ASTM A1109-2018 Standard Specification for Special Fittings for Single-Stack Hubless Cast Iron Soil Pipe Fittings for Sanitary Waste and Vent Piping Applications《卫生、废物和通风管道用单层无轮毂铸铁.pdf

1、Designation: A1109 18Standard Specification forSpecial Fittings for Single-Stack Hubless Cast Iron Soil PipeFittings for Sanitary, Waste, and Vent Piping Applications1This standard is issued under the fixed designation A1109; the number immediately following the designation indicates the year oforig

2、inal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers special hubless cast iron soilpipe fi

3、ttings for use in a one-pipe combination vent and wastestack unvented for gravity flow applications. It establishesstandards covering material, manufacture, mechanical andchemical properties, dimensions, coating, test methods,inspection, certification, and product marking for hubless castiron soil p

4、ipe fittings. These fittings are intended for nonpres-sure applications, where the selection of the proper size forsanitary, drain, and waste systems allows free air space forgravity drainage.NOTE 1The fittings covered by this standard are special fittingsintended to be used for engineered designed

5、systems and will requirespecial approval by the authority having jurisdiction for use. It is not theintent of this standard to endorse or recommend the use of these fittings forthese special applications.1.2 The EDP/ASA numbers indicated in this section repre-sent a uniform industry code adopted by

6、the American SupplyAssociation (ASA). A group designation prefix, 022, is as-signed to hubless products, followed by the four-digit identi-fication assigned to individual items and a check digit. Thissystem has been instituted to facilitate EDP control throughdistribution channels, and is to be used

7、 universally in orderingand specifying product items. Those items with no EDPnumbers are new, special, or transitory, and will be assignednumbers on subsequent prints of this specification.1.3 This specification covers fittings of the following pat-terns and applies to any other patterns that confor

8、m with theapplicable requirements given in this specification.NOTE 2The text of this standard references notes and footnotes thatprovide explanatory material. These notes and footnotes (excluding thosein tables and figures) shall not be considered as requirements of thestandard.NOTE 3Some sellers of

9、 these fittings use the terms “aerator” and“de-aerator” fittings to describe the two types of fittings covered by thisstandard.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for the

10、Development of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2A48/A48M Specification for Gray Iron CastingsA644 Terminology Relating to Iron CastingsD3960 Practice for D

11、etermining Volatile Organic Compound(VOC) Content of Paints and Related CoatingsE8/E8M Test Methods for Tension Testing of Metallic Ma-terialsE1645 Practice for Preparation of Dried Paint Samples byHotplate or Microwave Digestion for Subsequent LeadAnalysis2.2 U.S. Federal Standard:3Federal Standard

12、 No. 123 Marking for Shipment (CivilAgencies)2.3 Military Standard:3MIL-STD-129 Marking for Shipment and Storage2.4 Other Documents:Uniform Freight Classification Rules4National Motor Freight Classification Rules53. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 manufacturerthe

13、entity that casts the fittings coveredby this standard.1This specification is under the jurisdiction of ASTM Committee A04 on IronCastings and is the direct responsibility of Subcommittee A04.12 on Pipes andTubes.Current edition approved Feb. 15, 2018. Published March 2018. Originallyapproved in 201

14、8. DOI: 10.1520/A1109-18.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from DLA Document Service

15、s, Building 4/D, 700 Robbins Ave.,Philadelphia, PA 19111-5094, http:/quicksearch.dla.mil.4Available from Uniform Classification Commission, Room 1106, 222 S.Riverside Plaza, Chicago, IL 60606.5Available from National Motor Freight Traffic Association, Inc. (NMFTA),1001 N. Fairfax St., Suite 600, Ale

16、xandria, VA 22314-1798, http:/www.nmfta.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decisi

17、on on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.14. Materials and Manufacture4.1 The fittings shall be iron castings suitable for installationand service for sanitary, storm

18、drain, and waste vent pipingapplications. The fittings shall meet all applicable requirementsand tests given in this specification.4.2 The castings shall be made of cast iron, produced by anestablished commercial method that provides control overchemical and mechanical properties. “Cast iron” is a g

19、enericterm for a series of alloys as defined in Terminology A644 andincludes gray iron as well as ductile iron. The castings shall besound, true to pattern, and of compact close grain that permitsdrilling and cutting by ordinary methods. The interior surfaceshall be reasonably smooth and free from d

20、efects that wouldmake the castings unfit for the use for which they are intended.4.3 To minimize the possibility of introducing radioactivematerial to a melting operation, ferrous scrap, pig iron, and anyrecycled ferrous material shall be screened by the manufacturerfor radioactivity with suitable d

