AECMA PREN 3544-3-2002 (CANCELLED) Aerospace Series Titanium and Titanium Alloys Wrought Products Technical Specification Part 3 Bar and Section Edition P 2 [Replaced By ASD-STAN P.pdf

1、AECMA STANDARD NORME AECMA AECMA NORM Withdrawal approved 31 December 2002 prEN 3544-3 Edition P 2 December 2002 Material Domain Comments should be sent within six months after the date of publication to AECMA-STAN PUBLISHED BY THE EUROPEAN ASSOCIATION OF AEROSPACE INDUSTRIES - STANDARDIZATION nfd G

2、ulledelle 94 - 8-1200 Brussels - Tel. + 32 2 775 81 10 - Fax. + 32 2 775 81 11 - www.aecma-stan.org Descriptors: Supersedes edition PI April 1994 ENGLISH VERSION Aerospace series Titanium and titanium alloys Wrought products Technical specification Part 3: Bar and section Srie arospatiale Titane et

3、alliages de titane Produits corroys Spcification technique Partie 3: Barres et profils Luft- und Raumfahrt Titan und Titanlegierungen Kneterzeugnisse Technische Lieferbedingungen Teil 3: Stangen und Profile This “Aerospace Series“ Prestandard has been drawn up under the respo European Association of

4、 needs of the European concerned Domain Subsequent to the publication of shall not be changed to an extent that re-identification of the standard. Replace page I of the previous edition by this page 1 Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under lic

5、ense with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PRENr3544 PART*3 9V m 3404589 0062286 9T5 m Page 2 prEN 3544-3 : 1994 Contents list 1 Scope 2 Normative references 3 Manufacture 4 Inspection and testing 5 Marking Copyright Association Europeene de

6、s Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PRENg3544 PART*3 94 3404589 00b2287 831 Page 3 prEN 3544-3 : 1994 1 Scope This standard specifies the particular requirements for tit

7、anium and titanium alloy bar (including bar for fasteners) and section and shall be used in conjunction with EN 3544-1. 2 Normative references EN 2002-1 EN 2002-2 EN 2002-5 EN 2002-8 EN 2002-16 EN 2002-20 EN 2003-8 EN 2003-9 EN 2954-1 EN 31 14-1 EN 3238 EN 3544-1 EN 3683 EN 3684 Aerospace series - T

8、est methods for metallic materials - Part 1 : Tensile testing at ambient temperature i Aerospace series - Test methods for metallic materials - Part 2 : Tensile testing at elevated temperature Aerospace series - Test methods for metallic materials - Part 5 : Uninterrupted creep and rupture testing 1

9、 Aerospace series - Test methods for metallic materials - Part 8 : Micrographic determination of grain size i Aerospace series - Test methods for metallic materials - Part 16 : Dye penetrant testing 2) Aerospace series - Test methods for metallic materials - Part 20 : Eddy current testing of circula

10、r cross-section tubes 2, Aerospace series - Test methods for steel, titanium, titanium alloys, aluminium alloys and heat resisting alloy products - Part 8 : Ultrasonic inspection of billets, bars, plates and forgings 2, Aerospace series - Test methods for titanium and titanium alloys - Part 9 : Dete

11、rmination of surface contamination 2, Aerospace series - Macrostructure of titanium alloy wrought products - Part 1 : General requirements 2) Aerospace series - Microstructure of a + 13 - titanium alloy wrought products - Part 1 : General requirements 2, Aerospace series - Shear test for rivet wires

12、 and rivets in metallic materials 2, Aerospace series - Titanium and titanium alloys - Wrought products - Technical specification - Part 1 : General requirements Aerospace series - Titanium and titanium alloys - Wrought products - Determination of primary a-content - Point count method and line inte

13、rcept method 2, Aerospace series - Titanium and titanium alloys - Wrought products - Determination of -transus temperature - Metallographic method 2, 1 1 Published as AECMA Prestandard at the date of the publication of this standard 2) In preparation at the date of publication of this standard Copyr

14、ight Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PRENx3544 PARTL3 94 3404589 O062288 778 Page 4 prEN 3544-3 : 1994 3 Manufacture Unless otherwise specifi

15、ed by the material standard or order, the method of production shall be at the option of the manufacturer. Unless otherwise specified by the material standard or order, products shall be supplied in the descaled or machined condition. Any metallurgical defects such as cracks, burrs, etc., shall be r

