1、 Collection of SANS standards in electronic format (PDF) 1. Copyright This standard is available to staff members of companies that have subscribed to the complete collection of SANS standards in accordance with a formal copyright agreement. This document may reside on a CENTRAL FILE SERVER or INTRA
2、NET SYSTEM only. Unless specific permission has been granted, this document MAY NOT be sent or given to staff members from other companies or organizations. Doing so would constitute a VIOLATION of SABS copyright rules. 2. Indemnity The South African Bureau of Standards accepts no liability for any
3、damage whatsoever than may result from the use of this material or the information contain therein, irrespective of the cause and quantum thereof. ISBN 978-0-626-20150-0 SANS 6507-4:2008Edition 1ISO 6507-4:2005Edition 1SOUTH AFRICAN NATIONAL STANDARD Metallic materials Vickers hardness test Part 4:
4、Tables of hardness values This national standard is the identical implementation of ISO 6507-4:2005 and is adopted with the permission of the International Organization for Standardization. Published by Standards South Africa 1 dr lategan road groenkloof private bag x191 pretoria 0001 tel: 012 428 7
5、911 fax: 012 344 1568 international code + 27 12 www.stansa.co.za Standards South Africa SANS 6507-4:2008 Edition 1 ISO 6507-4:2005 Edition 1 Table of changes Change No. Date Scope National foreword This South African standard was approved by National Committee StanSA SC 5120.20C, Engineering materi
6、als Mechanical testing of metals, in accordance with procedures of Standards South Africa, in compliance with annex 3 of the WTO/TBT agreement. This SANS document was published in February 2008. Reference numberISO 6507-4:2005(E)ISO 2005INTERNATIONAL STANDARD ISO6507-4First edition2005-12-15Metallic
7、 materials Vickers hardness test Part 4: Tables of hardness values Matriaux mtalliques Essai de duret Vickers Partie 4: Tableaux des valeurs de duret SANS 6507-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 6507-4:2005(E) PDF discl
8、aimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file, parties a
9、ccept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General Info relative to th
10、e file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below. ISO 2005 All ri
11、ghts reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of t
12、he requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2005 All rights reservedSANS 6507-4:2008This s tandard may only be used and printed by approved subscription and f
13、reemailing clients of the SABS .ISO 6507-4:2005(E) ISO 2005 All rights reserved iiiContents Page Foreword iv 1 Scope . 1 2 Tables of Vickers hardness values for use in tests made on flat surfaces 1 SANS 6507-4:2008This s tandard may only be used and printed by approved subscription and freemailing c
14、lients of the SABS .ISO 6507-4:2005(E) iv ISO 2005 All rights reservedForeword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO techni
15、cal committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely w
16、ith the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft Int
17、ernational Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document m