21、etection devices operated inaccordance with the detection manufacturers instructions.Written operating, calibration, and maintenance procedures forthe detection equipment shall be provided to the purchaser forreview when requested. Records shall be maintained by load ofthese tests for a period of se

22、ven years.4.3.1 Only radiation detection devices designed specificallyfor the purpose of screening ferrous material shipments shall beused for the purpose of conforming to this requirement.Handheld detection devices (Geiger counters) are not appro-priate and shall not be used for the purpose of conf

23、orming tothis requirement.4.3.2 Material that is found contaminated with radioactivityshall not be used to produce products covered by this specifi-cation.4.3.3 Analysis of castings after the time of production shallnot be used to determine compliance to this specification.4.4 Fittings shall not be

24、patched, filled, or welded by themanufacturer to repair cosmetic or material defects that occurduring the course of manufacturing.5. Mechanical Properties5.1 Mechanical Tests for Gray IronThe manufacturershall perform tests to determine mechanical properties of thegray iron used in the manufacture o

25、f gray iron soil pipe fittings.Tension tests on the specimens shall be employed. Themanufacturer shall maintain a record of mechanical tests for aminimum of seven years.5.1.1 Tensile Strength TestThe tensile strength shall be notless than 21 000 psi (145 MPa).5.1.2 Tension test reports shall include

26、 breaking load of testbars, machined diameter of test bars, and calculated tensilestrength. Section 11 provides details of the test bar dimensions.5.1.3 Analysis of castings or test bars after the time ofproduction shall not be used as evidence of compliance to thisspecification.6. Chemical Test for

27、 Gray Iron6.1 The manufacturer shall perform tests to determine thesignificant chemical constituents of the gray iron used in themanufacture of gray iron soil pipe fittings. Analysis shall beperformed at a minimum of once per lot as defined in thisspecification. The manufacturer shall maintain a rec

28、ord ofchemical tests performed for a minimum of seven years. Thetest results shall conform to the following requirements as tochemical composition:Phosphorous (P) 0.38 % maximumSulfur (S) 0.15 % maximumChromium (Cr) 0.50 % maximumTitanium (Ti) 0.10 % maximumAluminum (Al) 0.50 % maximumLead (Pb) 0.01

29、5 % maximumCarbon Equivalent 4.10 % minimum by massNote: Carbon equivalent for gray iron = %C+%Si/3+%P/3.6.1.1 Chemical tests shall be performed at the time ofproduction of the castings covered by this specification.6.1.2 Analysis of castings after the time of production shallnot be used as evidence

30、 of compliance to this specification.7. Dimensions and Permissible Variations7.1 Dimensions of FittingsAll fittings shall conform to thedimensions and tolerances specified in Table 1 and Fig. 1 asapplicable. Fittings not listed shall conform to Table 1 for wallthickness and dimension R for the minim

31、um radius of any draininlets that any such fittings provide. Stack fittings and specialfittings that perform the function of a sanitary tee, designed forthe conveyance of soil or waste effluents, or both, shall have aradius not less than the following:7.1.1 Nominal Size of the Run or BranchSizes 112

32、 to 2 in.shall have a minimum radius of 125 % of the smaller run orbranch. Sizes 3 to 4 in. shall have a minimum radius of 100 %of the smaller run or branch. Sizes 5 to 6 in. shall have aminimum radius of 80 % of the smaller run or branch. Sizes 8to 10 in. shall have a minimum radius of 70 % of the

33、smallerrun or branch.7.2 Ends of FittingsSpigot beads and poisoning lugs asshown in Fig. 1 are optional. Positioning lugs and spigot beadsshall be as described in Fig. 1 or continuous around circum-ference of the fitting when the manufacturer chooses to cast onthe fittings. It is permissible to incr

34、ease the wall thickness onthe inside surface of fitting ends to reduce breakage. Theincreased thickness shall not reduce the minimum B dimensionin Table 1 in excess of 0.06 in. and shall not extend more than414 in. from the plain end. The increased thickness shall betapered and shall offer no obstru

35、ction to flow.8. Methods of Specifying Fittings8.1 Method of Specifying Sizes of Fittings of More Than OneSizeThe sizes shall be designated by the order of listing, asfollows:8.1.1 Branch and Tapped Fittings:8.1.1.1 Size of RunThe run shall be that portion of thefitting that forms part of the main p

36、ipe line.8.2 Methods of Specifying Hand of Fittings with SideInletsWhen placed in the position described below, if theside inlet appears on the right, it shall be a right-hand fitting; ifon the left, it shall be a left-hand fitting.A1109 1828.2.1 Branch FittingsThe branch shall be placed towardthe o

