1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS EN 15815:2011Polymer modifiedbituminous thick coatings forwaterproofing Resistance tocompressionBS EN 15815:2011 BRITISH STANDARDNational forewordThis British Standard is the
2、UK implementation of EN 15815:2011. The UK participation in its preparation was entrusted to TechnicalCommittee B/546, Flexible sheets for waterproofing and water vapour control.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does no
3、t purport to include all the necessary provisions of a contract. Users are responsible for its correct application. BSI 2011 ISBN 978 0 580 62266 3 ICS 91.100.50 Compliance with a British Standard cannot confer immunity from legal obligations.This British Standard was published under the authority o
4、f the Standards Policy and Strategy Committee on 31 August 2011.Amendments issued since publicationDate T e x t a f f e c t e dBS EN 15815:2011EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 15815 March 2011 ICS 91.100.50 English Version Polymer modified bituminous thick coatings for waterproof
5、ing - Resistance to compression Revtements bitumineux pais modifis aux polymres pour impermabilisation - Rsistance la compression Kunststoffmodifizierte Bitumendickbeschichtungen zur Bauwerksabdichtung - Bestndigkeit gegen Stauchung This European Standard was approved by CEN on 13 February 2011. CEN
6、 members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on appl
7、ication to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Ma
8、nagement Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Neth
9、erlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2011 CEN All rights of exploitation
10、 in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 15815:2011: EBS EN 15815:2011EN 15815:2011 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Terms and definitions .44 Principle 45 Apparatus .46 Test specimens 46.1 General 46.2 Preparation .56.3 D
11、imensions of the test specimens.56.4 Conditioning of test specimens .57 Procedure .57.1 Test conditions 57.2 Procedure .58 Expression of results and precision 68.1 Expression of results 68.2 Precision .69 Test report 7BS EN 15815:2011EN 15815:2011 (E) 3 Foreword This document (EN 15815:2011) has bee
12、n prepared by Technical Committee CEN/TC 361 “Project Committee Polymer modified bituminous thick coatings for waterproofing Definitions/requirements and test methods”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publica
13、tion of an identical text or by endorsement, at the latest by September 2011, and conflicting national standards shall be withdrawn at the latest by September 2011. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELE
14、C shall not be held responsible for identifying any or all such patent rights. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic
15、, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. BS EN 15815:2011EN 15815:2011 (E) 4 1 Scope This European S
16、tandard specifies a procedure for determining the resistance to compression of polymer modified bituminous thick coatings for waterproofing. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited
17、applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 206-1, Concrete Part 1: Specification, performance, production and conformity FprEN 15814:2011, Polymer modified bituminous thick coatings for waterproofing Definitions and requireme
18、nts ISO 554, Standard atmospheres for conditioning and/or testing Specifications 3 Terms and definitions For the purposes of this document, the terms and definitions given in FprEN 15814:2011 apply. 4 Principle After coating the substrate and conditioning the test specimen is placed in a test rig. A
19、fter then the surface of the coated substrate is stressed with a constant load till a stabilization of the reduction of thickness is reached. 5 Apparatus 5.1 Flat base with a diameter equal to or greater than 10 mm (accuracy of 10 m) to measure the thickness of layers prior to loading. 5.2 Test rig,
20、 capable of exerting a constant pressure on a surface over an extended period of time. 5.3 Extensometer or vernier calliper (accuracy of 10 m), measuring marks, micrometer. 5.4 Metal or a plastic frame or a screed template. 5.5 Concrete support/loading platens with an area greater or equal than 20 c
21、m 20 cm and with a thickness greater or equal than 4 cm thick, minimum 28 days old, minimum quality C 20/25 in accordance with EN 206-1. The upper and lower surfaces of the support/platens are ground so as to be flat and parallel to each other. 6 Test specimens 6.1 General Squared test specimen with
22、 a size of approximately 20 cm 20 cm. BS EN 15815:2011EN 15815:2011 (E) 5 6.2 Preparation The supports and the components of the polymer modified bituminous thick coatings shall be conditioned prior to the preparation of the specimens in a normal climate of (23 2) C and a relative humidity of (50 5)
23、 % in accordance with ISO 554 for at least 24 h. The polymer modified bituminous thick coating shall be prepared at room temperature as specified by the manufacturer of the product and applied to the ground surface of the concrete support over an area of 20 cm 20 cm, also at a room temperature. The
24、thickness of the wet layer shall be such that the thickness of the dry layer corresponds to that specified by the manufacturer for each type of use after drying (at least 3 mm or 4 mm) within a tolerance of 10 %. A frame of the appropriate height or screed template, in which the layer is struck off,
25、 shall be used to obtain the required thickness. The specimens shall be left to dry in a normal climate of (23 2) C and a relative humidity of (50 5) % in accordance with ISO 554 for 28 days prior to testing. 6.3 Dimensions of the test specimens The thickness of the dry layer shall be measured using
26、 vernier callipers permitting a reading to 0,1 mm. 12 readings shall be taken. The highest and lowest values shall be ignored and the mean value calculated from the remaining 10 values. 6.4 Conditioning of test specimens The test specimens shall be stored for at least 28 days at a normal climate (23
27、 2) C and a relative humidity of (50 5) % prior to testing. 7 Procedure 7.1 Test conditions The test shall be carried out at (23 2) C. 7.2 Procedure The thicknesses of the layer shall be determined at sixteen measuring points distributed evenly over the surface of the specimen, but at a distance of
