1、AECMA STANDARD NORME AECMA AECMA NORM Edition approved for publication 30 September 2004 prEN 4615 Edition P 1 September 2004 Comments should be sent within six months after the date of publication to AECMA-STAN PUBLISHED BY THE EUROPEAN ASSOCIATION OF AEROSPACE INDUSTRIES - STANDARDIZATION d%k?&?!f
2、f! Gulledelle 94 - B-1200 Brussels - Tel. + 32 2 775 81 10 - Fax. + 32 2 775 81 11 - www.aecma-stan.org ICs: Descriptors: ENGLISH VERSION Aerospace series Magnesium alloy MG-CI 8002 T4 Sand casting Srie arospatiale Alliage de magnsium MG-CI8002 T4 Produit coul en sable Luft- und Raumfahrt Magnesiuml
3、egierung MG-CI8002 T4 Sandgustck This “Aerospace Series“ frestandard has been drawn up under the responsibility of AECMA-STAN (The European Association of Aerospace Industries - Standardization). It is published for the needs of the European Aerospace Industry. It has been technically approved by th
4、e experts of the concerned Domain following member comments. Subsequent to the publication of this frestandard, the technical content shall not be changed to an extent that interchangeabilify is affected, physically or functionally, without re-identification of the standard. After examination and re
5、view by users and formal agreement of AECMA-STAN, it will be submitted as a draft European Standard (prEN) to CEN (European Committee for Standardization) for formal vote and transformation to full European Standard (EN). The CEN national members have then to implement the EN at national level by gi
6、ving the EN the status of a national standard and by withdrawing any national standards conflicting with the EN. Metallic Material Domain Copytight 2004 O by AECMA-STA1 Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo
7、reproduction or networking permitted without license from IHS-,-,-Page 2 prEN 461 52004 Foreword This standard was reviewed by the Domain Technical Coordinator of AECMA-STANS Metallic Material Domain. After inquiries and votes carried out in accordance with the rules of AECMA-STAN defined in AECMA-
8、STANS General Process Manual, this standard has received approval for Publication. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 3 prEN 461 5:20
9、04 O Introduction This standard is part of the series of EN metallic material standards for aerospace applications. The general organization of this series is described in EN 4258. This standard has been prepared in accordance with EN 4500-2. 1 Scope This standard specifies the requirements relating
10、 to: Magnesium alloy MG-CI 8002 T4 Sand casting for aerospace application. 2 Normative references This European Standard incorporates by dated or undated reference, provisions from other publications. These normative references are cited at the appropriate places in the text and the publications are
11、 listed hereafter. For dated references, subsequent amendments to or revisions of any of these publications apply to this European Standard only when incorporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies (including amendments).
12、EN 2076-3, Aerospace series - Aluminium and magnesium alloy ingots and castings - Technical specification - Part 3: Pre-production and production castings EN 4258, Aerospace series - Metallic materials - General organization of standardization - Links between types of EN standards and their use EN 4
13、500-2, Aerospace series - Metallic materials - Rules for drafting and presentation of material standards - Part 2: Specific rules for aluminium, aluminium alloys and magnesium alloys 1) Published as AECMA Prestandard at the date of publication of this standard Copyright Association Europeene des Con
14、structeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 4 prEN 461 5:2004 Limit dimension(s) mm Technical specification Magnesium alloy MG - CI8002 a I Material designation - EN 2076-3 Chemical
15、 composition % 3.1 Element min. Cut-up, undesignated location, Cut-up, designated location Test sample(s) Separately cast gated or integral Method of melting I 3.2 3.3 9 - -orm I Sand casting Test piece(s) See EN 2076-3. See EN 2076-3. See EN 2076-3. Heat treatment Use condition Use condition Use co
16、ndition Dimensions concerned mm See EN 2076-3. as20 as20 Method of production Thickness of cladding on each face Sand casting % - - - Elongation Reduction of area I T4 I 6.1 I Delivery condition A% 27 25c 25c Z % - I U I 6.2 I Delivery condition code 17 18 19 I T4 I 7 I Use condition Hardness - Shea
17、r strength R, MPa - Bending k- - I Heat treatment I Delivery condition I 23 -c 24 25 26 27 - - Characteristics Stress oa MPa - Elongation a% - Rupture stress oR MPa - Elongation at A % - rupture abc Notes (see line 98) - I - I - I 11 I Direction of test piece Ambient I Ambient I Temperature I 0 I “C
18、 I Ambient Proof stress I I MPa I 2 80 I 260 I 260 Strength I R, I MPal 2 200 I 2 120 I 2 120 - 20 I Impact strength I 21 I ITemperature I 0 I “C I - 22 I ITime Ihl - Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo re
19、production or networking permitted without license from IHS-,-,-Page 5 prEN 461 5:2004 Hardness ixternal defects 55 (Typical value) 20 per batch HB nternal defects 3atch uniformity Marking inspection 3imensional inspection Votes rypical use See EN 2076-3. See EN 2076-3. See EN 2076-3. See EN 2076-3.
20、 See EN 2076-3. a Similar to alloy designation IS0 - MgA18Zn and alloy designations AZ81A and AZ80 but has tighter controls on impurity elements in order to promote maximum corrosion resistance. Unless otherwise advised by the purchaser, the manufacturer may, at his discretion, and especially to min
21、imize distortion in thin sections, alternatively air cool to ambient temperature from the solution heat treatment temperature or use water with quench additives (polymer quench) at 6% 30 OC. The tensile properties stated may not be consistently achievable in all parts of all castings. Any differing
22、requirements stated on the drawing shall take precedence over those of this material standard. b Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-100 Page 6 prEN 461 5:2004 - Product qualification Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-