NAVISTAR MPAPS B-51-2018 Dry Film Lubricant for Fasteners.pdf

1、This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2018 by Navistar, Inc. FEBRUARY 2018 Page 1 of 3 NAVISTAR, INC. Material, Parts, and Process Specificatio

2、ns (MPAPS) NUMBER: MPAPS B-51 Former Designation: CEMS B-51 TITLE: Dry Film Lubricant for Fasteners CURRENT REV No.: 1802 DATE: Feb. 2018 WRITTEN/EDITED BY: W. Cook APPROVED BY: R. Goluch SUPERSEDES: Rev. June 2013 PRINTED COPIES OF THIS DOCUMENT MUST BE VERIFIED FOR CURRENT REVISION This specificat

3、ion may involve hazardous materials, equipment, and procedures. This specification does not purport to address all of the safety issues associated with its use. The user is responsible to consult appropriate safety and health practices and to determine the applicability of regulatory limits prior to

4、 use. 1.0 APPLICATION This specification applies to a solid film lubricant coating containing molybdenum disulfide and other lubricating pigments used on fasteners to lower the coefficient of friction, reduce wear, minimize metallic adhesion of parts operating dry and provide good corrosion resistan

5、ce on the threaded sections of fasteners. This coating is suitable for internal threads of nuts and tapping plates, and external threads of bolts and studs. 2.0 SCOPE This specification covers the general coating requirements, quality, source approval and quality control, packing, shipping, and iden

6、tification requirements, and designation on drawings. 2.1 Restricted Chemical Substances Effective April 1, 2013 all product supplied to the requirements of this specification must comply with the requirements of the MPAPS B-50 specification. 3.0 REFERENCE DOCUMENTS Unless otherwise specified the la

7、test issue of all referenced standards shall apply. The following standards, specifications, and regulations are referenced in this specification: ISO 9001/TS 16949 Quality Management Systems- Requirements CFR Title 29, Part 1910 Occupational Health and Safety Standards NAVISTAR ISQ-001-QM Integrate

8、d Suppler Quality Requirements NAVISTAR D-13 Supplier Packing and Shipping Standard. NAVISTAR MPAPS B-50 Restricted Chemical Substances ASTM D 2714 - Standard Test Method for Calibration and Operation of the Falex Block-on-Ring Friction and Wear Testing Machine ASTM B 117 - Standard Practice for Ope

9、rating Salt Spray (Fog) Apparatus NUMBER: MPAPS B-51 TITLE Dry Film Lubricant CURRENT ISSUE REV: 1802 This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 201

10、8 by Navistar, Inc. FEBRUARY 2018 Page 2 of 3 4.0 GENERAL REQUIREMENTS 4.1 Coating Requirements 4.1.1 Coating Cure and Appearance The cure parameters for the coating shall be determined using the appropriate time/temperature relationship recommended by the manufacturer to achieve the desired perform

11、ance. The cure cycle should not affect the mechanical or dimensional properties of the parts being coating. 4.1.1.1 The cured coating shall be sufficiently damage resistant to prevent chipping or other coating removal during normal handling and shipping of parts. 4.1.1.2 Coating shall have a uniform

12、 appearance and be free of tears, runs, and flaked areas. 4.1.2 Coating Coverage 4.1.2.1 The coating is a dip-spin coating which provides anti-seizing and controlled frictional properties. This coating process does not generate hydrogen; however, pre-treatment processes, i.e., acid pickling could ca

13、use hydrogen adsorption. Thickness of coating shall be 5 - 20m. 4.1.3 Coefficient of Friction Coefficient of friction of the coated parts shall be .03 -.07 when measured per ASTM D2714. 4.1.4 Heat Resistance This material shall remain stable up to the temperature of + 260 Celsius. 4.1.5 Salt Spray R

14、esistance The test specimen shall show no evidence of corrosion, and the coating shall show no pinholes or separation from the metal, after testing for 72 hours per ASTM B 117. 4.1.6 Adhesion The coating must not chip, flake or expose any base metal surface. A uniform deposit of powdery material cli

15、nging to the tape shall not be objectionable. 4.1.7 Initial Approval Samples for initial approval shall be accepted based on compliance to the requirements of this specification. 5.0 QUALITY All product supplied per this specification shall be clean and free from dirt, oils, sharp edges, or defects

16、harmful to product performance. 6.0 SOURCE APPROVAL AND QUALITY CONTROL 6.1 Supplier Requirements All suppliers to NAVISTAR are subject to the requirements defined in ISQ-001-QM- NAVISTAR Integrated Supplier Quality Requirements. Suppliers must be compliant with ISO 9001 or TS 16949 and fulfill all

17、AIAG PPAP (Production Part Approval Process) documentation and all approval requirements as indicated in NAVISTAR ISQ-001-QM. 6.2 Approval Parts supplied against contracts or purchase orders citing this specification shall be equivalent in all respects to those samples which were approved by the pur

18、chaser. No changes in formulation or processing practices are permitted without approval. In the event that changes in material, properties, processing practices, construction, color, or labeling of the product are required, the supplier shall notify NAVISTAR Integrated Supplier Quality (ISQ) of the

19、 proposed change(s) by contacting their NUMBER: MPAPS B-51 TITLE Dry Film Lubricant CURRENT ISSUE REV: 1802 This document is restricted and may not be sent outside Navistar, Inc. or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liabilit

20、y. 2018 by Navistar, Inc. FEBRUARY 2018 Page 3 of 3 Navistar Supplier Quality representative or sending an email to ISQ. Test data indicating conformance to all requirements of this specification, test samples, and new or amended or updated SDS Safety Data Sheet(s) (formerly MSDS) in accordance with

21、 CFR Title 29, Part 1910, shall be submitted with the request for change. 6.3 Process Control The supplier shall either perform and report results of tests on specific lots of parts produced using ISO 9001 or TS-16949 guidelines, or provide statistical evidence of the lot having been produced in a s

22、tate of statistical control and with a process capable of providing all required properties. The part supplier and the plant metallurgist and/or the quality control manager of the using International plant may determine testing and reporting requirements on specific products. 7.0 SHIPPING, PACKING A

23、ND IDENTIFICATION Shipping and identification shall be in accordance with NAVISTAR Supplier Packing and Shipping Standard D-13. Parts shall be packaged so as to avoid any damage in shipment detrimental to the appearance of the part. 8.0 DESIGNATION ON DRAWINGS “Finish per MPAPS B-51” 9.0 APPROVED SO

24、URCES E/M Engineered Coating Solutions E/M 6340 10.0 TECHNICAL INFORMATION For further information related to the technical content of this specification, contact: Suppliers may purchase controlled copies of this specification by contacting: Materials Engineering and Technology Dept. 10400 W. North Avenue Melrose Park, IL 6016 E-mail: MaterialsEngineeringN IHS Markit Inc. 15 Inverness Way East Englewood CO 80112-5776 Phone: 1-800-854-7179 E-mail: AutomotiveIHS.com Website: http:/ REVISION HISTORY Revision Level Change Approved by Date Approved 1802 Converted to MPAPS R. Goluch 2/13/2018