INTERN CEMS E-2-2008 Steel Castings Includes Appendix《钢铸件》.pdf

1、This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2008 by Navistar, Inc. AUGUST 2008 Page 1 of 13 NAVISTAR, INC. CEMS (CORPORATE ENGINEERING MATERIAL SPECI

2、FICATION) NUMBER: CEMS E-2 TITLE: Steel Castings CURRENT ISSUE DATE: August 2008 WRITTEN/REVIEWED BY: Materials Engineering APPROVED BY: Materials Engineering SUPERSEDES ISSUE OF: February 2002 PRINTED COPIES OF THIS DOCUMENT MUST BE VERIFIED FOR CURRENT REVISION This specification may involve hazar

3、dous materials, equipment, and procedures. This specification does not purport to address all of the safety issues associated with its use. The user is responsible to consult appropriate safety and health practices and to determine the applicability of regulatory limits prior to use. Change Notice:

4、Replaced “International Truck and Engine Corporation” with “Navistar, Inc.” per corporate directive; added CEMS B-50 requirement; updated reference documents; corrected Table I; updated Table III; editorial changes. 1.0 SCOPE This specification covers the Companys requirements for steel castings. 2.

5、0 INTRODUCTION Cast steels offer a wide range of properties, achievable by heat treatment, and are readily weldable at most strength levels. They offer good impact resistance but are less castable and more expensive than the gray cast irons. 2.1 Restricted Chemical Substances Effective January 1, 20

6、07, all product supplied to the requirements of this specification must comply with the requirements of the CEMS B-50 specification. 3.0 CONTENTS PAGE REFERENCE DOCUMENTS 1 GENERAL REQUIREMENTS 2 QUALITY 8 METHODS OF TEST 10 SOURCE APPROVAL AND QUALITY CONTROL 11 DESIGNATION ON DRAWINGS AND PURCHASE

7、 ORDERS 12 PACKING AND SHIPPING 12 APPENDIX - GENERAL INFORMATION (Green Sheets) 4.0 REFERENCE DOCUMENTS Unless otherwise specified, the latest issue of all referenced standards shall apply. The following standards, specifications and regulations are referenced in this specification. Quality System

8、Standard ISO 9001 or TS-16949 NAVISTAR EPS-91 NAVISTAR Manufacturing Standard MS-D-13 ASTM E 446 ASTM A370 NAVISTAR Manufacturing Standard MS-E-1A2 ASTM E 10 ASTM E 94 CFR Title 29, Part 1910 ASTM E 71 ASTM E 208 NAVISTAR CEMS AT-2 ASTM E 125 ASTM E 112 NAVISTAR EPS-143 ASTM E 709 SAE J435 Copyright

9、 Navistar International Corporation Provided by IHS under license with INTERNNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-NUMBER: CEMS E-2 TITLE: Steel Castings CURRENT ISSUE DATE: August 2008 This document is restricted and may not be sent outside Navistar, Inc

10、. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2008 by Navistar, Inc. AUGUST 2008 Page 2 of 13 5.0 CLASSIFICATION OR DESIGNATION Steel castings are classified on the basis of strength and heat treatment process. 6.0 GENER

11、AL REQUIREMENTS 6.1 Mechanical Properties The primary intent of this specification is to obtain castings with controlled mechanical properties. (Refer to Section 6.2 for chemical requirements.) All castings purchased to this specification will be supplied heat treated and have mechanical properties

12、conforming to Tables I, IA and II. Other required heat treatments and/or properties will be specified on the drawing. All heat treat agreements and specifications will remain in effect until mutually changed or terminated. 6.1.1 Castings - Normalized Or Normalized And Tempered Grades SC-0, 1, 2, and

13、 SC-3 will be either normalized or normalized and tempered, unless otherwise specified. Normalizing and tempering is required for Grades SC-2R, 4, 5, 6 and 6R but these grades may be supplied quenched and tempered with approval of the controlling design engineering department, after consultation wit

14、h the materials engineer. After quenching and tempering, they will meet the mechanical properties required for normalized and tempered castings, unless otherwise specified on the drawing. Grades SC-2 and SC-6 will be assigned an R suffix designation when impact requirements are specified. Example SC

15、-2R, SC-6R. 6.1.2 Castings - Quenched And Tempered Where quenching and tempering is required for Grades SC-3 through SC-6 the appropriate suffix letter shown in Tables I and IA (suffix letters A, B, C, or D) indicating the required mechanical properties will be added: Example: SC-6B. Note: A suffix

16、letter need not be added to those castings which are quenched and tempered to meet normalized and tempered mechanical properties. See ”Castings - Normalized or Normalized and Tempered” above. 6.1.2.1 Quenched castings will be tempered at 425C (800F) minimum, except those used in abrasion resistant a

