1、Designation: B 107/B 107M 07Standard Specification forMagnesium-Alloy Extruded Bars, Rods, Profiles, Tubes, andWire1This standard is issued under the fixed designation B 107/B 107M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, t
2、he year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification cover
3、s magnesium-alloy extrudedbars, rods, profiles, tubes, and wire of the composition given inTable 1.1.2 The values stated in either inch-pound or SI units are tobe regarded separately as standards. The SI units are shown inbrackets or in separate tables or columns. The values stated ineach system are
4、 not exact equivalents; therefore, each systemmust be used independent of the other. Combining values fromthe two systems may result in nonconformance with thespecification.1.3 Unless the order specifies the “M” specification desig-nation, the material shall be furnished to the inch-pound units.2. R
5、eferenced Documents2.1 The following documents of the issue in effect on dateof order acceptance form a part of this specification to theextent referenced herein.2.2 ASTM Standards:2B 296 Practice for Temper Designations of MagnesiumAlloys, Cast and WroughtB 557 Test Methods for Tension Testing Wrou
6、ght and CastAluminum- and Magnesium-Alloy ProductsB 557M Test Methods for Tension Testing Wrought andCast Aluminum- and Magnesium-Alloy Products MetricB 660 Practices for Packaging/Packing of Aluminum andMagnesium ProductsB 666/B 666M Practice for Identification Marking of Alu-minum and Magnesium Pr
7、oductsB 951 Practice for Codification of Unalloyed Magnesiumand Magnesium-Alloys, Cast and WroughtE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE35 Test Methods for Chemical Analysis of Magnesiumand Magnesium AlloysE55 Practice for Sampling Wrought
8、 Nonferrous Metals andAlloys for Determination of Chemical CompositionE 527 Practice for Numbering Metals and Alloys (UNS)3. Terminology3.1 Definitions:3.1.1 extruded bara solid extrusion, long in relation to itscross-sectional dimensions, having a symmetrical cross sectionthat is square or rectangu
9、lar with sharp or rounded corners oredges, or is a regular hexagon or octagon, and whose width orgreatest distance between parallel faces is over 0.375 in. 10mm.3.1.2 extruded profilea hollow or solid extrusion, long inrelation to its cross-sectional dimensions, whose cross sectionis other than that
10、 of wire, rod, bar, or tube.3.1.3 extruded roda solid round extrusion, long in relationto its diameter, whose diameter is over 0.375 in. 10 mm.3.1.4 extruded tubea hollow extrusion, long in relation toits cross-sectional dimensions, which is symmetrical and isround, square, rectangular, hexagonal, o
11、ctagonal, or ellipticalwith sharp or rounded corners, and has a uniform wallthickness except as affected by corner radii.3.1.5 producerthe primary manufacturer of a material.3.1.6 supplierincludes only the category of jobbers anddistributors as distinct from producer.3.1.7 wirea solid section long i
12、n relation to its cross-sectional dimensions, having a cross section that is round,hexagonal, or octagonal, and whose diameter, width, or great-est distance between parallel faces is up through 0.375 in. 10mm, or having a symmetrical cross section that is square orrectangular (excluding flattened wi
13、re) with sharp or roundedcorners or edges.3.2 Definitions of Terms Specific to This Standard:1This specification is under the jurisdiction of ASTM Committee B07 on LightMetals and Alloys and is the direct responsibility of Subcommittee B07.04 onMagnesium Alloy Cast and Wrought Products.Current editi