16、emoved from the edges and ends of the product by a method agreed between manufacturer and purchaser. Straightening and stress relieving operations shall not cause any defects prejudicial to the intended use. 4 Inspection and testing 4.1 Non-destructive tests 4.1 .l Dimensions and tolerances Dimensio

17、ns shall conform to the requirements of the order. Tolerances shall conform to the relevant dimensional standard stated by the material standard or order. The frequency of examination adopted by the manufacturer shall be sufficient to enable him to certify compliance with the requirements. 4.1.2 Int

18、ernal defects When requirsd by the material standard or order, products shall be ultrasonically tested in accordance with EN 2003-8. Bar 12 mm in diameter or minor sectional dimension shall be ultrasonically tested in the delivery condition. Bar with dimensions I 12 mm shall be tested at an intermed

19、iate stage of manufacture. For section the test method and area to be checked shall be stated on the order. Unless otherwise agreed between the manufacturer and the purchaser, each bar or section shall be 1 O0 % tested. The level of acceptance for bars 12 mm 5 D I 225 mm shall be class 5 (1,2 mm FBH

20、) in accordance with EN 2003-8, unless otherwise specified by the material standard or order. 4.1.3 External defects 4.1 3.1 Visual examination Bar and section shall be examined for surface defects in the delivery condition by visual inspection after etching. Each bar or section shall be 100 % inspe

21、cted. Bar and section shall be clean and free from harmful defects (such as cracks, laps, seams, segregations or inclusions). The presence of surface segregation or inclusions shall require further investigation by a method agreed between the manufacturer and purchaser. Copyright Association Europee

22、ne des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PREN*:3544 PART*3 94 3404589 0062289 604 m Minor transverse dimension of product Direction of test sample Page 5 prEN 3544-3 : 1

23、994 Location of test piece 4.1.3.2 Dye penetrant inspection D 75 Bar for manufacture of fasteners shall be penetrant tested after etching in accordance with EN 2002-16. Transverse (TI or Mid radius Longitudinal (LI Bar for machining and section shall be penetrant tested after etching in accordance w

24、ith EN 2002-16, when required by the material standard or order. When penetrant testing is required by the material standard or order : - products supplied in the ground condition shall be penetrant tested before final grinding; - each bar or section shall be 100 % tested; - products shall be free f

25、rom harmful defects (such as cracks, laps, seams, etc). NOTE : Eddy current based on EN 2002-20 may also be used as an alternative test. 4.1.3.3 Surface dressing Local dressing may be carried out by the manufacturer provided the dimensions of the product remain within the tolerance limits and within

26、 the conditions agreed between the manufacturer and the purchaser . Local dressing shall not affect the sensitivity of any ultrasonic test which may be required. The dressed area shall be reinspected to verify that defects have been removed. 4.2 Mechanical tests When required by the material standar

27、d or order, mechanical testing shall be carried out in accordance with 4.2.1 to 4.2.3. Unless otherwise required by the material standard or order, the location and orientation of test pieces shall be as defined in table 1. Table 1 D I30 I Longitudinal (LI I Centre I 30 100 100 % One end D2 20 100 %

28、 One end All 10 % One end 4.2.2 Creep and creep rupture tests Testing shall be carried out in accordance with EN 2002-5. Tests shall be performed at a frequency of one per batch. 4.2.3 Shear tests Testing shall be carried out in accordance with EN 3238. Tests shall be performed at a frequency of one

29、 per batch. 4.3 Metallographic examination 4.3.1 Macrostructure When required by the material standard or order, samples from bar and section shall be etched and visually examined in accordance with EN 2954-1. Tests shall be performed at the following frequency : A transverse slice shall be selected

30、 at a convenient stage in manufacture from locations corresponding to the top and bottom end of each ingot. In addition, transverse samples shall subsequently be taken from finished bars and sections at the frequency given in table 2. Table 2 Alternatively, at the option of the manufacturer, transve

31、rse samples shall be taken from each end of each manufactured product prior to cutting to length. The level of acceptance shall meet the requirements of the material standard. If any sample fails to meet the requirements, the corresponding end of the bar or section may be cut back and retested. If s

