ASTM A1031-2005 Standard Specification for Steel Sheet and Strip Heavy-Thickness Coils Alloy Drawing Steel and Structural Steel Hot-Rolled《热轧合金钢、拉制钢和结构钢薄板和带材、特厚卷材的标准规范》.pdf

1、Designation: A 1031 05Standard Specification forSteel, Sheet and Strip, Heavy-Thickness Coils, Alloy,Drawing Steel and Structural Steel, Hot-Rolled1This standard is issued under the fixed designation A 1031; the number immediately following the designation indicates the year oforiginal adoption or,

2、in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers hot-rolled, heavy thicknesscoils beyond the size limi

3、ts of Specifications A 506 and A 507.1.2 The product is available in three designations: AlloySteel, Drawing Steel, and Structural Alloy Steel.1.3 Alloy steel is furnished to chemical composition re-quirements and is intended primarily for general or miscella-neous use where bending and moderate for

4、ming is a require-ment.1.4 Drawing steel is produced principally for applicationsinvolving severe cold plastic deformation such as deep drawnor severely formed parts.1.4.1 Drawing steel may be furnished in several conditions,heat treatments, surface finishes, and edges, as specified herein.1.5 Struc

5、tural steel is furnished to chemical compositionrequirements and to specific mechanical property requirementswhich may include tension tests, hardness tests, or othercommonly accepted mechanical tests.1.5.1 The formability of structural steel decreases withincreasing yield strength or hardness. Ther

6、efore, product de-sign in relation to the mechanical properties of the grade usedmust be considered.1.6 This material is available only in coils described asfollows:Product Size Limits, Coils OnlyWidth, in. (mm) Thickness, in. (mm)Strip Over 8 to 12, incl 0.230 to 1.000, incl(Over 200 to 300) (Over

7、6.0 to 25)Sheet Over 12 to 48, incl 0.230 to 1.000, incl(Over 300 to 1200) (Over 6.0 to 25)Sheet Over 48 0.180 to 1.000, incl(Over 1200) (Over 4.5 to 25)1.7 Sheet and strip in coils of sizes noted in 1.6 are coveredby this specification only with the following provisions:1.7.1 The material is not to

8、 be converted into steel plates forstructural or pressure vessel use unless tested in completeaccordance with the appropriate sections of SpecificationsA 6/A 6M (plates provided from coils) or A 20/A 20M (platesproduced from coils). A plate produced in this manner is nolonger governed by this sheet

9、steel specification and since thismaterial is now plate, the appropriate plate standard must nowapply.1.7.2 The dimensional tolerances of Specification A 635/A 635M are applicable to material produced to this specifica-tion.1.7.3 The material is to be fed directly from coils into ablanking press, dr

10、awing or forming operation, tube mill, rollingmill, or sheared or slit into blanks for subsequent drawing orforming.1.8 The values stated in either inch-pound units and SI units(metric) are to be regarded separately as standard. Within thetext the SI units are shown in brackets. The values stated in

11、each system are not exact equivalents; therefore, each systemmust be used independently of each other.2. Referenced Documents2.1 ASTM Standards:2A 6/A 6M Specification for General Requirements forRolled Structural Steel Bars, Plates, Shapes, and SheetPilingA 20/A 20M Specification for General Requir

12、ements forSteel Plates for Pressure VesselsA 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA 505 Specification for Steel, Sheet and Strip, Alloy, Hot-Rolled and Cold-Rolled, General Requirements forA 506 Specification for Alloy and Structural Alloy Steel,Sheet and Strip, Ho

13、t-Rolled and Cold-RolledA 507 Specification for Drawing Alloy Steel, Sheet andStrip, Hot-Rolled and Cold-RolledA 635/A 635M Specification for Steel, Sheet and Strip,Heavy-Thickness Coils, Carbon, Commercial Steel, Draw-ing Steel, Structural, High-Strength Low-Alloy, and High-Strength Low-Alloy with

14、Improved Formability, Hot-Rolled, General Requirements forA 751 Test Methods, Practices, and Terminology for1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.19 on Steel Sheet and Strip.

