HOLDEN HN 1555-2009 FILM ADHESIVE - PRESSURE SENSITIVE ACRYLIC《胶膜 压敏型压克力》.pdf

1、ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN1555 1 of 6 February, 1978October, 2009 NAME: FILM ADHESIVE - PRESSURE SENSITIVE ACRYLIC THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIE

2、NT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 1. SCOPE A form of pressure sensitive adhesive dry film protected with release paper. The thickness of this material is sufficient to

3、 adhere satisfactorily to textured or uneven surfaces plus where some surface mismatch exists. There are two types described in this specification. Type A is primarily intended for exterior application or where maximum adhesive shear strength and high temperature properties are important. It may be

4、applied to painted surfaces, plated surfaces, glass or plastics (excluding polyolefins). Type B is intended for interior use and with the capability of adhering to similar surfaces as Type A but with lower adhesive shear strength and holding properties. Type B also have a capability of adhering to p

5、olyolefin surfaces. 2. REFERENCES GM9010P ASTM D3330 PSTC101D PSTC-7 PSTC-4B ASTM D3652 ASTM 3654 HN 1000 GMW3059 3. REQUIREMENTS 3.1 Table 1 Properties Values Test Method TYPE A TYPE B Thickness of Adhesive 0.11 - 0.15 mm 0.04 - 0.15 mm Thickness of Liner 0.08 mm Nominal 0.08 mm Nominal Solids Cont

6、ent 98 % minimum 98 % minimum GM9010P 90 Peel Adhesion to Stainless Steel 1500 N/m minimum 600 N/m minimum ASTM D3330 PSTC101D Holding Power 1440 minutes minimum 23 C30 minutes minimum 23 C PSTC-7 Liner Removability 50 N/m maximum 50 N/m maximum PSTC-101D PSTC-4B ABN 84 006 893 232 GM Holden Limited

7、 Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN1555 2 of 6 February, 1978October, 2009 NAME: FILM ADHESIVE - PRESSURE SENSITIVE ACRYLIC THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOC

8、UMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 3. REQUIREMENTS (continued) 3.2 Form and Quality Shelf Life. Material shall pass all requirements of this specification after ageing material in the original container 9

9、0 days at 35C. 3.3 Test Procedures 3.3.1 Conditioning The rolls shall be conditioned and specimens selected in accordance with PSTC Appendage D. 3.3.2 Specimen Preparation Each specimen to be used for testing in 3.3.4 and 3.3.5 shall be prepared in the following manner: Laminate the adhesive to a su

10、itable size strip of aluminium foil. Prior to conducting the actual test remove the liner. This gives a strip of tape with the adhesive on 1 side of an aluminium foil backing. 3.3.3 Thickness The adhesive thickness shall be determined according to ASTM D3652. 3.3.4 Adhesion The initial adhesion of s

11、pecimens prepared in 3.3.2 shall be determined in accordance with ASTM D3330 or PSTC101D. A constant rate of extension type instrument with a 300 mm/minute crosshead speed shall be used in lieu of the pendulum type instrument. Tapes should be tested at a 90 angle on a stainless steel panel after 72h

12、 dwell, aluminium foil backing should be used. Peel at 305 mm/minute. ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN1555 3 of 6 February, 1978October, 2009 NAME: FILM ADHESIVE - PRESSURE SENSITIVE ACRYLIC THIS DOCUMENT MUST NOT B

13、E REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 3. REQUIREMENTS (continued) 3.3 Test Procedures (continued) 3.3

14、5 Holding Power The holding power test on specimens as prepared in 3.3.2 shall be conducted as specified in ASTM D3654 and PSTC-7. The time in minutes for the specimen to separate completely from the panel shall be used to determine its qualification as per requirements listed in this specification

15、 Samples should be 12.7 x 12.7 mm tested on a stainless steel test panel after 72 h dwell, aluminium foil backing should be used. Load with a 1000 g mass. 4. APPROVAL, INSPECTION AND REJECTION Refer HN 1000, Clauses A and C. 5. HAZARDOUS MATERIALS Refer HN 1000, Clause H. 6. RESTRICTED AND REPORTAB

16、LE SUBSTANCES (i) All substances and parts must meet the requirements of GMW3059. (ii) All chemical components present in materials supplied to this specification must comply with Australian NICNAS (National Industrial Chemicals Notification and Assessment Scheme) obligations. ABN 84 006 893 232 GM

17、Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN1555 4 of 6 February, 1978October, 2009 NAME: FILM ADHESIVE - PRESSURE SENSITIVE ACRYLIC THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO C

18、ONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 7. APPROVED SUPPLIERS AND MATERIALS Material known to meet the full requirements of this specification: APPROVED MATERIALS APPROVED SUPPLIER Type A No. 468

19、 “Scotch Brand Nameplate Adhesive Transfer Tape 3M FAS Tape 1125 HL Avery Dennison Type B C3 Cling Adhesive Products 39 Northgate Drive, Thomastown 501 L 5000NS Nitto Denko Y9485PC Adhesive Tape Transfer 3M 9786 Adhesive Tape Transfer 3M CT 6348 Tissue Tape 3M FT 9220 Avery Dennison FT7271 Avery Den

20、nison 3688 Venture Tape Radical 1252 Radical 1253 Radical 1254 Radical 2252 Radical 3252 INC Corporation ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN1555 5 of 6 February, 1978October, 2009 NAME: FILM ADHESIVE - PRESSURE SENSITI

21、VE ACRYLIC THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 8. REVISIONS April, 1996 - W

22、ater Resistance & Adhesion Requirements amended - Avery Dennison and Nitto - Denko added as approved suppliers November, 1997 - Hazardous Materials and Restricted Chemical clauses added. - 90 oPeel Adhesion Specification amended. January, 1998 - Type A and B introduced in Clause 1. - Table 1, Types

23、A and B Added. - Approved Material and Suppliers divided into Types A and B. Avery Dennison and Venture Tapes added for Type B - Initial Source Approval Clause deleted. September, 2000 - Formatting corrections. August, 2001 - New approved supplier added, peel strength requirement increased. November

24、 2001 - Test methods updated - Type B thickness range changed - Trademark added to product names. August, 2005 - Added Adhesive Tape Transfer 9786 (to Type B) in section “7.APPROVED SUPPLIERS AND MATERIALS”.March, 2006 - Added Adhesive Tape Transfer FT7271(to Type B) in section “7.APPROVED SUPPLIER

25、S AND MATERIALS”.October, 2007 - Revised section “6.RESTRICTED AND REPORTABLE SUBSTANCES” to directly refer to GMW3059 and NICNAS requirements. - Section “7. APPROVED SUPPLIERS AND MATERIALS”, Type B. -added approved material Radical 1253 ABN 84 006 893 232 GM Holden Limited Engineering Department M

26、ATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN1555 6 of 6 February, 1978October, 2009 NAME: FILM ADHESIVE - PRESSURE SENSITIVE ACRYLIC THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL

27、 VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 8. REVISIONS (continued) June, 2008 - Section “7. APPROVED SUPPLIERS AND MATERIALS”, Type B. -added Tissue Tape CT6348. October, 2009 - Section “7. APPROVED SUPPLIERS AND MATERIALS”, Type B. - added Adhesive Tape 5000NS Prepared by : Y. Zia