SANS 257-2008 Wax shoe polish《蜡质鞋油》.pdf

1、 Collection of SANS standards in electronic format (PDF) 1. Copyright This standard is available to staff members of companies that have subscribed to the complete collection of SANS standards in accordance with a formal copyright agreement. This document may reside on a CENTRAL FILE SERVER or INTRA

2、NET SYSTEM only. Unless specific permission has been granted, this document MAY NOT be sent or given to staff members from other companies or organizations. Doing so would constitute a VIOLATION of SABS copyright rules. 2. Indemnity The South African Bureau of Standards accepts no liability for any

3、damage whatsoever than may result from the use of this material or the information contain therein, irrespective of the cause and quantum thereof. ISBN 978-0-626-21944-4 SANS 257:2008Edition 2.3 SOUTH AFRICAN NATIONAL STANDARD Wax shoe polish Published by SABS Standards Division 1 Dr Lategan Road Gr

4、oenkloof Private Bag x191 Pretoria 0001 Tel: +27 12 428 7911 fax: +27 12 344 1568 www.sabs.co.za SABS SANS 257:2008 Edition 2.3 Table of changes Change No. Date Scope Amdt 1 2004 Amended to change the designation of SABS standards to SANS standards, to change the definition of acceptable, to change

5、the descriptive reference of the reflectometer to SANS 2813 and to delete the footnote that refers to appendix A. Amdt 2 2006 Amended to delete reference to SANS 716 and to remove reference to legislation from the text. Amdt 3 2008 Amended to update the applicable standards. Foreword This South Afri

6、can standard was approved by National Committee SABS SC 1006A, Detergents, polishes and other chemicals Polishes, in accordance with procedures of SABS Standards Division, in compliance with annex 3 of the WTO/TBT agreement. This document was published in August 2008. This document supersedes SANS 2

7、57:2006 (edition 2.2). A vertical line in the margin shows where the text has been technically modified by amendment No.s 1, 2 and 3. A reference is made in 4.2 to “national regulations and statutory requirements on trade metrology”. In South Africa this means the Trade Metrology Act, 1973 (Act No.

8、77 of 1973). SANS 257:2008 Edition 2.3 1 Contents Page Foreword 1 Scope 3 2 Definitions 3 3 Requirements 3 4 Packing and marking. 5 5 Sampling and compliance with the specification. 5 6 Inspection and methods of test . 6 6.1 Inspection. 6 6.2 Conditioning of samples. 6 6.3 Heat-cool stability. 6 6.4

9、 Penetration. 6 6.5 Performance. 6 6.6 Non-volatile matter content 7 6.7 Softening point of the non-volatile matter 7 6.8 Ash content of the non-volatile matter . 7 6.9 Water content. 7 Appendix A Applicable standards 8 Appendix B Notes to purchasers . 8 SANS 257:2008 Edition 2.3 2 This page is inte

10、ntionally left blank SANS 257:2008 Edition 2.3 3 Wax shoe polish 1 Scope 1.1 This specification covers wax polish suitable for use on shoes, boots, and leather goods. NOTE a) The standards referred to in the specification are given in appendix A. b) Requirements that must be specified by the purchas

11、er are listed in appendix B. 2 Definitions 2.1 For the purposes of this specification the following definitions shall apply: acceptable acceptable to the authority administering this standard or to the parties concluding the purchase contract, as relvant Amdt 1 batch the material from a single mix l

12、ot the quantity of wax polish from the same batch and from one manufacturer that is submitted at any one time for inspection and testing 3 Requirements 3.1 General The polish shall be either a solvent polish or an emulsion polish. It shall consist essentially of a wax or blend of waxes in an organic

13、 solvent in the case of a solvent polish and water and an organic solvent in the case of an emulsion polish. It shall be a homogeneous smooth paste free from lumps and granulations. It shall not be harmful to surfaces of the type to which it is intended to be applied. It shall not be irritating to t

14、he normal skin, and its vapours shall not be toxic to human beings. The odour of the polish shall be acceptable. 3.2 Freedom from grit When approximately 0,1 g of the polish is rubbed between two glass slides there shall be no evidence of grit. SANS 257:2008 Edition 2.3 4 3.3 Colour and intensity of

15、 colour The colour of the polish shall be as specified by the purchaser, and the intensity of the colour shall be acceptable. 3.4 Heat-cool stability When tested in accordance with 6.3, the polish shall not show signs of separation. 3.5 Penetration The penetration of the polish, determined in accord

16、ance with 6.4, shall be 40 70 units (tenths of a millimetre) at 20 C and not more than 80 units (tenths of a millimetre) at 35 C. 3.6 Performance When tested in accordance with 6.5, the polish shall apply evenly and shall dry to a non-tacky film, and on buffing, the 60 specular gloss of the leather

17、shall increase by at least 5 units. When a second quantity of polish is applied, allowed to dry, and buffed, there shall be no decrease in the gloss. 3.7 Non-volatile matter 3.7.1 Content The non-volatile matter content of the polish, determined in accordance with 6.6, shall be at least 25,0 % (m/m)

18、. 3.7.2 Properties The non-volatile matter of the polish shall comply with the requirements given in table 1. Table 1 Properties of the non-volatile matter 1 2 3 Property Requirement Test method subsection Softening point, C, min. Ash content, % (m/m), max. 75 1,0 6.7 6.8 3.8 Solvent The solvent sha