28、not less than 2 cm from the edges of the specimen The mean thickness of the dry layer shall then be determined (Sv). A minimum of three specimens shall be tested in each test. Several specimens may be stacked and tested simultaneously for convenience. The surface of the coating shall be prevented fr
29、om adhering to the support of the specimen above it or to the loading platens by inserting a suitable separating layer (e.g. silicone-coated paper) between the specimens. Specimens tested simultaneously shall be placed in a suitable test rig to prevent any lateral displacement of the specimens occur
30、ring during the test and to ensure an evenly distributed application of force over the entire surface of the specimens. Two gauge marks shall be made on the four sides of the specimen supports and loading platens at a distance of one third of the side length from the edges to enable the mean change
31、in the thickness of the layers of each specimen during the test to be determined. BS EN 15815:2011EN 15815:2011 (E) 6 After the specimens have been mounted in the test rig, the distance between the gauge marks on each specimen shall be measured to 10 m. A preliminary load of 0,01 MN/m shall then be
32、applied. The distances between the gauge marks shall be measured again immediately afterwards. The mean change in the thickness of each specimen (S0) shall be determined from the differences between individual measurements. The thickness of the layers at the start of the test (S0) is therefore: 0v0-
33、 SSS = (1) where S0is the thickness of the layer at the start of the test, in millimetre (mm); Svis the mean thickness of the dry layer, in millimetre (mm); S0is the mean change of the thickness, in millimetre (mm). The main load is then applied in accordance with FprEN 15814. The layer thickness of
34、 each specimen shall be measured daily. The test is deemed to have been passed if the mean change in the thickness of each specimen after 5 days (S5) is less than 50 % of the initial thickness of the layer and the difference between the changes over the last three days, e.g. between the 2ndday and 5
35、thday (S5 S2), does not exceed 3 % (stabilisation). If the change over three days exceeds 3 %, the test can be extended up to a maximum of 40 days or until the change over three days (Sn Sn-3) is 3 % for an overall change of 50 %. All three specimens shall fulfil these requirements. 8 Expression of
36、results and precision 8.1 Expression of results The mean deviation of the thickness of each specimen (Sn) from the initial thickness (S0) at each measurement n is expressed as the relative change in the thickness of the layer Sn. ()100/0nn= SSS (2) where Snis the relative change of the thickness of
37、the layer, in percent (%); Snis the mean deviation of the thickness of each specimen, in millimetre (mm); S0is the initial thickness, in millimetre (mm). The test results for each specimen shall be recorded (or plotted, as required) over time and analysed. 8.2 Precision Precision data are currently
38、not available. BS EN 15815:2011EN 15815:2011 (E) 7 9 Test report The test report shall include at least the following information: a) all details necessary to identify the product tested; b) a reference to this European Standard (i.e. EN 15815) and any deviation from it; c) details of preparation of
39、 test specimens in accordance with Clause 6; d) test procedure including: test pressure; deviation of test conditions; e) the test results in accordance with Clause 8; f) the dates of the tests. This page deliberately left blankThis page deliberately left blankBSI is the independent national body re
40、sponsible for preparing British Standardsand other standards-related publications, information and services. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter.British Standards Institution (BSI)raising standards worldwideBSI Group Head
41、quarters389 Chiswick High Road London W4 4AL UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 Standards are updated by amendment or revision. Users of British Stan-dards should make sure that they possess the latest amendments or editions.It is the constant aim of BSI to improve the quality of our produ
42、cts and serv-ices. We would be grateful if anyone finding an inaccuracy or ambiguity whileusing this British Standard would inform the Secretary of the technical com-mittee responsible, the identity of which can be found on the inside frontcover.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001BSI o
43、ffers Members an individual updating service called PLUS which ensuresthat subscribers automatically receive the latest editions of standards.Tel: +44 (0)20 8996 7669 Fax: +44 (0)20 8996 7001Email: Buying standardsYou may buy PDF and hard copy versions of standards directly using acredit card from t
44、he BSI Shop on the website addition all orders for BSI, international and foreign standards publicationscan be addressed to BSI Customer Services.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001Email: In response to orders for international standards, it is BSI policy tosupply the BSI implementati
45、on of those that have been publishedas British Standards, unless otherwise requested.Information on standardsBSI provides a wide range of information on national, Europeanand international standards through its Knowledge Centre.Tel: +44 (0)20 8996 7004 Fax: +44 (0)20 8996 7005Email: Various BSI elec
46、tronic information services are also available whichgive details on all its products and services. Tel: +44 (0)20 8996 7111 Fax: +44 (0)20 8996 7048Email: BSI Subscribing Members are kept up to date with standardsdevelopments and receive substantial discounts on the purchase priceof standards. For d
47、etails of these and other benefits contact Membership Ad-ministration. Tel: +44 (0)20 8996 7002 Fax: +44 (0)20 8996 7001 Email: Information regarding online access to British Standards via BritishStandards Online can be found at information about BSI is available on the BSI website at www.bsi- sub
48、sists in all BSI publications. BSI also holds the copyright,in the UK, of the publications of the international standardization bodies. Ex-cept as permitted under the Copyright, Designs and Patents Act 1988 no ex-tract may be reproduced, stored in a retrieval system or transmitted in anyform or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the freeuse, in the course of implementing the standard of necessary details such a