15、Current edition approved Dec. 1, 2005. Published December 2005. Originallyapproved in 2004. Last previous edition approved in 2004 as A 1031 04.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards v

16、olume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Chemical Analysis of Steel ProductsE

17、29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifications3. General Requirements for Delivery3.1 Material furnished under this specification shall con-form to the applicable requirements of Specification A 505,current edition, unless otherwise provided herein.

18、4. Ordering Information4.1 Orders for material under this specification shall includethe following information, as required, to adequately describethe desired material.4.1.1 ASTM specification number and year of issue,4.1.2 Classification of the material (hot-rolled sheet orhot-rolled strip),4.1.3 C

19、hemical composition (grade),4.1.4 ConditionMaterial in accordance with this specifi-cation is furnished in the hot rolled condition. Pickled (or blastcleaned) must be specified if required. Material ordered aspickled (or blast cleaned) will be oiled unless ordered dry,4.1.5 Heat treatment required,

20、if any,4.1.6 Type of edge must be specified for hot rolled sheetcoils and strip coils, either mill edge or cut edge (sheet), milledge or slit edge (strip),4.1.7 Dimensions (decimal thickness and width of material),4.1.7.1 As agreed upon between the purchaser and theproducer, material ordered to this

21、 specification will be suppliedto meet the appropriate standard or restricted thickness toler-ances shown in Specification A 635/A 635M,NOTE 1Not all producers are capable of meeting all the limitations ofTABLE 1 Standard Steels Commonly Produced for Alloy Steel Sheet and StripUNSDesign.SAENo.Chemic

22、al Composition Ranges and Limits, % (Heat Analysis)ACMnPSSiBNi Cr Mo V. . . E3310 0.08-0.13 0.45-0.60 0.025 0.025 0.15-0.30 3.25-3.75 1.40-1.75 . . . . . .G40120 4012 0.09-0.14 0.75-1.00 0.025 0.025 0.15-0.30 . . . . . . 0.15-0.25 . . .G41180 4118 0.18-0.23 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.40

23、-0.60 0.08-0.15 . . .G41300 4130 0.280.33 0.400.60 0.025 0.025 0.15-0.30 . . . 0.801.10 0150.25 . . .G41350 4135 0.33-0.38 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G41370 4137 0.35-0.40 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G41400 4140 0.380.43 0.751.00

24、 0.025 0.025 0.15-0.30 . . . 0.801.10 0.15-0.25 . . .G41420 4142 0.40-0.45 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G41450 4145 0.43-0.48 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G41470 4147 0.45-0.50 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.

25、25 . . .G41500 4150 0.48-0.53 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G43200 4320 0.17-0.22 0.45-0.65 0.025 0.025 0.15-0.30 1.65-2.00 0.40-0.60 0.20-0.30 . . .G43400 4340 0.380.43 0.600.80 0.025 0.025 0.15-0.30 1.65-2.00 0.700.90 0.20-0.30 . . .G43406 E4340 0.38-0.43 0.65-0.85

26、 0.025 0.025 0.15-0.30 1.65-2.00 0.70-0.90 0.20-0.30 . . .G45200 4520 0.18-0.23 0.45-0.65 0.025 0.025 0.15-0.30 . . . . . . 0.45-0.60 . . .G46150 4615 0.13-0.18 0.45-0.65 0.025 0.025 0.15-0.30 1.65-2.00 . . . 0.20-0.30 . . .G46200 4620 0.17-0.22 0.45-0.65 0.025 0.025 0.15-0.30 1.65-2.00 . . . 0.20-0

27、.30 . . .G47180 4718 0.16-0.21 0.70-0.90 0.025 0.025 0.15-0.30 0.90-1.20 0.35-0.55 0.30-0.40 . . .G48150 4815 0.13-0.18 0.40-0.60 0.025 0.025 0.15-0.30 3.25-3.75 . . . 0.20-0.30 . . .G48200 4820 0.18-0.23 0.50-0.70 0.025 0.025 0.15-0.30 3.25-3.75 . . . 0.20-0.30 . . .G50150 5015 0.12-0.17 0.30-0.50