14、on approved June 1, 2007. Published June 2007. Originallyapproved in 1936. Last previous edition approved in 2006 as B 107/B 107M 06.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume infor
15、mation, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.3.2.1 capable ofmeans that the test need not be
16、 performedby the producer of the material. However, should subsequenttesting by the purchaser establish that the material does notmeet these requirements, the material shall be subject torejection.4. Ordering Information4.1 Orders for material to this specification shall include thefollowing informa
17、tion:4.1.1 This specification number,4.1.2 Quantity in pieces or pounds kilograms,4.1.3 Alloy (Section 6),4.1.4 Temper (Section 7),4.1.5 Nominal cross-sectional dimensions as follows:4.1.5.1 For rod and round wirediameter,4.1.5.2 For square corner bars and wiredepth and width,4.1.5.3 For sharp corne
18、red hexagonal or octagonal bars andwiredistance across flats,4.1.5.4 For round tubeoutside or inside diameter and wallthickness,4.1.5.5 For square or sharp cornered other than roundtubedistance across flats and wall thickness,4.1.5.6 For round cornered bars and wire; profiles; tubeother than round,
19、square, rectangular, hexagonal or octagonalwith sharp cornersdrawing required,4.1.6 Length,4.1.7 Surface finish (see 9.2),4.1.8 Whether inspection or witness of inspection and testsby the purchasers representative is required prior to materialshipment (Section 10),4.1.9 Whether certification is requ
20、ired (Section 12),4.1.10 Whether marking for identification is required (Sec-tion 13 and Practices B 660), and4.1.11 Whether special packaging is required for shipment(Section 14).5. Quality Assurance5.1 Responsibility for InspectionUnless otherwise speci-fied in the contract or purchase order, the
21、producer or supplieris responsible for the performance of all inspection and testrequirements specified herein. Except as otherwise specified inthe contract or order, the producer or supplier may use his ownor any other suitable facilities for the performance of theinspection and test requirements s
22、pecified herein, unless dis-approved by the purchaser at the time the order is placed. Thepurchaser shall have the right to perform any of the inspectionsand tests set forth in this specification where such inspectionsare deemed necessary to assure that material conforms toprescribed requirements.6.
23、 Chemical Composition6.1 LimitsThe bars, rods, profiles, tubes, or wire shallconform to the chemical requirements in Table 1.6.2 Number of SamplesThe number of samples taken fordetermination of chemical composition shall be as follows:6.2.1 When samples are taken at the time extrusion ingotsare cast
24、 for determination of conformance to Table 1, onesample shall be taken for each group of ingots of the samealloy, poured at the same time, from the same source of moltenmetal when a batch process is employed. In cases where acontinuous casting process is employed, one sample shall betaken for each q
25、uantity of material cast equivalent in size(weight or volume) to the last holding vessel before casting or5000 lb 2270 kg, whichever is less. Ingots not conforming toTable 1 shall be rejected.6.2.2 Unless compliance is established by 6.2.1, sampling ofthe finished product shall be in accordance with
26、 Practice E55.One sample shall be taken for each 4000 lb (2000 kg) or lessof material comprising the lot, except that not more than oneanalysis shall be required per piece.TABLE 1 Chemical RequirementsANOTE 1Analysis shall regularly be made only for the elements specifically mentioned in this table.
