ASTM D913-2003e1 Standard Test Method for Evaluating Degree of Resistance to Wear of Traffic Paint《评价路标漆耐磨程度的标准试验方法》.pdf

1、Designation: D 913 03e1Standard Test Method forEvaluating Degree of Resistance to Wear of Traffic Paint1This standard is issued under the fixed designation D 913; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last rev

2、ision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.e1NOTEAdjunct references were corrected editorially in April 2006.1. Scope1.1 This test method covers the evaluation of degree ofresistan

3、ce to wear that may occur with traffic paints in roadtests (see Practice D 713) or in actual service, using photo-graphic standards for comparative evaluation.1.2 This standard does not purport to address all of thesafety problems, if any, associated with its use. It is theresponsibility of the user

4、 of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D 713 Practice for Conducting Road Service Tests on FluidTraffic Marking Materials2.2 ASTM Adjuncts:Glossy Prints

5、 of Photographic Reference Standards33. Description of Term Specific to This Standard3.1 failure, described by these reference standardsthatcondition manifested in traffic paint by actual detachment ofentire sections of the film from its substrate or from paintpreviously applied. The degree of resis

6、tance to failure is judgedby the amount of substrate that is covered.4. Significance and Use4.1 This test method is designed to evaluate the resistance towear of a traffic paint. It must be remembered that a highdegree of performance of paint applied to a bare road surfacemay not guarantee similar r

7、esults when the same paint isapplied over old paint lines.5. Type of Failure5.1 The failure as described in Section 3 does not presumeany specific mechanism, and all areas where the substrate isvisible shall be considered a failure.6. Use of Photographic Reference Standards6.1 The photographic refer

8、ence standards3that are part ofthis test method are representative of the degrees of resistanceto wear of stripes of traffic paint. The examples shown in Fig.1 are for illustration purposes only and should not be used forevaluation.6.1.1 The degree of resistance to wear is likely to vary overany giv

9、en area. It is therefore necessary to use one of thefollowing grading methods:6.1.1.1 Select an area as representative and base the ratingof the stripe on this area or6.1.1.2 Grade segments of the stripe and average thesegradings.6.1.2 The photographic reference standards (Note 1) repre-sent four de

10、grees (97 %, 92 %, 77 %, 60 %) of resistance towear. Substrate revealed by failure is readily discernible withthe naked eye.NOTE 1The reference standards are representative of stripes of trafficpaints. The percentage of surface covered is shown on each referencestandard.7. Procedure7.1 Compare the r

11、epresentative areas of the traffic paintstripes with the photographic reference standards and estimatethe percent of intact film.8. Report8.1 Report the mean and range of the substrate coverageestimations, if appropriate.9. Keywords9.1 resistance to wear; traffic paint1This test method is under the

12、jurisdiction of ASTM Committee D01 on Paintand Related Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.44 on Traffic Coatings.Current edition approved March 31, 2006. Published June 2003. WithdrawnOctober 2002 and reinstated as D 913 03.2For referenced ASTM

13、standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Full-size (8 by 10-in. (203 by 254-mm) glossy prints of the photographicreference

14、 standards showing degrees of chipping are available from ASTMInternational Headquarters. Order Adjunct No: ADJD0913.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.(Film 97 % Intact) (Film 92 % Intact)(Film 77 % Intact) (Film 60 % I

15、ntact)FIG. 1 Percent of Substrate CoveredD91303e12ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent right

16、s, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for r

17、evision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing y

18、ou shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D91303e13