1、Designation: C578 15aC578 15bStandard Specification forRigid, Cellular Polystyrene Thermal Insulation1This standard is issued under the fixed designation C578; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revisi
2、on. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This specification2 covers the types, physi
3、cal properties, and dimensions of cellular polystyrene boards with or withoutfacings or coatings made by molding (EPS) or extrusion (XPS) of expandable polystyrene. Products manufactured to thisspecification are intended for use as thermal insulation for temperatures from -65 to +165F (-53.9 to +73.
4、9C). This specificationdoes not apply to laminated products manufactured with any type of rigid board facer including fiberboard, perlite board, gypsumboard, or oriented strand board.1.1.1 For Type XIII only, this specification covers the physical properties, and dimensions of cellular polystyrene i
5、ntended foruse as thermal insulation for temperatures from 297 to +165F (183 to +73.9C).1.2 Consult the manufacturer for specific recommendations and properties in cryogenic conditions.1.2.1 This specification does not cover cryogenic properties except for the k-factors for Type XIII in Appendix X1.
6、 For TypeXIII in specific cryogenic applications, the manufacturer and purchaser shall agree upon the actual temperature limits and physicalproperty requirements in addition to the k-factors in Appendix X1.1.3 The use of thermal insulation materials covered by this specification may be regulated by
7、building codes that address fireperformance. For some end uses, specifiers should also address the effect of moisture and wind pressure resistance. Guidelinesregarding these end use considerations are included in Appendix X1.1.4 The values stated in inch-pound units are to be regarded as standard. T
8、he values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standar
9、d to establish appropriate safety and health practices and determine the applicability of regulatorylimitations prior to use.2. Referenced Documents2.1 ASTM Standards:3C165 Test Method for Measuring Compressive Properties of Thermal InsulationsC168 Terminology Relating to Thermal InsulationC177 Test
10、 Method for Steady-State Heat Flux Measurements and Thermal Transmission Properties by Means of theGuarded-Hot-Plate ApparatusC203 Test Methods for Breaking Load and Flexural Properties of Block-Type Thermal InsulationC272 Test Method for Water Absorption of Core Materials for Structural Sandwich Co
11、nstructionsC303 Test Method for Dimensions and Density of Preformed Block and BoardType Thermal InsulationC335 Test Method for Steady-State Heat Transfer Properties of Pipe InsulationC390 Practice for Sampling and Acceptance of Thermal Insulation LotsC518 Test Method for Steady-State Thermal Transmi
12、ssion Properties by Means of the Heat Flow Meter Apparatus1 This specification is under the jurisdiction of ASTM Committee C16 on Thermal Insulation and is the direct responsibility of Subcommittee C16.22 on Organic andNonhomogeneous Inorganic Thermal Insulations.Current edition approved Dec. 1, 201
13、5Dec. 15, 2015. Published December 2015. Originally approved in 1965. Last previous edition approved in 2015 asC578 15.C578 15a. DOI: 10.1520/C0578-15A.10.1520/C0578-15B.2 This specification is similar to ISO 4898-1984, “Cellular PlasticsSpecification for Rigid Cellular Materials Used in the Thermal
14、 Insulation of Buildings,” in title only.The scope and technical content are significantly different.ISO standards are available from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.3 For referencedASTM standards, visit theASTM website,
15、 www.astm.org, or contactASTM Customer Service at serviceastm.org. ForAnnual Book ofASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of w
16、hat changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered t
17、he official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1C550 Test Method for Measuring Trueness and Squareness of Rigid Block and Board Thermal InsulationC870 Practice for Conditioning of Thermal Insulating MaterialsC1045
18、 Practice for Calculating Thermal Transmission Properties Under Steady-State ConditionsC1058 Practice for Selecting Temperatures for Evaluating and Reporting Thermal Properties of Thermal InsulationC1114 Test Method for Steady-State Thermal Transmission Properties by Means of the Thin-Heater Apparat
19、usC1303 Test Method for Predicting Long-Term Thermal Resistance of Closed-Cell Foam InsulationC1363 Test Method for Thermal Performance of Building Materials and EnvelopeAssemblies by Means of a Hot BoxApparatusC1512 Test Method for Characterizing the Effect of Exposure to Environmental Cycling on T