18、ay be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 6507-4 was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals, Subcommittee SC 3, Hardness testing. This first edition cancels and replaces Annexes B, C and
19、D of ISO 6507-1:1997. ISO 6507 consists of the following parts, under the general title Metallic materials Vickers hardness test: Part 1: Test method Part 2: Verification and calibration of testing machines Part 3: Calibration of reference blocks Part 4: Tables of hardness values SANS 6507-4:2008Thi
20、s s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .INTERNATIONAL STANDARD ISO 6507-4:2005(E) ISO 2005 All rights reserved 1Metallic materials Vickers hardness test Part 4: Tables of hardness values 1 Scope This part of ISO 6507 gives tables of Vick
21、ers hardness for use in tests made on flat surfaces. 2 Tables of Vickers hardness values for use in tests made on flat surfaces See Table 1 for range HV 0,2. See Table 2 for range HV 0,2 to HV 3. See Table 3 for range HV 5 to HV 100. Table 1 Range HV 0,2 Test force, F N 0,009 807 0,019 61 0,049 03 0
22、,098 07 0,196 12 0,245 2 0,490 3 0,980 7 Vickers hardness Mean diagonal of indentation d mm HV 0,001 HV 0,002 HV 0,005 HV 0,01 HV 0,02 HV 0,025 HV 0,05 HV 0,1 0,020 0 0,020 2 0,020 4 0,020 6 0,020 8 4,64 4,54 4,46 4,37 4,29 9,27 9,09 8,91 8,74 8,57 23,18 22,72 22,28 21,85 21,43 46,36 45,45 44,56 43,
23、70 42,86 92,72 90,89 89,12 87,39 85,72 115,9 113,6 111,4 109,3 107,2 231,8 227,2 222,8 218,5 214,3 463,6 454,5 445,6 437,0 428,6 0,021 0 0,021 2 0,021 4 0,021 6 0,021 8 4,21 4,13 4,05 3,97 3,90 8,41 8,25 8,10 7,95 7,80 21,02 20,63 20,25 19,87 19,51 42,05 41,26 40,49 39,75 39,02 84,10 82,52 80,98 79,
24、49 78,04 105,1 103,2 101,2 99,38 97,57 210,2 206,3 202,5 198,7 195,1 420,5 412,6 404,9 397,5 390,2 0,022 0 0,022 2 0,022 4 0,022 6 0,022 8 3,83 3,76 3,70 3,63 3,57 7,66 7,52 7,39 7,26 7,13 19,16 18,81 18,48 18,15 17,84 38,32 37,63 36,96 36,31 35,67 76,62 75,25 73,91 72,61 71,34 95,80 94,08 92,41 90,
25、78 89,20 191,6 188,1 184,8 181,5 178,4 383,2 376,3 369,6 363,1 356,7 0,023 0 0,023 2 0,023 4 0,023 6 0,023 8 3,51 3,45 3,39 3,33 3,27 7,01 6,89 6,77 6,66 6,55 17,53 17,23 16,93 16,65 16,37 35,06 34,45 33,87 33,30 32,74 70,11 68,90 67,73 66,59 65,47 87,65 86,15 84,68 83,25 81,86 175,3 172,3 169,3 166
26、,5 163,7 350,6 344,5 338,7 333,0 327,4 SANS 6507-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 6507-4:2005(E) 2 ISO 2005 All rights reservedTable 1 (continued) Test force, F N 0,009 807 0,019 61 0,049 03 0,098 07 0,196 12 0,245 2
27、0,490 3 0,980 7 Vickers hardness Mean diagonal of indentation d mm HV 0,001 HV 0,002 HV 0,005 HV 0,01 HV 0,02 HV 0,025 HV 0,05 HV 0,1 0,024 0 0,024 2 0,024 4 0,024 6 0,024 8 3,22 3,17 3,11 3,06 3,02 6,44 6,33 6,23 6,13 6,03 16,10 15,83 15,57 15,32 15,07 32,20 31,67 31,15 30,64 30,15 64,39 63,33 62,2
28、9 61,28 60,30 80,50 79,17 77,88 76,62 75,39 161,0 158,3 155,7 153,2 150,7 322,0 316,7 311,5 306,4 301,5 0,025 0 0,025 2 0,025 4 0,025 6 0,025 8 2,97 2,92 2,87 2,83 2,79 5,93 5,84 5,75 5,66 5,57 14,83 14,60 14,37 14,15 13,93 29,67 29,20 28,74 28,30 27,86 59,34 58,40 57,48 56,59 55,72 74,19 73,01 71,8