19、ll be mineral turpentine. Amdt 2 3.9 Water content of solvent polish The water content of solvent polish, determined in accordance with 6.9, shall not exceed 1,0 % (m/m). SANS 257:2008 Edition 2.3 5 3.10 Storage stability After storage at room temperature in two original unopened containers, the pol

20、ish a) in one container shall, after 6 months, show no more than 1 mm shrinkage from the side of the container at any point, and b) in the other container shall, after 12 months, comply with all the other requirements of the specification. 4 Packing and marking 4.1 Packing The wax polish shall be pa

21、cked in containers of metal, if specified by the purchaser, of glass, or a plastics material1). It shall be so packed as to prevent leakage and deterioration of the product, and the containers shall be strong enough to withstand normal handling and transportation. Each container shall contain polish

22、 from the same batch only. These containers may be packed in bulk packages, but only containers of the same size and containing polish from the same batch shall be packed together in a bulk package. 4.2 Marking Each container and each bulk package shall bear in prominent, legible, and indelible mark

23、ing the information required in terms of the regulations promulgated under the current relevant national regulations and statutory requirements on trade metrology. Amdt 2 a) Containers 1) The name or trade name or trade mark of the manufacturer, or a combination of these; 2) words indicating that th

24、e polish is intended for use on shoes; 3) the colour; 4) if larger than 1 L, the batch identification; 5) the net volume of the contents. b) Bulk-packages 1) The information in (a)(1) and (3) 2) the batch identification; 3) the number of containers and their size. 5 Sampling and compliance with the

25、specification NOTE This section applies to the sampling for inspection and testing before acceptance or rejection of single lots (consignments) in cases where no information about the implementation of quality control or testing during manufacture is available to help in assessing the quality of the

26、 lot. It is also used as the procedure for adjudicating in cases of dispute. 1) It is not recommended that the container be of polyethylene. SANS 257:2008 Edition 2.3 6 5.1 Sampling The following sampling procedure shall be applied in determining whether a lot complies with the appropriate requireme

27、nts of the specification. The sample so drawn shall be deemed to represent the lot. After inspecting the lot for compliance with the appropriate requirements of section 4, take from it at random at least six containers and mark each container with the date of sampling and the batch number. 5.2 Compl

28、iance with the specification The lot shall be deemed to comply with the requirements of the specification if, on inspection of the lot and inspection and testing of the samples taken in accordance with 5.1, they are found to comply with all the relevant requirements of the specification. 6 Inspectio

29、n and methods of test 6.1 Inspection After conditioning (see 6.2), check the contents of each container in the sample taken in accordance with 5.1 for compliance with those requirements of the specification compliance with which is not assessed by the tests given in 6.3 6.9 (inclusive). 6.2 Conditio

30、ning of samples Condition all the samples at room temperature for at least 7 d before testing. 6.3 Heat-cool stability Use SANS 5976. 6.4 Penetration Use SANS 5977. 6.5 Performance 6.5.1 Apparatus a) Standard leather tiles, of leather that complies with the requirements of CKS 471, of size 100 mm x

31、100 mm, and having an initial 60 specular gloss, after buffing (see 6.5.2(a), of at least 10 units. b) A glossmeter as described in SANS 2813. Amdt 1 6.5.2 Procedure a) Buff the smooth surface of the tile with clean cotton wool using moderate pressure until a constant 60 specular gloss, determined i

32、n accordance with SANS 2813 is obtained. b) Evenly apply 0,1 g of the polish over the prepared surface of the tile with clean cotton wool. c) Allow to dry for 5 min. Check for compliance with the relevant requirements of 3.6. SANS 257:2008 Edition 2.3 7 d) Using clean cotton wool, buff the tile to a

33、 constant 60 specular gloss. Record the gloss value. e) Repeat steps (b) (d). 6.6 Non-volatile matter content Use SANS 5981. Amdt 3 6.7 Softening point of the non-volatile matter Use SANS 5980. 6.8 Ash content of the non-volatile matter Use SANS 5981. 6.9 Water content Use SANS 5982. SANS 257:2008 E

34、dition 2.3 8 Appendix2)A Amdt 1 Applicable standards Reference is made to the latest issues of the following standards: CKS 471, Side upper leather (with a smooth corrected grain). Deleted by amendment No. 2. Amdt 2 SANS 2813/ISO 2813, Paints and varnishes Determination of specular gloss of non-meta

35、llic paint films at 20, 60 and 85. Amdt 1 SANS 5976, Heat-cool stability of wax polishes. SANS 5977, Penetration of wax (paste) polishes. SANS 5979 (SABS SM 979), Non-volatile matter content of wax polishes. Amdt 3 SANS 5980, Softening point of the non-volatile matter of wax polishes. SANS 5981, Wax

36、 polishes Non-volatile matter content and the ash content of non-volatile matter. Amdt 3 SANS 5982, Water content of solvent-based wax polishes. Appendix B Notes to purchasers The following requirements must be specified in tender invitations and in each order or contract: a) When relevant, that a s

37、pecific type of polish is required (see 3.1). b) The colour of the polish (see 3.3). c) When relevant, the material of the container in which the polish is packed (see 4.1). SABS 2 The information in the appendices is additional to that in the specification and has been included purely for information and guidance. Amdt 1