HOLDEN HN 2116-2009 SEALER - PLASTISOL - EXTERIOR - ENAMEL《密封胶 搪瓷外部塑料溶胶》.pdf

1、ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2116 1 of 9 April, 1993May, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPO

2、NSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 1. GENERAL DESCRIPTION This specification covers a plastisol type sealer, capable of being applied directly over ELPO primed surfaces, and inten

3、ded for sealing body joints. It is used under exterior enamel painted surfaces. The sealer shall be a contrasting colour to ELPO primer. It shall be smooth, homogeneous, and free from lumps and unmixed particles. It shall be compatible with wet primer surface and GM Holden enamel paint systems. It s

4、hall cure in the primer surfacer oven into a tough, resilient seal. The sealer must be capable of being applied by extrusion gun or airless spray. It must also be capable of accepting up to 50% air by volume when used in conjunction with the Nordson Foam Mix System. The applied bead may be brushed w

5、here necessary and should be removable with a dry cloth. 2. DETAILED REQUIREMENTS 2.1 Odour The sealer must not be toxic or noxious. After curing it must be relatively non-odorous. 2.2 Stability The shelf life of the material shall be 90 days at a temperature not to exceed 35 C. Shelf life of materi

6、al commences upon receipt of the material at the assembly plant. Material at the end of this period must be capable of passing all the applicable requirements of this specification except viscosity which shall be a maximum of 60 seconds when tested as in clause 2.4. 2.3 Solids Content 93.0% by weigh

7、t minimum.ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2116 2 of 9 April, 1993May, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIEN

8、T IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 2. DETAILED REQUIREMENTS (continued) 2.4 Viscosity by Extruding Method Extrude 100g of material at 276kPa through a 1.32mm diameter x

9、13.5mm long orifice at 25 C. Release viscosity to be 60 - 70 seconds. 2.5 Sag 5 mm max. Test Method - Apply a bead of material 4.8 mm x 4.8 mm x 178 mm (3/16“ x 3/16“ x 7“) with a scraper to a 250 mm x 250 mm (10“ x 10“) primed panel. Set the test panel in the vertical position with the bead horizon

10、tal, air dry for 20 minutes. Bake the panel in the air dry position at 145 C 5 C for 30 minutes and measure the sag. Sag is the total width of the bead minus the width of the original bead. 2.6 Viscosity and Yield Stress (Sag) by Rheometer Method Release viscosity at 131 s-1to be 57-63 Poise and rel

11、ease Bingham Yield stress 400-460 Pa. Test Method Use a Physica MCR 300 rheometer fitted with CP-50-1 measuring system and a TEK 150P-C measuring cell. Run a rotational measuring profile as specified below. Set temperature constant at 25C and set measuring position at 0.05 mm. Record the viscosity a

12、t 131 s-1in Poise from the value measured in the final measuring point of interval 3. Calculated yield stress in Pa according to the Bingham rheological model with RS100/120 compatible error weighting using the shear stress and shear rate data for all data points in interval 4. ABN 84 006 893 232 GM

13、 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2116 3 of 9 April, 1993May, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE

14、 DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 2.6 Viscosity and Yield Stress (Sag) by Rheometer Method (continued) Measuring profile Interval 1 shear rate of zero for 2 minutes 18 seconds Interval 2 shear rate t

15、o increase in a linear ramp from 5 131 s-1over a time period of exactly 3 minutes; 30 measuring points to be recorded with 4.2s-1shear-rate intervals. Interval 3 Constant shear rate of 131 s-1over a time period of 3 minutes 20 seconds, 10 measuring points to be recorded at 20 seconds intervals Inter

16、val 4 shear rate to reduce in a linear ramp from 131 5 s-1over a time period of exactly 3 minutes; 30 measuring points to be recorded with 4.2s-1shear-rate intervals. 2.7 Coefficient of Expansion Volume change during cure +5% to -10%. Not applicable when used in conjunction with Nordson Foam Mix equ

17、ipment. Test Method - Use Aluminium coupons approximately 75 mm x 25 mm. Extrude an approximate 6 mm diameter bead of material on to the coupon. Calculate the volume of the sealer V1, by weighing in air and water. Cure the sealer by baking in an oven for 30 minutes at 145 C 5oC. Calculate the volume

18、 of the cured sealer V2, by weighing in air and water. Per cent Expansion = V2 - V1 x 100 V1 2.8 Pressure Stability The sealer must be capable of withstanding pumping pressure without adversely affecting the viscosity of the sealer. Material shall not cake or separate oil under pressure. ABN 84 006

19、893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2116 4 of 9 April, 1993May, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO C

20、ONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 2. DETAILED REQUIREMENTS (continued) 2.9 Characteristics of Cured Sealer The material must adhere to primed steel and be paintable with GM Holden current p

21、roduction enamel. It must have no plasticiser migration stain, and must not cause enamel cracking, or lose adhesion during and after the following environments: 14 days S-1 Sunlamp 14 days ageing at 70 C 6 months outdoor exposure at Townsville GM Corrosion Cycle (HN 0127) GM Cracking Cycle (HN 0127)

22、 7 days humidity (38 C, 100% R.H.) Panel Preparation - A 200 mm x 6 mm x 2 mm bead of sealer is applied to a 250 mm x 250 mm steel panel that has been coated with ELPO primer and baked. The panel and applied sealer is then sprayed with GM Holden current production enamel primer surfacer and baked at

