HOLDEN HN 1242-1972 Tape Wiring Harness《线束胶带》.pdf

1、A.C.N. 006 893 232Holden LimitedEngineering DepartmentMATERIAL SPECIFICATIONNUMBERSHEETRELEASEREVISION:HN 12421 of 2February, 1972October, 1972NAME: TAPE WIRING HARNESSTHIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TOTHE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TOCONFIRM THE DOCUMEN

2、T ISSUE DATE IS STILL VALID.FORM : I:LABRTORYFORMSTDMATSPEC.DOC1. APPLICATION:This specification covers a synthetic tape used for the outer covering of wiringharnesses by hand or machine wrapping.2. GENERAL REQUIREMENTS:The tape shall be a plasticised vinyl resin film and shall be resistant to abras

3、ion,oil, water and acid and is normally smooth and non-adhesive.3. SPECIFIC REQUIREMENTS:Tests conducted at 25oC unless otherwise noted.3.1 AppearanceThe tape shall be free from pinholes, hard or foreign particles,tears orcuts.3.2 ColourAs specified on Part Drawing.3.3 FinishGloss and smooth3.4 Tens

4、ile StrengthThe minimum tensile strength shall be 10,300 kPa (1500 p.s.i.) whentested in accordance with ASTM D412.3.5 Ultimate ElongationThe minimum ultimate elongation shall be 250% when tested inaccordance with ASTM D412.A.C.N. 006 893 232Holden LimitedEngineering DepartmentMATERIAL SPECIFICATION

5、NUMBERSHEETRELEASEREVISION:HN 12422 of 2February, 1972October, 1972NAME: TAPE WIRING HARNESSTHIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TOTHE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TOCONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID.FORM : I:LABRTORYFORMSTDMATSPEC.DOC3. SPECIFIC R

6、EQUIREMENTS: (continued)3.6 Elongation at 6890 kPa (1000 p.s.i) load.The elongation at 6890 kPa (1000 p.s.i.) shall be in the range of 80 -325% when tested in accordance with ASTM D412.3.7 ThicknessThe thickness shall be 150 - 230 m (0.006 - .009 inches).3.8 Width - 0 (-0 )The width of the tapes sha

7、ll be within + 1.6 mm (+1/16) inches of specifiedwidth. The individual widths should be specified on the purchase order.3.9 Specific GravityThe specific gravity shall be 1.25 maximum when tested in accordancewith ASTM D792.3.10 Dielectric StrengthThe dielectric strength shall be 700 v.p.m. minimum when tested inaccordance with ASTM D1000.3.11 Heat AgeingThe tape shall not be brittle or crack after ageing 7 days at 70oC.4. APPROVAL: )CERTIFICATION: ) Refer Clauses B C and G of) Specification HN 1000.INSPECTION AND REJECTION: )