ASTM D7082-2004(2010) 8750 Standard Specification for Polyethylene Stay In Place Form System for End Walls for Drainage Pipe《排水管端壁的聚乙烯固定型系统标准规范》.pdf

1、Designation: D7082 04 (Reapproved 2010)Standard Specification forPolyethylene Stay In Place Form System for End Walls forDrainage Pipe1This standard is issued under the fixed designation D7082; the number immediately following the designation indicates the year oforiginal adoption or, in the case of

2、 revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification addresses the requirements for poly-ethylene stay in place forms for end wal

3、ls or head walls for usewith standard storm drainage systems.1.2 The wall form system consists of a base wall form, acap, an optional riser to adjust the height of the wall above thepipe, and an optional adaptor to adjust the pipe opening toaccommodate smaller pipe sizes.1.3 The form system is manuf

4、actured using the rotationalmolding process and is available in different colors.1.4 The values stated in SI units are to be regarded as thestandard, the inch-pounds in brackets are given for informationonly.1.5 This standard does not purport to address all of thesafety concerns, if any, associated

5、with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory requirements prior to use.NOTE 1There is no known ISO equivalent to this standard.2. Referenced Documents2.1 ASTM Standards:2D638 Te

6、st Method for Tensile Properties of PlasticsD648 Test Method for Deflection Temperature of PlasticsUnder Flexural Load in the Edgewise PositionD790 Test Methods for Flexural Properties of Unreinforcedand Reinforced Plastics and Electrical Insulating MaterialsD883 Terminology Relating to PlasticsD123

7、8 Test Method for Melt Flow Rates of Thermoplasticsby Extrusion PlastometerD1505 Test Method for Density of Plastics by the Density-Gradient TechniqueD1600 Terminology for Abbreviated Terms Relating toPlasticsD1693 Test Method for Environmental Stress-Cracking ofEthylene PlasticsD4883 Test Method fo

8、r Density of Polyethylene by theUltrasound TechniqueD5033 Guide for Development of ASTM Standards Relat-ing to Recycling and Use of Recycled Plastics33. Terminology3.1 DefinitionsDefinitions used in this specification are inaccordance with definitions in Terminology D883 and abbre-viations in accord

9、ance with Terminology D1600 unless other-wise indicated.3.1.1 end walla wall installed at the outlet of a stormdrainage pipe.3.1.2 head walla wall installed at the inlet of a stormdrainage pipe.4. Ordering Information4.1 Number and color of base wall forms,4.2 Number and color of riser forms,4.3 Num

10、ber and color of caps, and4.4 Number, color and size of adaptors.5. Materials and Manufacture5.1 The material used shall be a polyethylene meeting thecriteria in Table 1.5.2 Only virgin materials (Guide D5033) shall be used.5.3 This product shall be manufactured using a rotationalmolding process.6.

11、Requirements6.1 Wall System Description:6.1.1 Base wall form is hollow with opening at the top toaccept fill material and designed to accept either cap or risersection. Base wall has opening in the center for pipe andadaptors as needed. Pipe is secured to base wall form withgalvanized screws. (See F

12、ig. 1.)1This specification is under the jurisdiction of ASTM Committee D20 onPlastics and is the direct responsibility of Subcommittee D20.24 on Plastic BuildingProducts.Current edition approved April 1, 2010. Published June 2010. Originallyapproved in 2004. Last previous edition approved in 2004 as

13、 D7082 - 04. DOI:10.1520/D7082-04R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. The last app

14、roved version of this historical standard is referencedon www.astm.org.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6.1.2 Riser form is hollow with opening at top to accept fillmaterial and cap section. Multiple risers can be inst

15、alled onbase wall. (See Fig. 2.)6.1.3 Cap fits on top of base wall or riser and is secured withgalvanized screws. (See Fig. 1.)6.1.4 Adaptor section is used to adjust the size of the pipeopening as needed. Adaptor is secured to base wall form withgalvanized screws and pipe is secured to adaptor with

16、 galva-nized screws. (See Fig. 2.)6.2 Workmanship, Finish, and Appearance:6.2.1 Workmanship of the form system components shall besuch that the quality is agreeable between the producer and theend user.6.2.2 The surface of the form system components shall befinished to mimic a split stone face, with

17、 the appearance ofmortar joints and with the vertical joints offset on alternatingcourses.6.2.3 Physical properties of finished form system compo-nents.6.2.3.1 DimensionsSee Figs. 1 and 2.TABLE 1 Material SpecificationsResin Properties ASTM Method Value UnitsDensity (Range) D1505 / D4883 0.9335 0.93

18、95 g/ccMelt Index (Range) D1238 Cond. 190C, 2.16 kg 3.5 7.5 g/10 minEnvironmental Stress Crack Resistance (ESCR), F50D1693, Cond. A100 % lgepal10 % lgepal27555HrHrFlexural Modulus (Minimum) D790 at 1 % secant Procedure B 600 (87) Mpa (kpsi)Tensile Strength at Yield (Minimum) D638, Type IV specimen 1

19、7.2 (2500) Mpa (psi)Tensile Break Elongation (Minimum) 50.8 mm/min 3.12 mm thick(2 in./min 18 in. thick)420 %Deflection Temperature (Minimum) D648 0.455 MPa (66 psi) 1.82 MPa (264 psi)5035CCFIG. 1 Base Wall and LidD7082 04 (2010)27. Test Methods7.1 Physical Properties:7.1.1 Dimensions shall be measu

20、red to the nearest 2 mmwith the exception of the material thickness, which is measuredas noted on Fig. 2, Note E.8. Sampling, Inspection, and Retest8.1 SamplingThe selection of samples shall be as agreedupon by the purchaser and the seller. Unless otherwise speci-fied, a minimum of five randomly sel

21、ected samples shall betested.8.2 Inspection:8.2.1 Inspection and TestingInspection and testing shallbe made as agreed upon between the purchaser and themanufacturer as part of the purchase contract.8.3 Retest and RejectionIf the results of any test(s) do notmeet the requirements of this specificatio

22、n, the test(s) shall beconducted again only if agreed to by the purchaser and theseller.9. Certification9.1 When specified in the purchase order or contract, amanufacturers certification that the material was designed,manufactured, sampled, tested, and inspected in accordancewith this specification,

23、 and has been found to meet therequirements shall be furnished to the purchaser. When speci-fied in the purchase order or contract, a report of the test resultsshall be furnished. Each certification so furnished shall besigned by an authorized agent of the manufacturer.10. Product Marking10.1 Markin

24、g on the product shall include the following:10.1.1 The letters “ASTM” followed by the designationnumber of this specification,10.1.2 The letters “PE,”10.1.3 The product name, and10.1.4 The name or trademark of the manufacturer.11. Packaging and Package Marking11.1 Unless otherwise specified in the

25、contract, materialsshall be packaged in accordance with the suppliers standardpractice.12. Quality Assurance12.1 When the product is marked with this designation,D7082, the manufacturer affirms that the product was manu-factured, inspected, sampled, and tested in accordance with thisspecification an

26、d has been found to meet the requirements ofthis specification.FIG. 2 Optional Riser Section and AdaptorD7082 04 (2010)313. Keywords13.1 drainage; endwall; headwall; stay in place formASTM International takes no position respecting the validity of any patent rights asserted in connection with any it

27、em mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical com

28、mittee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a

29、meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Driv

30、e, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D7082 04 (2010)4