20、hermal Performance of InsulationProductsD1600 Terminology for Abbreviated Terms Relating to PlasticsD1621 Test Method for Compressive Properties of Rigid Cellular PlasticsD1622 Test Method for Apparent Density of Rigid Cellular PlasticsD2126 Test Method for Response of Rigid Cellular Plastics to The
21、rmal and Humid AgingD2863 Test Method for Measuring the Minimum Oxygen Concentration to Support Candle-Like Combustion of Plastics(Oxygen Index)E84 Test Method for Surface Burning Characteristics of Building MaterialsE96/E96M Test Methods for Water Vapor Transmission of MaterialsE176 Terminology of
22、Fire Standards2.2 CAN/ULC Standard4CAN/ULC S770 Standard Test Method for the Determination of Long-Term Thermal Resistance of Closed-Cell ThermalInsulating Foams3. Terminology3.1 Definitions:3.1.1 Terms used in this specification are defined in Terminology C168.3.1.2 Terms used in this specification
23、 that relate to fire standards are defined in Terminology E176.3.2 Definitions of Terms Specific to This Standard:3.2.1 EPSletter designation for the molded expanded polystyrene thermal insulation classified by this specification. It isdefined as cellular plastic product manufactured from pre-expand
24、ed polystyrene beads subsequently molded into desired shapesand sizes resulting in a product which is rigid with closed cellular structure.3.2.2 RCPSletter designations for the rigid cellular polystyrene thermal insulation classified by this specification that identifiesthe product as rigid cellular
25、 polystyrene.3.2.3 PSused in this specification to represent polystyrene in accordance with Terminology D1600.3.2.4 XPSletter designation for the extruded expanded polystyrene thermal insulation classified by this specification. It isdefined as cellular plastic product manufactured in a one stage pr
26、ocess by extrusion and expansion of the base polymer in thepresence of blowing agent(s) resulting in a product which is rigid with closed cellular structure.4. Classification4.1 This specification covers types of RCPS thermal insulations currently commercially available as described by the physicalp
27、roperty requirements in Table 1.5. Ordering Information5.1 Acquisition documents shall specify the following:5.1.1 Title, number, and year of this specification,5.1.2 Type (see Table 1),5.1.3 R-value or thickness required (see Tables 1 and 2),5.1.3.1 Thermal Resistance/Thickness RelationshipThe ther
28、mal resistance (R-value) and the thermal resistivity (R-value/inch)of RCPS thermal insulation may vary with thickness. Therefore, when ordering, specify the R-value or the thickness, or both. Foradditional information, see Practice C1045.5.1.4 Density, if other than specified in Table 1,5.1.5 Tolera
29、nce, if other than specified (see 8.2),5.1.6 Length and width required (see Table 2 and 8.1),5.1.7 If other than straight edges are required (see 8.3),5.1.8 If either ship-lap or tongue-and-groove edges are required (see 8.6),4 Available from Underwriters Laboratories (UL), 2600 N.W. Lake Rd., Camas
30、, WA 98607-8542, http:/.C578 15b25.1.9 Tapered Insulationspecial ordering information. In addition to other applicable requirements in Section 5 (Note 1),acquisition documents for tapered RCPS thermal insulation shall specify the following:5.1.9.1 Minimum starting thickness,5.1.9.2 Slope, in./ft (mm
31、/m),5.1.9.3 Average R-value,5.1.9.4 Minimum thickness,5.1.9.5 Shop DrawingsThe tapered insulation supplier shall provide shop drawings to illustrate installation patterns anddimensions for each tapered module,5.1.10 Sampling, if different (see 10.1),5.1.11 If a certificate of compliance is required
32、(see 14.1), and5.1.12 If marking is other than specified (see 15.1).NOTE 1Physical properties of tapered insulation should be determined on blocks of RCPS thermal insulation before the insulation is tapered.TABLE 1 Physical Property Requirements of RCPS Thermal InsulationNOTE 1The values for propert
33、ies listed in this table may be affected by the presence of a surface skin which is a result of the manufacturing process.The values for Type XIII properties listed in this table must be generated on material with the surface skin removed. Where products are tested withskins-in-place, this condition
34、 shall be noted in the test report.NOTE 2Type III has been deleted because it is no longer available.NOTE 3In addition to the thermal resistance values in Table 1, values at mean temperatures of 25 2F (-4 1C), 40 2F (4 1C), and 110 2F (43 1C) are provided in X1.8 for information purposes.NOTE 4For T