17、pplications. Castings must be in a homogeneous state, achieved by either a normalizing operation or a longer austenitizing time, prior to quenching and tempering, unless otherwise specified. However, when castings are specified quenched and tempered, they are not required to meet the mechanical prop

18、erties specified for normalized or normalized and tempered castings, prior to quenching and tempering. The purchaser and supplier will agree upon the necessary process and material to assure mechanical properties, machinability and weldability requirements are acheived. 6.1.3 Tensile Requirements Th

19、e tensile requirements specified for test bars pertain to standard tensile test specimens machined from keel blocks or test coupons having a thickness of 25 mm (1 inch). Casting tensile requirements will be determined on tensile test specimens taken from the center of sections up to 25 mm (1 inch) t

20、hick, inclusive and from the mid-radius of sections over 25 mm (1 inch) thick. See “Methods of Test”, Section 8.0. 6.1.3.1 If the foundry anticipates or finds that it cannot meet the strength requirements throughout the casting as determined above, the foundry will request the controlling engineerin

21、g department to identify significant sections on the drawing. When sections of a casting are deemed significant for reasons of stress, function or reliability, the controlling design engineering department must designate the location Copyright Navistar International Corporation Provided by IHS under

22、 license with INTERNNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-NUMBER: CEMS E-2 TITLE: Steel Castings CURRENT ISSUE DATE: August 2008 This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technic

23、al Standards. Suppliers are required to assume all patent liability. 2008 by Navistar, Inc. AUGUST 2008 Page 3 of 13 of the significant section or sections on the drawing. The purpose of this procedure is to clearly establish that strength (or corresponding hardness) determinations be made in those

24、required areas. 6.1.4 Hardness Hardness requirements for casting will be met on finished machined surfaces. Therefore, it may be necessary to control hardness at or near the casting surfaces to a range different than specified herein, to compensate for stock removal. The plant metallurgist and suppl

25、ier will agree upon the different hardness ranges. The conversion of hardness to tensile strength will be according to the Hardness Conversion Chart per NAVISTAR Manufacturing Standard MS-E-1A2, available from Corporate Technical Standards, TDTC, 2911 Meyer Road, P.O. Box 1109, Fort Wayne, IN 46801-

26、1109. TABLE I - MECHANICAL PROPERTIES* Designation Tensile Strength, min ksiYield Strength, 0.2% offset, min ksi Elongation in 2 inches, % min Reduction of Area, % min Brinell Hardness Number HBW Navistar Grade Suffix Letter Obsolete Navistar Grade Required Heat Treatment test bars castingstest bars

27、 castingstest bars castingstest bars castingstest bars and castingsSC-0 187 max SC-1 65 52 35 28 24 19 35 28 131-187 SC-2 75 60 45 36 20 16 20 24 156-207 SC-3 normalized or normalized and tempered 85 68 45 36 16 13 24 19 170-229 SC-4 SC-5 SC-6 SC-7 90 72 60 48 16 13 35 28 187-241 SC-2R 75 60 45 36 2

28、0 16 30 24 156-207 SC-6R none SC-R normalized and tempered * 90 72 60 48 16 13 35 28 187-241 SC-3 A 100 80 70 56 10 8 15 12 207-255 SC-4 SC-5 SC-6 B SC-7 105 84 85 68 17 14 35 28 217-269 SC-4 SC-5 SC-6 C SC-7 120 96 95 76 14 11 30 24 255-302 SC-4 SC-5 D quenched and tempered * 150 120 125 100 9 7 22

29、 18 302-363 * See ”Appendix - General Information” for mechanical properties design criteria. * These grades may be quenched and tempered with approval of the controlling design engineering department. In such cases, the materials engineer should be consulted. * When castings and test bars are quenc

30、hed and tempered, they do not have to meet the mechanical properties specified for normalized or normalized and tempered castings and test bars prior to quenching and tempering. Copyright Navistar International Corporation Provided by IHS under license with INTERNNot for ResaleNo reproduction or net

31、working permitted without license from IHS-,-,-NUMBER: CEMS E-2 TITLE: Steel Castings CURRENT ISSUE DATE: August 2008 This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all paten

32、t liability. 2008 by Navistar, Inc. AUGUST 2008 Page 4 of 13 TABLE I A - METRIC EQUIVALENT OF TABLE I* Designation Tensile Strength MPa, minYield Strength, 0.2% offset MPa, min Elongation in 50 mm % min Reduction of Area, % min Brinell Hardness Number HBW Navistar Grade Suffix Letter Obsolete Navist