23、 145 C for 1 hour. The panel is then sprayed with 2 coats of GM Holden current production top coat and baked at 145 C for 30 minutes. 2.10 Cold Resistance The material shall not crack enamel paint, nor lose adhesion prior to or after two 1.69 J (15 inch pound) impacts at -10 C. Panel preparation is

24、as described in Clause 2.8. The painted panel is cooled at -10 C for 4 hours and inverted and clamped in the impact fixture. Two impacts are made with 51 mm diameter (2“) steel ball weighing 535 grams.ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET REL

25、EASE REVISION : HN 2116 5 of 9 April, 1993May, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAn

26、dAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 2. DETAILED REQUIREMENTS (continued) 2.11 Corrosion Resistance The sealer when subjected to 200 C for 1 hour shall not show any corrosion on phosphated steel panels. The material shall be subjected to one week at 38 C 95% Relative Humidity to

27、evaluate corrosion susceptibility. 2.12 Material Characteristics Shear Strength (ASTM D1002) Panels 100 x 25 x 0.7 mm ELPO painted thickness of adhesive - 1 mm. Cure - 60 mins 145 C. Test after 4 hours - 1500 kPa. When foamed 50% through Nordson Foam Mix-690 kPa (100 psi) min. 2.13 Solvent Resistanc

28、e The cured painted sample shall show no harmful effects when wiped with a cheesecloth saturated with X55 solvent. Surface should remain wet with solvent for 10 minutes. Sample is then washed with water, dried and examined. The appearance of the painted sealer shall not be different from the surroun

29、ding painted panel. 2.14 Water Absorption - 1.5% Max. Test Method Weigh a test specimen approx. 25mm x 25mm x 6mm (obtained from Nordson Foam Mix equipment and containing 40 - 50 % air). Submerge in water at 25c for 48 hours. Carefully dry specimen and reweigh. ABN 84 006 893 232 GM Holden Limited E

30、ngineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2116 6 of 9 April, 1993May, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE D

31、ATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc 2. DETAILED REQUIREMENTS (continued) 2.15 Cell Size- Typical size shown in Fig. 1. Fig. 1 3. APPROVAL, INSPECTION AND REJECTION Refer HN 1000, Clauses A, C and G (Line Trial). 4. HAZ

32、ARDOUS MATERIALS Refer HN 1000, Clause H (Documentation submission only required if material supplied for direct use in GM Holden premises) 5. RESTRICTED AND REPORTABLE SUBSTANCES (i) All substances and parts must meet the compositional requirements of GMW3059. (ii) All chemical components present i

33、n materials supplied to this specification must comply with Australian NICNAS (National Industrial Chemicals Notification and Assessment Scheme) obligations. ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2116 7 of 9 April, 1993M

34、ay, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFor

35、msMatspec.doc 6. APPROVED SUPPLIERS AND MATERIALS Material known to meet the full requirements of this specification: APPROVED SUPPLIER APPROVED MATERIAL Henkel Australia Terolan 8510-13 7. REFERENCES HN 0127 ASTM D1002 HN 1000 GMW3059 8. REVISIONS August, 2002 -Corrected Page numbering. -Expanded S

36、ection 3 to Sections 3, 4 and 5 -Added Section 6, Approved Materials -General format editing for readability August, 2003 -Section 2.4 Viscosity requirement changed from 96-112 seconds (4 x 25-28s) to 115-140 seconds, the required viscosity for robot application. -Section 6 (APPROVED SUPPLIERS AND M

37、ATERIALS); Approved material name changed from Inco 7212 to Terolan 8500-13. -Revised section 2.8 (Characteristics of Cured Sealer) to make reference to Holden instead of GMHA. -Added section 7 (REFERENCES). August, 2005 -Section “2.DETAILED REQUIREMENTS”. - Section “2.4 Viscosity”. Revised conditio

38、ns. - Section “2.11 Material Characteristics” Revised conditions of test (Shear Strength). -Section “6.APPROVED SUPPLIERS AND MATERIALS”. Material updated from Terolan 8500-13 to Terolan 8510-13. ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE

39、REVISION : HN 2116 8 of 9 April, 1993May, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppe

40、aranceNBRspecific0AdminMgmtStandardFormsMatspec.doc 8. REVISIONS (continued) April, 2007 -Section “2.DETAILED REQUIREMENTS”. -Revised heading of section “2.4 Viscosity” to “2.4 Viscosity by Extruding Method” -Added section “2.6 Viscosity and Yield Stress (Sag) by Rheometer Method” to reflect measure

41、ments by Rheometer -Revised section “5.RESTRICTED AND REPORTABLE SUBSTANCES” to directly refer to GMW3059 and NICNAS requirements. May, 2009 -Section “2.DETAILED REQUIREMENTS”, Section “2.6 Viscosity and Yield Stress (Sag) by Rheometer Method” -Viscosity and Yield Stress values revised from 61-67 Po

42、ise and release Bingham Yield stress 430-480 Pa. to 57-63 Poise and release Bingham Yield stress 400-460 Pa. ABN 84 006 893 232 GM Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2116 9 of 9 April, 1993May, 2009NAME: SEALER - PLASTISOL - EXTERIOR - ENAMEL THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : S:EngBusProcessEngMaterialsMatlsAndAppearanceNBRspecific0AdminMgmtStandardFormsMatspec.doc Prepared By: Y. Zia