35、ype XIII, in addition to the Thermal resistance property requirements shown in Table 1, there are Apparent Thermal Conductivityproperty values shown for informational purposes in Table X1.2 of Appendix X1.NOTE 5Values quoted are maximum values for 1.00 in. (25.4 mm) thick samples with natural skins
36、intact. Lower values will result for thickermaterials. Where water vapor permeance is a design issue, consult manufacturer.NOTE 6The values for thermal resistance listed in this table may be determined on product at a thickness other than 1 in. (25.4 mm) in accordancewith 7.2.2.1. When tested at a t
37、hickness other than 1 in. (25.4 mm), the thermal resistance per inch shall meet the minimum requirement.NOTE 7Types XI, I, VIII, II, IX, XIV and XV are typically EPS insulation. Types XII, X, XIII, IV, VI, VII and V are typically XPS insulation.Classification TypeXITypeITypeVIIITypeIITypeIXTypeXIVTy
38、peXVTypeXIITypeXTypeXIIITypeIVTypeVITypeVIITypeVCompressive resistance atyield or 10 % deformation,whichever occurs first(with skins intact), min, psi(kPa)5.0(35)10.0(69)13.0(90)15.0(104)25.0(173)40.0(276)60.0(414)15.0(104)15.0(104)20.0(138)25.0(173)40.0(276)60.0(414)100.0(690)Thermal resistance of
39、1.00-in.(25.4-mm) thickness, min,Fft2h/Btu (Km2/W)3.1(0.55)3.6(0.63)3.8(0.67)4.0(0.70)4.2(0.74)4.2(0.74)4.3(0.76)4.6(0.81)5.0(0.88)3.9(0.68)5.0(0.88)5.0(0.88)5.0(0.88)5.0(0.88)Mean temperature:75 2F (24 1C)Flexural strength, min, psi (kPa) 10(70)25(173)30(208)35(240)50(345)60(414)75(517)40(276)40(27
40、6)45(310)50(345)60(414)75(517)100(690)Water vapor permeance of1.00-in. (25.4-mm) thickness(See Note 5.), max, perm(ng/Pasm2)5.0(287)5.0(287)3.5(201)3.5(201)2.5(143)2.5(143)2.5(143)1.5(86)1.5(86)1.5(86)1.5(86)1.1(63)1.1(63)1.1(63)Water absorption by totalimmersion, max, volume %4.0 4.0 3.0 3.0 2.0 2.
41、0 2.0 0.3 0.3 1.0 0.3 0.3 0.3 0.3Dimensional stability (changein dimensions), max,%2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0Oxygen index, min, volume % 24.0 24.0 24.0 24.0 24.0 24.0 24.0 24.0 24.0 24.0 24.0 24.0 24.0 24.0Density, min, lb/ft3 (kg/m3) 0.70(12)0.90(15)1.15(18)1.35(22)1.80
42、(29)2.40(38)3.00(48)1.20(19)1.30(21)1.60(26)1.45(23)1.80(29)2.20(35)3.00(48)TABLE 2 Common Dimensions of RCPS Thermal InsulationType XI, I, VIII, II, IX, XIV, XV X, IV, XII VI, VII V XIIIWidth, in. (mm) 12 to 48 (305 to 1219) 16, 24, 48 (406, 610, 1219) 24 (610) 16 (406) 14 to 20 (356 to508)Length,
43、in. (mm) 48 to 192 (1219 to 4877) 48, 96 108 (1219, 2438, 2743) 48, 96, (1219, 2438) 96 (2438) 36 to 112 (914 to2845)Thickness, in. (mm) 38 to 24 (9.5 to 610) 12 to 4 (13 to 102) 1 to 4 (25 to 102) 1 to 4 (25 to 102) 7 to 10 (178 to254)C578 15b35.1.13 Type XIIISpecial ordering information. In additi
44、on to other applicable requirements in Section 5, acquisitiondocuments for Type XIII thermal insulation shall specify if presence of surface skins is required.6. Materials and Manufacture6.1 RCPS thermal insulation shall be formed by the expansion of polystyrene resin beads or granules in a closed m
45、old, or bythe expansion of polystyrene base resin in an extrusion process. RCPS thermal insulation shall be of uniform density and haveessentially closed cells. All RCPS thermal insulation shall contain sufficient flame retardants to meet the oxygen indexrequirements of Table 1.7. Physical Requireme
46、nts7.1 Inspection Requirements:7.1.1 The physical requirements listed in this section are defined as inspection requirements (refer to Practice C390).7.1.2 All dimensional requirements are described in Section 8.7.1.3 All workmanship, finish, and appearance requirements are described in Section 9.7.
47、1.4 Density shall be in accordance with Table 1.NOTE 2For lots of 150 units or less, the tightened inspection sampling plan in Practice C390 will be followed.7.2 Qualification Requirements:7.2.1 The physical properties listed in this section of the specification are defined as qualification requirem
48、ents (refer to PracticeC390). Thermal resistance, compressive resistance, flexural strength, water vapor permeance, water absorption, dimensionalstability, and oxygen index shall be in accordance with Table 1. The average test value based upon testing the number of testspecimens required by the spec
49、ified test method for each physical property or Section 11 of this specification shall be used todetermine compliance.7.2.2 The mean thermal resistance of the material tested shall not be less than the minimum value identified in Table 1. Thethermal resistances of individual specimens tested shall not be less than 90 % of the minimum value identified in Table 1.7.2.2.1 Test 1 in. (25.4 mm) thick specimens for determination of compliance with thermal resistance, compressive resistance,water vapor permeance, wate