 of atmosphere temperature for 4 hrs, cool it to the room temperature and repeat this process three times.

17、Conduct the following test : 4095% RH24 hrs -4024 hrs 9024 hrs. 6.2.3. Determinations Unless otherwise specified in drawings, the detailed requirements of the Table 2, 3 in clause 5.2 shall be followed. 6.3. Heat aging resistance 6.3.1. Test apparatus Forced air circulation oven which can keep requi

18、red temperature at 2.5 K. 6.3.2. For a test sample, more than three samples of min. 300 mm 300 mm which are taken from a completed product shall be used. The test sample shall be heat aged in the oven at 110 for 500 hrs, cooled to the room temperature, and visually checked. 6.3.3. Determinations Unl

19、ess otherwise specified in drawings, the detailed requirements of the Table 2, 3 in clause 5.2 shall be followed. 6.4. Light resistance 6.4.1. Test apparatus : Light exposure equipment(xenon-arc type) described in 5.1 of EDS-T-7415. 6.4.2. More than three samples of min. 50 150 mm which are taken fr

20、om a flat part of a completed product shall be tested under the below conditions : (1) Black panel temperature : 80 (2) Strength : 0.55 W/m2(3) Lamp power consumption : 6,000 W (4) Test time : 1240.8 KJ/m26.4.3. Determinations Unless otherwise specified, the detailed requirements of Table 2, 3 in cl

21、ause 5.2 shall be followed. 6.5. Chemical resistance EDS-T-7041THE TEST METHOD OF INSTRUMENT PANEL PAGE: 4/5 ISSUED DATE: 1997. 01. 16 REVISED DATE: 2008. 10. 15 VERSION: 4 GM DAEWOO Auto & Technology 6.5.1. More than three samples of min. 50 100 mm which are taken from a completed product shall be

22、tested under the below conditions : (1) Using a solution-soaked gauze, rub the sample lightly three times and expose the sample for 24 hrs. Remove the solution and check the surface. (2) Test solution : grease, engine oil, antifreeze liquid, 3% sulfuric acid, liquid soap, leather wax. 6.5.2. Determi

23、nations Unless otherwise specified, the detailed requirements of Table 2, 3 in clause 5.2 shall be followed. 6.6. Vibration characteristic test The test shall be mainly for DVP test. For PVP test, it shall be discussed with the design department. 6.6.1. Test apparatus (1) Vibration tester (2) Hot/Co

24、ld chamber 6.6.2. Test method (1) Mount a test sample and vibration test-related components(cluster, steering column, ashtray, HVAC system etc.) on the jig(or cut body) and conduct the test. (2) The jig shall have enough rigidity not to generate its own resonance. (3) Vibration method and temperatur

25、e conditions are as follows : Temperature Room temperature (202) Hot temperature(602) Cold temperature(-202)Remarks Vibration direction Upward/downward Vibration acceleration Max. 0.5 G(4.9 m/s2)Vibration frequency 550 Hz Vibration sweep time 510 minute - Room temperature Hot temperature Cold temper

26、ature - One reciprocating time 6.6.3. Determinations Unless otherwise specified in drawings, the following shall be met. (1) Resonance points shall be min. 35 Hz at the room temperature. (2) At 550 Hz, there shall be no noise. 6.7. Vibration durability test The test shall be mainly for DVP test. For

27、 PVP test, it shall be discussed with the design department. 6.7.1. Test apparatus (1) Vibration tester (2) Hot/Cold chamber 6.7.2. Test method (1) Mount a test sample and vibration test-related components (cluster, steering column, ashtray, HVAC system EDS-T-7041THE TEST METHOD OF INSTRUMENT PANEL

28、PAGE: 5/5 ISSUED DATE: 1997. 01. 16 REVISED DATE: 2008. 10. 15 VERSION: 4 GM DAEWOO Auto & Technology etc.) on the jig (or cut body) and conduct the test. (2) The jig shall have enough rigidity to generate its own resonance. Also, when accelerating at 15 Hz, 1 G(9.8 m/s2), the vibrator acceleration

29、shall be within 10.1 G(9.80.98 m/s2). (3) Vibration method and temperature conditions 1 cycle consists of the following vibration. Changing the acceleration from the lower to the higher, a total of 12 cycles shall be performed, which are 6 cycles at the room temperature, 3 cycles at the hot temperat

30、ure(602) and 3 cycles at the cold temperature(-202). Vibration order Acceleration Number Time Remarks 1 0.6 G(5.9 m/s2) 6 10466 min. 40 sec. 2 1.0 G(9.8 m/s2) 2.5 10427 min. 46 sec. 3 1.4 G(13.7 m/s2) 7 1037 min. 46 sec. 4 1.8 G(17.7 m/s2) 1.5 1031 min. 40 sec. 5 2.4 G(23.5 m/s2) 3 10220 sec. -Direc

31、tion : upward/downward - Frequency : 15 Hz - constant 6.7.3. Determinations Unless otherwise specified in drawings, the measurement items before and after the test are as follows. (1) Resonance frequency : to be measured with a accelerometer (2) Test samples shall hot show no shakes, cracks, breaks,

32、 detachment, abrasion, looseness, shape change, and noise. : to be checked visually and using a scale. 7. ADDITIONAL REQUIREMENT 7.1. The test for a glove box equipped to a instrument panel shall conform to EDS-T-4101. 7.2. The test for a ashtray equipped to a instrument panel shall conform to EDS-T

33、-4102. 7.3. The test for a cup holder equipped to a instrument panel shall conform to EDS-T-4103. 7.4. The test for a ventilation grill equipped to a instrument panel shall conform to EDS-T-4605. 7.5. Other test requirements and test methods for other parts are specified in related drawings. 8. DEVIATIONS Deviations from the above standards or other additional requirements shall be specified in drawings and test certificates or reports.