28、0.025 0.025 0.15-0.30 . . . 0.30-0.50 . . . . . .G50460 5046 0.43-0.50 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.20-0.35 . . . . . .G51150 5115 0.13-0.18 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.70-0.90 . . . . . .G51200 5120 0.170.22 0.700.90 0.025 0.025 0.15-0.30 . . . 0.700.90 . . . . . .G51300 5130

29、 0.28-0.33 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.80-1.10 . . . . . .G5132 5132 0.30-0.35 0.60-0.90 0.025 0.025 0.15-0.30 . . . 0.75-1.00 . . . . . .G51400 5140 0.380.43 0.700.90 0.025 0.025 0.15-0.30 . . . 0.700.90 . . . . . .G51500 5150 0.480.53 0.700.90 0.025 0.025 0.15-0.30 . . . 0.700.90 . . .

30、 . . .G51600 5160 0.550.65 0.751.00 0.025 0.025 0.15-0.30 . . . 0.700.90 . . . . . .G15116 E51100 0.95-1.10 0.25-0.45 0.025 0.025 0.15-0.30 . . . 0.90-1.15 . . . . . .G15216 E52100 0.95-1.10 0.25-0.45 0.025 0.025 0.15-0.30 . . . 1.30-1.60 . . . . . .G61500 6150 0.48-0.53 0.70-0.90 0.025 0.025 0.15-0

31、.30 . . . 0.80-1.10 . . . 0.15 minG61580 6158 0.550.62 0.701.10 0.025 0.025 0.15-0.30 . . . 0.901.20 . . . 0.100.20G86150 8615 0.130.18 0.700.90 0.025 0.025 0.15-0.30 0.400.70 0.400.60 0.150.25 . . .G86170 8617 0.15-0.20 0.70-0.90 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86200 8620

32、0.180.23 0.700.90 0.035 0.035 0.15-0.30 0.40-0.70 0.400.60 0.15.025 . . .G86300 8630 0.28-0.33 0.70-0.90 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86400 8640 0.38-0.43 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86420 8642 0.40-0.45 0.75-1.00 0.025 0.025 0.15-

33、0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86450 8645 0.43-0.48 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86500 8650 0.48-0.53 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86550 8655 0.50-0.60 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.2

34、5 . . .G86600 8660 0.55-0.65 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G87200 8720 0.18-0.23 0.70-0.90 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.20-0.30 . . .G87350 8735 0.33-0.38 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.20-0.30 . . .G87400 8740 0.38-0.43 0.75

35、-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.20-0.30 . . .G92600 9260 0.55-0.65 0.70-1.00 0.025 0.025 1.80-2.20 . . . . . . . . . . . .G92620 9262 0.55-0.65 0.75-1.00 0.025 0.025 1.80-2.20 . . 0.25-0.40 . . . . . . . . E9310 0.08-0.13 0.45-0.65 0.025 0.025 0.20-0.35 3.30-35.0 1.00-1.40 0.08-0.1

36、5 . . .AThe chemical ranges and limits shown are subject to product analysis tolerances. See Specification A 505.BOther silicon ranges are available. Consult the producer.A1031052the thickness tolerance tables in Specification A 635/A 635M. The pur-chaser should contact the producer regarding possib

37、le limitations prior toplacing an order.4.1.8 Coil size and weight requirements (must includeinside diameter, ID; outside diameter, OD), and maximumweight,4.1.9 Quantity (weight),4.1.10 Application (part identification and description),4.1.11 Special requirements (if required),4.1.12 Test reports (i

38、f required), and4.1.13 Cast or heat analysis (if required).NOTE 2A typical ordering description is as follows: (inch poundunits) ASTM A 1031: Alloy, hot rolled sheet coils, grade SAE 4118,pickled and oiled, cut edge, 0.500 by 40 in. by coil; ID 24 in., OD 72 in.maximum, coil weight 40 000 lb maximum