37、bserver and the outlet end of the run lower than thebranch.9. Coating9.1 The fittings shall be uniformly coated with a materialsuitable for the purpose that is adherent and not brittle. Thecoating shall be applied in accordance with the coatingmanufacturers requirements. External touch marks frompoi

38、nts of contact during the coating process are permitted. Thecoating shall not contain asbestos above current SDS report-able levels. (The Global Harmonized System of classificationand labeling of chemicals sets the same rules for classifyinghazards and mandates the same format and content for labels

39、and Safety Data Sheets around the world.) Safety Data Sheetsshall be furnished by the coating manufacturer when requested.The coating shall be evenly and smoothly applied to allsurfaces, except in threaded openings, unless the coating isspecifically designed for threaded openings.9.2 Fittings shall

40、not be coated with paint containing leadwhich exceeds levels above 0.06 % (600 PPM).9.2.1 The coating manufacturer shall annually prepare andsubmit samples to a qualified laboratory for tests in accordancewith Practice E1645. The manufacturer shall prepare andsubmit samples when changing sources of

41、supply or thecoating manufacturer changes formulations for the coating.9.3 Fittings coatings shall not contain levels of volatileorganic hazardous air pollutants (VOHAPs) which exceedlevels of 2.6 lb (0.31 kg L) of VOHAPs per gallon of solids inaccordance with Practice D3960.9.3.1 The manufacturer s

42、hall annually certify that the coat-ing meets the VOHAP requirement. It is permissible for thecoating manufacturer to provide the certification.9.4 Records shall be maintained for a period of seven years.9.5 Copies of the coating certification shall be furnishedwhen requested.10. Sampling10.1 Chemic

43、al and mechanical tests shall be made regularlyand at sufficiently close intervals for adequate determinationsof the significant chemical constituents and properties of thecast iron. Records of chemical analysis shall be maintained bythe manufacturer. Copies of these analyses shall be furnished toth

44、e purchaser when requested.10.2 A lot shall consist of one of the following:10.2.1 All the metal poured from a single heating in abatch-type furnace.10.2.2 All the metal from two or more batch-type meltingfurnaces poured into a single ladle or a single casting.10.2.3 All the metal poured from a cont

45、inuous meltingfurnace for a given period of time between changes in charge,processing conditions, or aim-for chemistry or 4 h, whicheveris the shorter period.11. Test Methods11.1 Gray Iron:11.1.1 Tensile Strength TestTest bars shall be cast inaccordance with the requirements of Specification A48/A48

46、M.The machined test bar dimensions and drawings and dimen-sions of as-cast test bars are found in Figs. 2-4. The tensilestrength shall be determined in accordance with Test MethodsE8/E8M.11.1.2 Tension test reports shall include breaking load oftest bars, machined diameter of test bars, and calculat

47、ed tensilestrength.TABLE 1 Dimensions and Tolerances in Inches (Millimetres) of Spigots and Barrels for Hubless FittingsBarrel SpigotSizeInsideDiameterOutsideDiameterOutsideDiameterBead WidthABarrel Thickness, TGasketPositioning LugAB J M N, 0.13 (3.3) Nominal Minimum W(38.1 2.29) (48.26 1.52) (49.7

48、8 1.52) (6.35) (3.3) (28.7)2 1.96 0.09 2.35 0.09 2.41 0.09 0.25 0.16 0.13 1.13(49.8 2.29) (59.69 2.29) (61.21 2.29) (6.35) (3.3) (28.7)3 2.96 0.09 3.35 0.09 3.41 0.09 0.25 0.16 0.13 1.13(75.2 2.29) (85.09 2.29) (86.61 2.29) (6.35) (3.3) (28.7)4 3.94 0.09 4.38 + 0.09 4.44 0.09 0.31 0.19 0.15 1.130.05

49、(100.08 2.29) (111.25 + 2.29) (112.78 2.29) (7.87) (3.81) (28.7)(1.27)5 4.94 0.09 5.30 + 0.09 5.36 0.09 0.31 0.19 0.15 1.500.05(125.48 2.29) (134.62 + 2.29) (136.14 2.29) (7.87) (3.81) (38.1)(1.27)6 5.94 0.09 6.30 + 0.09 6.36 0.09 0.31 0.19 0.15 1.500.05(150.88 2.29) (160.02 + 2.29) (161.54 2.29) (7.87) (3.81) (38.1)(1.27)8 7.94 0.13 8.38 + 0.09 8.44 0.09 0.31 0.23 0.17 2.000.09(201.68 3.3) (212.85 + 3.3) (214.38 2.29) (7.87) (4.32) (50.8)(2.29)ASee Fig. 1 for details of the spigot and gasket p