33、ar Grade Required Heat Treatment test bars castingstest bars castingstest bars castingstest bars castingstest bars and castingsSC-0 187 max SC-1 448 359 241 193 24 19 35 28 131-187 SC-2 517 414 310 248 20 16 20 24 156-207 SC-3 normalized or normalized and tempered 586 469 310 248 16 13 24 19 170-229

34、 SC-4 SC-5 SC-6 SC-7 620 496 414 331 16 13 35 28 187-241 SC-2R 517 414 310 248 20 16 30 24 156-207 SC-6R none SC-R normalized and tempered * 620 496 414 331 16 13 35 28 187-241 SC-3 A 689 552 483 386 10 8 15 12 207-255 SC-4 SC-5 SC-6 B SC-7 724 579 586 469 17 14 35 28 217-269 SC-4 SC-5 SC-6 C SC-7 8

35、27 662 655 524 14 11 30 24 255-302 SC-4 SC-5 D quenched and tempered * 1034 827 862 689 9 7 22 18 302-363 *, *, * See footnotes for Table I 6.1.5 Impact Test Requirements (Grade SC-2R and SC-6R) These grades of steel castings purchased to this specification will meet the following impact test requir

36、ements unless otherwise specified. See ”Methods of Test”, Section 8. 6.1.5.1 The requirements for standard and subsize Charpy V-Notch specimens are shown in Table II. The standard size specimen will be used except where the section thickness does not permit machining a 10 mm by 10 mm specimen. In su

37、ch cases, subsize specimens as listed will be used. The subsize specimen selected will be as large as the particular section thickness permits. 6.1.5.2 Nil Ductility Transition Temperature - Optional Method SC-2R and SC-6R Grades steel castings will have a maximum nil ductility transition temperatur

38、e (NDTT) of -34C (-30F). This requirement may be used in lieu of the Charpy V-Notch impact requirement for material with section thickness 15.9 mm (0.625 inch) and greater. Copyright Navistar International Corporation Provided by IHS under license with INTERNNot for ResaleNo reproduction or networki

39、ng permitted without license from IHS-,-,-NUMBER: CEMS E-2 TITLE: Steel Castings CURRENT ISSUE DATE: August 2008 This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent lia

40、bility. 2008 by Navistar, Inc. AUGUST 2008 Page 5 of 13 TABLE II - GRADES SC-2R however, grinding, machining, chipping and oxy-fuel gouging may be used. 6.6.1.2.1 Careful visual inspection of the prepared area to assure complete removal of defects is normally adequate. However, the use of magnetic p

41、article or dye penetrant inspection of the cavity may be desirable or be specified for specific castings or areas of castings. 6.6.1.2.2 Before welding, the prepared cavity and the immediate area will be clean of all residue from the oxy-fuel or arc-air gouging, and free of oil, water, heavy scale,

42、etc. which could adversely affect the quality of the weld repair. 6.6.1.2.3 All side walls of prepared cavities will be a minimum of 20 degrees from a line normal to the casting surface so that side wall fusion can be obtained during welding. 6.6.1.3 Arc welding will be used for all repair welds in

43、steel castings. Shielded metal-arc, gas metal-arc and flux-cored arc welding processes are satisfactory; prior approval must be obtained for other arc welding processes. 6.6.1.4 Electrode selection will be such that the properties of the resulting weld will be at least equal to the specified minimum

44、 properties of the casting. 6.6.1.5 Areas of castings that have been repair welded will be inspected to the same quality level, using the same method of inspection as specified or used for nonrepair welded castings. 6.6.1.6 Only personnel who have proven their ability through tests or other effectiv

45、e means will be used for preparing and repair welding of steel castings. 6.6.2 Other Machining errors or casting defects encountered during machining may be weld repaired only after a procedure has been developed, suitable for the casting grade involved and approved by the controlling design enginee

46、ring department. 7.0 QUALITY 7.1 General Castings will be clean and free of severe rust, corrosion and all scale. Unless otherwise specified, superficial rust and corrosion is permissible but surface finish texture must be satisfactory for the intended use. Castings will not be covered with any subs

47、tance which hides defects nor will they be painted unless authorized by the purchaser. Casting suppliers will not subcontract castings without approval of the Purchasing Department and the Plant Metallurgist and/or Quality Control Manager of the using plant. 7.2 Soundness Castings will be free from

48、injurious defects. They will meet the following requirements for soundness, unless otherwise specified. See “Sampling Procedure” (Section 7.3) and “Methods of Test” (Section 8.0). 7.2.1 Castings will exhibit a surface quality of machined surfaces which is suitable for intended use. 7.2.2 In general, soundness of the casting except item (1) above will m