27、 If, however, the presence of other elements issuspected or indicated in the course of routine analysis to be in amounts greater than the specified limits, further analysis shall be made to determine thatthe total of these other elements is not in excess of the limits specified in the last column of
28、 the table.NOTE 2The following applies to all specified limits in this table: For purposes of acceptance and rejection, an observed value or a calculated valueobtained from analysis should be rounded-off to the nearest unit in the last right-hand place of figures used in expressing the specified lim
29、it.AlloyBComposition, %UNSNo.ASTMNo.MagnesiumAlumi-numCal-ciumCop-perIron LithiumMan-ganeseNeodymium NickelRareEarthsSili-conYttriumZirco-nium,minZincOtherImpurities,eachTotalOtherCImpuritiesM11311 AZ31B remainder 2.5-3.5 0.04 0.05 0.005 0.20-1.0 0.005 0.10 . 0.6-1.4 0.30M11312 AZ31C remainder 2.4-3
30、.6 . 0.10 . 0.15-1.0D0.03 0.10 . 0.50-1.5 0.30M11610 AZ61A remainder 5.8-7.2 . 0.05 0.005 0.15-0.5 0.005 0.10 . 0.40-1.5 0.30M11800 AZ80A remainder 7.8-9.2 . 0.05 0.005 0.12-0.5 0.005 0.10 . 0.20-0.8 0.30M15100 M1A remainder . 0.30 0.05 . 1.2-2.0 0.01 0.10 . . 0.30M18432 WE43B remainder . . 0.02 0.0
31、10 0.2 0.03 2.0-2.5 0.005 1.9E. 3.7-4.3 0.40-1.0F0.01 .M18410 WE54A remainder . . 0.03 . 0.2 0.03 1.5-2.0 0.005 2.0E0.01 4.75-5.5 0.40-1.0 0.20 0.2 .M16400 ZK40A remainder . . . . . . . 0.45 3.54.5 0.30M16600 ZK60A remainder . . . . . . . 0.45 4.8-6.2 0.30ALimits are in weight percent maximum unless
32、 shown as a range or otherwise stated.BThese alloy designations were established in accordance with Practice B 951 (see also Practice E 527).CIncludes listed elements for which no specific limit is shown.DManganese minimum limit need not be met if iron is 0.005 %, or less.EOther Rare Earths shall be
33、 principally heavy rare earths, for example, Gadolinium, Dysprosium, Erbium, and Ytterbium. Other Rare Earths are derived from the Yttrium,typically 80 % Yttrium 20 % heavy rare earths.FZinc + Silver content shall not exceed 0.20 % in WE43B.B 107/B 107M 0726.3 Methods of Chemical AnalysisAny suitabl
34、e method ofchemical analysis may be used. In case of dispute, the analysisshall be made by methods given in Test Methods E35or anyother standard methods of analysis approved by ASTM unlesssome other method is agreed upon.7. Tensile Requirements Tensile Requirements7.1 LimitsThe bars, rods, profiles,
35、 tubes, and wire shallconform to the tensile properties requirements in Table 2 unlessother agreement is made between producer or supplier andpurchaser. Properties for sizes and tempers not shown in Table2 shall be as agreed by producer or supplier and purchaser.7.2 Number of SpecimensFrom material
36、having nominalweight of less than 1 lb/linear ft through 1.7 kg/linear m, onetension test sample shall be taken for each 1000 lb 500 kg orfraction thereof in the shipment. For material having a nominalweight of 1 lb/linear ft over 1.7 kg/linear m or more, onetension test shall be taken for each 1000
37、 ft 300 m or fractionthereof in the shipment. Other procedures for selecting samplesmay be employed if agreed upon by the seller and thepurchaser.7.3 Geometry of test specimens and the location in theproduct from which they are taken shall be as specified in TestMethods B 557 and B 557M.7.4 Test Met
38、hodsThe tension tests shall be made inaccordance with Test Methods B 557 and B 557M.7.5 RetestsIf any tension specimen fails to conform to therequirements prescribed in Table 2, two additional specimensshall be selected and tested from other bars, rods, profiles,tubes, or wire in the lot. If either
39、of these specimens fails toconform to the applicable requirements, the material may berejected. If, however, the failure of the specimens to conform tothe requirements is the result of an inadequate thermal treat-ment, the material may be reheat treated and resampled inaccordance with 7.2.TABLE 2 Te
40、nsile RequirementsNOTEFor purposes of determining conformance with this specification, each value for tensile strength and yield strength shall be rounded to thenearest 100 psi and each value for elongation shall be rounded to the nearest 0.5 %, both in accordance with the rounding method of Practic
41、e E29.AlloyATem-perAFormSpecifiedDiameter orThicknessOver-ThroughSpecifiedCross-Sec-tional Area,in.2or OD ofTube, in.TensileStrength,minYield Strength(0.2 % offset),minElongation in2 in. 50 mmor 4 3 Dia.,min, %B,CUNSNo.ASTMNo.in.D,Emm ksi MPa ksi MPaM11311 AZ31B F bars, rods, profiles, 0.249 and .6.