29、7 70,75 69,66 148,3 146,0 143,7 141,5 139,3 296,7 292,0 287,4 283,0 278,6 0,026 0 0,026 2 0,026 4 0,026 6 0,026 8 2,74 2,70 2,66 2,62 2,58 5,49 5,40 5,32 5,24 5,16 13,72 13,51 13,30 13,10 12,91 27,43 27,02 26,61 26,21 25,82 54,86 54,03 53,21 52,41 51,63 68,59 67,55 66,53 65,53 64,56 137,2 135,1 133,
30、0 131,0 129,1 274,3 270,2 266,1 262,1 258,2 0,027 0 0,027 2 0,027 4 0,027 6 0,027 8 2,54 2,51 2,47 2,43 2,40 5,09 5,01 4,94 4,87 4,80 12,72 12,53 12,35 12,17 12,00 25,44 25,07 24,70 24,34 24,00 50,87 50,13 49,40 48,69 47,99 63,60 62,67 61,76 60,87 60,00 127,2 125,3 123,5 121,7 120,0 254,4 250,7 247,
31、0 243,4 240,0 0,028 0 0,028 2 0,028 4 0,028 6 0,028 8 2,37 2,33 2,30 2,27 2,24 4,73 4,66 4,60 4,53 4,47 11,83 11,66 11,50 11,33 11,18 23,65 23,32 22,99 22,67 22,36 47,30 46,64 45,98 45,34 44,71 59,14 58,31 57,49 56,69 55,90 118,3 116,6 115,0 113,3 111,8 236,5 233,2 229,9 226,7 223,6 0,029 0 0,029 2
32、0,029 4 0,029 6 0,029 8 2,21 2,18 2,15 2,12 2,09 4,41 4,35 4,29 4,23 4,18 11,02 10,87 10,73 10,58 10,44 22,05 21,75 21,46 21,17 20,88 44,10 43,50 42,91 42,33 41,76 55,13 54,38 53,64 52,92 52,21 110,2 108,7 107,3 105,8 104,4 220,5 217,5 214,6 211,7 208,8 0,030 0 0,030 2 0,030 4 0,030 6 0,030 8 2,06 2
33、,03 2,01 1,98 1,95 4,12 4,07 4,01 3,96 3,91 10,30 10,17 10,03 9,90 9,77 20,61 20,33 20,07 19,81 19,55 41,21 40,66 40,13 39,61 39,09 51,52 50,84 50,17 49,52 48,88 103,0 101,7 100,3 99,02 97,74 206,1 203,3 200,7 198,1 195,5 0,031 0 0,031 2 0,031 4 0,031 6 0,031 8 1,93 1,91 1,88 1,86 1,83 3,86 3,81 3,7
34、6 3,71 3,67 9,65 9,52 9,40 9,28 9,17 19,30 19,05 18,81 18,57 18,34 38,59 38,10 37,61 37,14 36,67 48,25 47,63 47,03 46,43 45,85 96,48 95,25 94,04 92,85 91,69 193,0 190,5 188,1 185,7 183,4 0,032 0 0,032 2 0,032 4 0,032 6 0,032 8 1,81 1,79 1,77 1,74 1,72 3,62 3,58 3,53 3,49 3,45 9,05 8,94 8,83 8,72 8,6
35、2 18,11 17,89 17,67 17,45 17,24 36,22 35,77 35,33 34,90 34,47 45,28 44,72 44,17 43,63 43,10 90,54 89,42 88,32 87,24 86,18 181,1 178,9 176,7 174,5 172,4 0,033 0 0,033 2 0,033 4 0,033 6 0,033 8 1,70 1,68 1,66 1,64 1,62 3,41 3,36 3,32 3,28 3,25 8,51 8,41 8,31 8,21 8,12 17,03 16,82 16,62 16,43 16,23 34,
36、06 33,65 33,24 32,85 32,46 42,58 42,07 41,56 41,07 40,59 85,14 84,12 83,11 82,12 81,16 170,3 168,2 166,2 164,3 162,3 SANS 6507-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 6507-4:2005(E) ISO 2005 All rights reserved 3Table 1 (con
37、tinued) Test force, F N 0,009 807 0,019 61 0,049 03 0,098 07 0,196 12 0,245 2 0,490 3 0,980 7 Vickers hardness Mean diagonal of indentation d mm HV 0,001 HV 0,002 HV 0,005 HV 0,01 HV 0,02 HV 0,025 HV 0,05 HV 0,1 0,034 0 0,034 2 0,034 4 0,034 6 0,034 8 1,60 1,59 1,57 1,55 1,53 3,21 3,17 3,13 3,10 3,0
38、6 8,02 7,93 7,83 7,74 7,66 16,04 15,86 15,67 15,49 15,31 32,08 31,71 31,34 30,98 30,62 40,11 39,64 39,18 38,73 38,29 80,20 79,27 78,35 77,45 76,56 160,4 158,6 156,7 154,9 153,1 0,035 0 0,035 2 0,035 4 0,035 6 0,035 8 1,51 1,50 1,48 1,46 1,45 3,03 2,99 2,96 2,93 2,89 7,57 7,48 7,40 7,32 7,23 15,14 14
39、,97 14,80 14,63 14,47 30,27 29,93 29,59 29,26 28,94 37,85 37,42 37,00 36,59 36,18 75,69 74,83 73,99 73,16 72,34 151,4 149,7 148,0 146,3 144,7 0,036 0 0,036 2 0,036 4 0,036 6 0,036 8 1,43 1,42 1,40 1,38 1,37 2,86 2,83 2,80 2,77 2,74 7,15 7,08 7,00 6,92 6,85 14,31 14,15 14,00 13,84 13,69 28,62 28,30 2
