SAE AMS 3678 11-2010 Type 11 10% Aromatic Polymer Filled Virgin Polytetrafluoroethylene (PTFE) Moldings or Extrusions《11型 10%芳香族聚合物填充原聚四氟乙烯(PTFE)模制品或挤压制品》.pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、 from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2010 SAE International All rights reserved. No part of this publication

3、may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside

4、USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS3678/11AEROSPACEMATERIALSPECIFICATIONAMS3678/11 Issued 2010-11 Type 11 10% Aromatic Polym

5、er Filled Virgin Polytetrafluoroethylene (PTFE) Moldings or Extrusions RATIONALE This document addresses the specific properties of 10% aromatic polymer filled virgin polytetrafluoroethylene. 1. SCOPE 1.1 Form This specification covers a polytetrafluoroethylene (PTFE) resin filled with 10% aromatic

6、polymer in the form of extruded or molded rods or tubes which are sintered after molding or, in the case of extrusions, sintered during the extrusion process. 1.2 Application These products have been used typically for seal components in both static and dynamic applications requiring excellent wear

7、resistance against soft metals such as stainless steels and dimensional stability up to 450 F (232 C), but usage is not limited to such applications. Each application should be considered individually. 2. APPLICABLE DOCUMENTS See AMS3678. 3. TECHNICAL REQUIREMENTS 3.1 Basic Specification The complet

8、e requirements for procuring the products described herein shall consist of this document and the latest issue of the basic specification, AMS3678. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE

9、 AMS3678/11 Page 2 of 23.2 Material All products shall be molded or extruded from virgin polytetrafluoroethylene (PTFE) powder conforming to ASTM D 4894, Type II or Type IV, uniformly blended with the specified fillers. The blended powder shall consist of 10% 2% aromatic polymer and the remainder vi

10、rgin PTFE powder, filler percentage measured by weight. 3.2.1 Fillers 3.2.1.1 Aromatic Polymer It is recommended that the aromatic polymer should be highly crystalline, uniform in size and have excellent thermal stability. It shall be P-Oxybenzoyl Homopolyester or equivalent. 3.3 Properties The prod

11、uct shall conform to the requirements shown in Table 1. TABLE 1 - MATERIAL PROPERTY REQUIREMENTS Property Requirement Test Method 3.3.1 Tensile Strength, min 3000 psi (20.7 MPa) ASTM D 4745 3.3.2 Elongation, min 250% ASTM D 4745 3.3.3 Specific Gravity 1.95 to 2.15 ASTM D 792 3.3.4 Dimensional Stabil

12、ity 0.002 inch per 1 inch, max measured on circumference 4.5.3.1 of AMS3678 3.3.5 Color Tan to Dark Brown and color should be uniform throughout 4. QUALITY ASSURANCE PROVISIONS See AMS3678. 5. PREPARATION FOR DELIVERY See AMS3678. 6. ACKNOWLEDGMENT See AMS3678. 7. REJECTIONS See AMS3678. 8. NOTES See AMS3678. PREPARED BY AMS COMMITTEE “P” Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-