42、30 all 35.0 240 21.0 145 7and wire under0.2501.499 6.3040.00 all 35.0 240 22.0 150 71.5002.499 40.0060.00 all 34.0 235 22.0 150 72.5004.999 60.00130.00 all 32.0 220 20.0 140 7hollow profiles all all 32.0 220 16.0 110 8tubes 0.0280.250 0.706.30 6.000 150.00 32.0 220 20.0 140 8and under0.2500.750 6.30
43、20.00 32.0 220 16.0 110 4M11610 AZ61A F bars, rods, profiles, 0.249 and .6.30 all 38.0 260 21.0 145 8and wire under0.2502.499 6.3060.00 all 40.0 275 24.0 165 92.5004.999 60.00130.00 all 40.0 275 22.0 150 7hollow profiles all all 36.0 250 16.0 110 7tubes 0.0280.750 0.7020.00 6.000 150.00and under36.0
44、 250 16.0 110 7M11800 AZ80A F bars, rods, solid 0.249 and .6.30 all 43.0 295 28.0 195 9profiles, and wire under0.2501.499 6.3040.00 all 43.0 295 28.0 195 81.5002.499 40.0060.00 all 43.0 295 28.0 195 62.5004.999 60.00130.00 all 42.0 290 27.0 185 4M11800 AZ80A T5 bars, rods, solid 0.249 and .6.30 all
45、47.0 325 30.0 205 4profiles, and wire under0.2502.499 6.3060.00 all 48.0 330 33.0 230 42.5004.999 60.00130.00 all 45.0 310 30.0 205 2M15100 M1A F bars, rods, profiles, 0.249 and .6.30 all 30.0 205FF2and wire under0.2501.499 6.3040.00 all 32.0 220FF31.5002.499 40.0060.00 all 32.0 220 22.5004.999 60.0
46、0130.00 all 29.0 200FF2B 107/B 107M 073TABLE 2 ContinuedAlloyATem-perAFormSpecifiedDiameter orThicknessOver-ThroughSpecifiedCross-Sec-tional Area,in.2or OD ofTube, in.TensileStrength,minYield Strength(0.2 % offset),minElongation in2 in. 50 mmor 4 3 Dia.,min, %B,CUNSNo.ASTMNo.in.D,Emm ksi MPa ksi MPa
47、hollow profiles all all 28.0 195FF2tubes 0.0280.750 0.7020.00 6.000 150.00and under28.0 195FF2M18430 WE43B T5 bars, rods, solidprofiles and wire0.250-1.999 6.3-50.00 all 36.0 250 23.0 160 4M18430 WE43B T5 bars, rods, solidprofiles and wire2.00-5.00 50-130.00 all 35.0 240 22.0 150 4M18430 WE43B T6 ba
48、rs, rods, solidprofiles and wire0.250-1.999 6.3-50.00 all 36.0 250 22.0 150 4M18430 WE43B T6 bars, rods, solidprofiles and wire2.00-5.00 50-130.00 all 35.0 240 20.0 140 4M18410 WE54A T5 bars, rods, solidprofiles and wire0.250-1.999 6.3-50.00 all 36.0 250 26.0 180 4M18410 WE54A T5 bars, rods, solidpr
49、ofiles and wire2.00-5.00 50-130.00 all 36.0 250 25.0 170 4M18410 WE54A T6 bars, rods, solidprofiles and wire0.250-1.999 6.3-50.00 all 38.0 260 26.0 180 4M18410 WE54A T6 bars, rods, solidprofiles and wire2.00-5.00 50-130.00 all 36.0 250 25.0 175 4M16400 ZK40A T5 bars, rods, profiles,and wireall 3.000