39、; 200 000 lb for roll formingshapes; (SI units) ASTM A 1031: Alloy, hot rolled sheet coils, grade SAE4118, pickled and oiled, cut edge, 10 mm by 900 mm by coil; ID 600 mm,OD 1800 mm, maximum, coil weight 18 000 kg maximum; 90 000 kg forroll forming shapes.5. Manufacture5.1 Heat Treatment:5.1.1 As-ro

40、lled,5.1.2 Annealed,5.1.2.1 Spheroidized annealed,(1) Drawing SteelUnless otherwise specified on theorder, drawing steel will be furnished with a spheroidizedannealed heat treatment.(2) If the material is to be heat treated by other than theproducer, the order shall so state. The material may be ord

41、eredin the as-rolled condition, in such cases.5.1.2.2 Normalized, or5.1.2.3 Normalized-and-tempered.6. Chemical Requirements6.1 The heat analysis of the steel shall conform to therequirements for the grade specified on the order.6.2 Standard Alloy Steel grades listed in Table 1 are thosecommonly pro

42、duced for alloy steel sheet and strip.6.3 Nonstandard Alloy Steel grades may be specified usingthe ranges and limits shown in Table 2.6.4 Structural Alloy SteelThe grade shall be specified asoutlined in 6.2 or 6.3. However, since different mechanicalproperties may be expected for each of the many ch

43、emicalcompositions and conditions (heat treatment) that may bespecified, consideration must be given to these factors inselecting the chemical composition to be specified.7. Metallurgical Structure7.1 Microstructure:7.1.1 Drawing SteelA minimum of 75 % of the carbidemicrostructure shall be of the gl

44、obular type for material with anordered thickness of less than or equal to 0.400 in. (10 mm).For material with an ordered thickness greater than 0.400 in.(10 mm), the percent minimum globular carbide microstructureguarantee shall be by agreement between the purchaser and theproducer.7.1.2 Number of

45、TestsThe number of tests shall be inaccordance with the producers standard quality control pro-cedures.8. Mechanical Requirements8.1 Alloy SteelMechanical tests are not applicable toregular quality alloy steel sheet and strip.8.2 Test specimen preparation and mechanical testing shallbe in accordance

46、 with Test Methods and Definitions A 370.8.3 Drawing Steel and Structural Alloy Steel:8.3.1 Tension and Hardness Tests:8.3.1.1 Tensile, Hardness PropertiesWhen tension and/orhardness tests are specified on the order, the test results shallconform to the requirements specified on the order. Yieldstre

47、ngth, tensile strength, elongation and hardness require-ments may be specified. The properties will vary depending onthe chemical composition, condition, and heat treatment. Pro-ducers are frequently consulted as to grade, resultant mechani-cal properties, recommended heat treatment, and other infor

48、-mation needed to establish the property parameters to meet enduse requirements. Rockwell hardness requirements may bespecified, providing the requirements are compatible with thetension test requirements. These requirements do not apply tothe uncropped ends of unprocessed coils.8.3.1.2 Test Specime

49、n Location and OrientationTestspecimens shall be taken sufficiently far from the as hot rolledTABLE 2 Heat (Cast) Analysis Ranges for Other than StandardSteel Alloy Sheet and StripElementWhen Maximum ofSpecified Element is, %Range orLimit, %Carbon To 0.55 incl 0.05Over 0.55 to 0.70 incl 0.08Over 0.70 to 0.80 incl 0.10Over 0.80 to 0.95 incl 0.12Over 0.95 to 1.35 incl 0.13Manganese To 0.60 incl 0.20Over 0.60 to 0.90 incl 0.20Over 0.90 to 1.05 incl 0.25Over 1.05 to 1.90 incl 0.30Over 1.90 to 2.10 incl 0.40Phosphorus . 0.025 maxSulfur . 0.025