1、Designation: A 650/A 650M 03 (Reapproved 2008)Standard Specification forTin Mill Products, Black Plate, Double Reduced1This standard is issued under the fixed designation A 650/A 650M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision
2、, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers double-reduced black plate,produced from low-carbon cold-reduced steel, furni
3、shed incoils and cut sizes, for use predominantly in the manufacture ofcontainers. The product may be specified “as rolled,” withoutthe removal of the rolling solution, and with no additionalsurface or oiling treatment. It may also be specified “cleaned”with the rolling solution removed, with or wit
4、hout surfacetreatment and oiling. This product is normally supplied withtrimmed edges.1.2 This specification is applicable to orders in eitherinch-pound units (as A 650) which is supplied in thicknesses0.0050 in. to 0.0113 in. or SI units as A 650M which issupplied in thicknesses from 0.127 to 0.287
5、 mm.1.3 The values stated in either inch-pound or SI units are tobe regarded as standard. Within the text, the SI units are shownin brackets. The values stated in each system are not exactequivalents; therefore, each system must be used indepen-dently of the other. Combining values from the two syst
6、emsmay result in nonconformance with this specification.2. Referenced Documents2.1 ASTM Standards:2A 623 Specification for Tin Mill Products, General Require-mentsA 623M Specification for Tin Mill Products, General Re-quirements Metric3. Ordering Information3.1 Orders for material under this specifi
7、cation shall includethe following information, as required and applicable, toadequately describe the desired materials.3.1.1 Name of material (double-reduced black plate),3.1.1.1 As rolled, with the rolling solution not removed,3.1.1.2 Cleaned, with the rolling solution removed, notreoiled,3.1.1.3 C
8、leaned and oiled, with the rolling solution removedand reoiled,3.1.1.4 Cleaned, chemically treated and oiled, with therolling solution removed, chemically treated and reoiled.3.1.2 Thickness (see Specification A 623 SpecificationA 623M),3.1.3 Width,3.1.4 Length, for cut sizes only,3.1.5 Rolling dire
9、ction must be specified by underlining theslit (rolling width) for cut sizes (see 4.1),3.1.6 Steel type (see Specification A 623 SpecificationA 623M),3.1.7 Mechanical designation requirements (see Specifica-tion A 623 Specification A 623M),3.1.8 Intended application,3.1.9 Quantity, in base boxes SIT
10、AS (see Note 5),3.1.10 On coils, specify minimum or range of acceptableinside diameters. The standard inside diameter is approxi-mately 16 in. if ordered to Specification A 650 410 mm ifordered to Specification A 650M. Coils should be specified toa maximum coil weight if ordered to SpecificationA 65
11、0 massif ordered to Specification A 650M or maximum outsidediameter,3.1.11 Packaging,3.1.12 Special requirements where applicable, and3.1.13 ASTM specification number and year of issue(A 650/A 650M 88).NOTE 1A typical ordering description is as follows: 1200 base boxesdouble-reduced black plate, cle
12、aned and oiled, 60-lb base weight, 33116in. by coil, MR, DR8 CA, for 401 by 411 can bodies to ASTMSpecification A 650/A 650M - XX. 250 SITAS, double-reduced blackplate, cleaned and oiled, 0.17 mm thickness, 840 mm by coil, MR, DR8CA, for 99 mm can bodies to ASTM Specification A 650/A 650M.NOTE 2A ty
13、pical ordering description for cut sizes is as follows: 500base boxes, double-reduced black plate, cleaned and oiled, 60-lb baseweight MR, DR8 CA, 7C, 28 by 33116 in., for 401 by 411 can bodies inaccordance with Specification A 650/A 650M - XX. 100 SITAS, double-reduced black plate, cleaned and oile
14、d, MR, DR8 CA, 7C, 0.28 mmthickness, 781 by 773 mm, for 401 by 411 can bodies in accordance withSpecification A 650M/A 650M - XX.NOTE 3The production of coils does not afford the same opportunityfor inspection, grading, and sorting as does the production of cut sizes.Accordingly, appropriate process
15、ing and quality control procedures are1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.20 on Tin Mill Products.Current edition approved Oct. 1, 2008. Published October 2008. Originallya
16、pproved in 1971. Last previous edition approved in 2003 as A 650/A 650M 03.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe
17、 ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.required by the purchaser to obtain optimum utilization of the material.Cut sizes are line-inspected visu
18、ally and mechanically during production.Sheets having surface imperfections that will not interfere with theirutilization are included.NOTE 4Double-reduced black plate is highly susceptible to rustingand must be properly handled during transit and storage.NOTE 5In inch-pound units, double-reduced bl
19、ack plate is suppliedon an area basis expressed in base boxes. In coils, the number of baseboxes is computed from the measured length and the specified width. Thetheoretical weight of a coil is computed by multiplying the number of baseboxes in a coil by the specified base weight. In cut lengths, th
20、e number ofbase boxes is computed from the specified length and width dimensionsand sheet count. The theoretical weight of a bundle is computed bymultiplying the number of base boxes in the bundle by the specified baseweight.In SI units, double-reduced black plate is supplied on an area basisexpress
21、ed in SITAS. In coils, the number of SITAS is computed from themeasured length and the specified width. In cut sizes, the number ofSITAS is computed from the specified length and width dimensions andsheet count. For calculating mass, the density of steel for tin mill productsis 7850 kg/m3(see Specif
22、ication A 623M).4. Rolling Direction4.1 Double-reduced black plate is relatively brittle and hasvery distinct directional properties. The rolling direction mustbe specified on cut lengths and will be indicated by underliningthe slit (rolling width) dimension. To minimize the flange-cracking hazard w
23、hen the product is used for can bodies, therolling direction must be around the circumference of the can.5. Surface Finish5.1 Base Metal FinishDouble-reduced black plate is pro-duced with a ground roll finish.5.1.1 7CA smooth finish with grit lines. The surfaceroughness will range from 6 to 25 in. R
24、a 0.152 to 0.635 mRa. This is the standard finish for tin mill products.6. General Requirements for Delivery6.1 Material furnished under this specification shall con-form to the applicable requirements of the current edition ofSpecification A 623 Specification A 623M unless otherwiseprovided herein.
25、SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A 650/A 650M - 03) that may impact the use of this standard. (October 1, 2008)(1) Reapproved without changes.ASTM International takes no position respecting the validity of any paten
26、t rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision a
27、t any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your commen
28、ts will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted
29、by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).A 650/A 650M 03 (2008)2