32、amples were originally selected at a frequency of less than 100 %, all the remaining bars shall be tested. 4.3.2 Microstructure When required by the material standard or order, the samples from bar and section shall be etched and examined in accordance with EN 31 14-1. Unless otherwise specified by

33、the material standard, the location and frequency of micrographic test pieces for bars and section shall be as defined in table 3. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted w

34、ithout license from IHS-,-,-I Bar Section CEN PREN83544 PART83 94 3404589 0062293 mm All 10 % 262 Page 7 prEN 3544-3 : 1994 Table 3 Frequency Diameter or equivalent diameter Location of test piece One end longitudinal and transverse cut in the centre Unless otherwise specified, samples from bar and

35、section made from a + - titanium alloys shall show a globular-lamellar microstructure, resulting from alpha-beta processing. The microstructure shall meet the requirements of the material standard or order. 4.3.3 Grain size When required by the material standard or order, grain size shall be determi

36、ned in accordance with EN 2002-8. At least two of the samples macro etched in accordance with 4.3.1 shall be selected. The samples shall be from those exhibiting the coarsest grain size when macrographically examined. Longitudinal micro sections shall be prepared from each selected sample and the gr

37、ain size determined. The results shall meet the requirements of the material standard or order. 4.3.4 Primary-a content When required by the material standard or order, the primary-a content shall be determined in accordance with EN 3683. Unless otherwise agreed between the manufacturer and the purc

38、haser, at least one sample per batch shall be tested. The sample shall be taken from the centre of the product. The results shall meet the requirements of the material standard or order. 4.3.5 -transus temperature When required by the material standard or order, the -transus temperature shall be det

39、ermined in accordance with EN 3684. Unless otherwise agreed between the manufacturer and purchaser, at least two samples per ingot, representing top and bottom of the ingot, shall be used for the determination. The -transus temperature shall meet the requirements of the material standard or order. 4

40、.3.6 Surface contamination When required by the material standard or order, the extent of surface contamination shall be determined in accordance with EN 2003-9. Samples cut from bar and section shall be free from brittle, oxygen rich diffusion zones which adversely affect the machinability. Copyrig

41、ht Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PRENS3544 PARTS3 4 m 3404589 00b2292 IT9 m Page 8 prEN 3544-3 : 1994 5 Marking All products shall carry th

42、e following identification marking : - material standard number; - delivery condition code; - batch number; - manufacturers name and, where appropriate, identity of the plant; - inspectors stamp. Bar and section 20 mm diameter or minor cross section shall be bundled and a durable label securely atta

43、ched bearing the identification marking. For bar and section 2 20 mm diameter, at least the material standard number, the batch number and the inspectors stamp shall be hard stamped on one end of each product. The method of providing the remaining markings shall be at the option of the manufacturer.

44、 I Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-CEN PRENr3544 PARTa3 94 = 3404589 0062293 035 Chemical composition Hydrogen content Dimensions and t

45、olerances Internal defects External defects Tensile at ambient Page 9 prEN 3544-3 : 1994 Method See EN 3544-1 See EN 3544-1 4.1.1 Appropriate method 4.1.2 Ultrasonic 4.1.3.1 Visual after etching Dye penetrant or eddy current 4.1.3.2 inspection 4.2.1 Tensile Table 4 - Summary of requirements temperat

46、ure Tensile at elevated Requirement 1 Clause 4.2.1 Tensile temperature Creep and creep rupture Shear 4.2.2 Creep and creep rupture 4.2.3 Shear Macrostructure 4.3.1 1 Metallography Microstructure Grain size Primary a-content I 4.3.4 I Metallography I I 4.3.2 Metallography 4.3.3 Metallography -transus

47、 temperature Surface contamination Marking Inspection / Test Standard 4.3.5 Metallography 4.3.6 Metallography 5 Visual EN 2003-8 EN 2002-16 or EN 2002-20 EN 2002-1 EN 2002-2 EN 2002-5 EN 3238 EN 2954-1 EN 31 14-1 EN 2002-8 EN 3683 EN 3684 EN 2003-9 Frequency Two per ingot One per batch See 4.1.1 See

48、 4.1.2 100 % of each product One per batch One per batch One per batch One per batch See 4.3.1 See 4.3.2 See 4.3.3 See 4.3.4 See 4.3.5 See 4.3.6 See EN 3544-1 Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-