40、7,99 27,69 27,39 35,78 35,38 35,00 34,61 34,24 71,54 70,75 69,98 69,21 68,46 143,1 141,5 140,0 138,4 136,9 0,037 0 0,037 2 0,037 4 0,037 6 0,037 8 1,35 1,34 1,33 1,31 1,30 2,71 2,68 2,65 2,62 2,60 6,77 6,70 6,63 6,56 6,49 13,55 13,40 13,26 13,12 12,98 27,09 26,80 26,51 26,23 25,96 33,87 33,51 33,15
41、32,80 32,45 67,73 67,00 66,28 65,58 64,89 135,5 134,0 132,6 131,2 129,8 0,038 0 0,038 2 0,038 4 0,038 6 0,038 8 1,28 1,27 1,26 1,24 1,23 2,57 2,54 2,51 2,49 2,46 6,42 6,35 6,29 6,22 6,16 12,84 12,71 12,58 12,45 12,32 25,68 25,41 25,15 24,89 24,63 32,11 31,77 31,44 31,12 30,80 64,21 63,54 62,88 62,23
42、 61,59 128,4 127,1 125,8 124,5 123,2 0,039 0 0,039 2 0,039 4 0,039 6 0,039 8 1,22 1,21 1,19 1,18 1,17 2,44 2,41 2,39 2,36 2,34 6,10 6,03 5,97 5,91 5,85 12,19 12,07 11,95 11,83 11,71 24,38 24,13 23,89 23,65 23,41 30,48 30,17 29,87 29,57 29,27 60,96 60,34 59,73 59,12 58,53 121,9 120,7 119,5 118,3 117,
43、1 0,040 0 0,040 2 0,040 4 0,040 6 0,040 8 1,16 1,15 1,14 1,13 1,11 2,32 2,29 2,27 2,25 2,23 5,79 5,74 5,68 5,62 5,57 11,59 11,48 11,36 11,25 11,14 23,18 22,95 22,72 22,50 22,28 28,98 28,69 28,41 28,13 27,85 57,95 57,37 56,81 56,25 55,70 115,9 114,8 113,6 112,5 111,4 0,041 0 0,041 2 0,041 4 0,041 6 0
44、,041 8 1,10 1,09 1,08 1,07 1,06 2,21 2,18 2,16 2,14 2,12 5,52 5,46 5,41 5,36 5,31 11,03 10,93 10,82 10,72 10,61 22,06 21,85 21,64 21,43 21,23 27,58 27,32 27,05 26,79 26,54 55,16 54,62 54,09 53,58 53,06 110,3 109,3 108,2 107,2 106,1 0,042 0 0,042 2 0,042 4 0,042 6 0,042 8 1,05 1,04 1,03 1,02 1,01 2,1
45、0 2,08 2,06 2,04 2,02 5,26 5,21 5,16 5,11 5,06 10,51 10,41 10,32 10,22 10,12 21,02 20,83 20,63 20,44 20,25 26,29 26,04 25,79 25,55 25,31 52,56 52,06 51,57 51,09 50,61 105,1 104,1 103,2 102,2 101,2 0,043 0 0,043 2 0,043 4 0,043 6 0,043 8 1,00 2,01 1,99 1,97 1,95 1,93 5,01 4,97 4,92 4,88 4,83 10,03 9,
46、94 9,85 9,76 9,67 20,06 19,87 19,69 19,51 19,33 25,08 24,85 24,62 24,39 24,17 50,14 49,68 49,22 48,77 48,33 100,3 99,37 98,46 97,56 96,67 SANS 6507-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 6507-4:2005(E) 4 ISO 2005 All rights
47、 reservedTable 1 (continued) Test force, F N 0,009 807 0,019 61 0,049 03 0,098 07 0,196 12 0,245 2 0,490 3 0,980 7 Vickers hardness Mean diagonal of indentation d mm HV 0,001 HV 0,002 HV 0,005 HV 0,01 HV 0,02 HV 0,025 HV 0,05 HV 0,1 0,044 0 0,044 2 0,044 4 0,044 6 0,044 8 1,92 1,90 1,88 1,86 1,85 4,
48、79 4,75 4,70 4,66 4,62 9,58 9,49 9,41 9,32 9,24 19,16 18,98 18,81 18,64 18,48 23,95 23,73 23,52 23,31 23,10 47,89 47,46 47,03 46,61 46,20 95,79 94,93 94,07 93,23 92,40 1,83 4,58 9,16 18,31 22,90 45,79 91,58 1,82 4,54 9,08 18,15 22,70 45,38 90,77 1,80 4,50 9,00 17,99 22,50 44,98 89,97 1,78 4,46 8,92
49、17,84 22,30 44,59 89,19 0,045 0 0,045 2 0,045 4 0,045 6 0,045 8 1,77 4,42 8,84 17,68 22,10 44,20 88,41 1,75 4,38 8,76 17,53 21,91 43,82 87,64 1,74 4,34 8,69 17,38 21,72 43,44 86,88 1,72 4,31 8,61 17,23 21,54 43,06 86,14 1,71 4,27 8,54 17,08 21,35 42,70 85,40 0,046 0 0,046 2 0,046 4 0,046 6 0,046 8 1,69 4,23 8,47 16,93 21,17 42,33 84,67 0,047 0 1,68 4,20 8,40 16,79 20,99 41,97 83,95 0,047 2 1,66 4,16 8,32 16,65 20,81 41,62 83,24 0,047 4 1,65 4,13 8,25 16,51 20,64 41,27 82,54 0,047