ASTM D8051 D8051M-2016 3966 Standard Specification for Wax-Modified Asphalt Used in Roofing《屋面用蜡改性沥青的标准规格》.pdf

1、Designation: D8051/D8051M 16Standard Specification forWax-Modified Asphalt Used in Roofing1This standard is issued under the fixed designation D8051/D8051M; the number immediately following the designation indicates theyear of original adoption or, in the case of revision, the year of last revision.

2、 A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers wax-modified asphaltic prod-ucts intended for use in built-up roof construction, constructionof bituminous

3、 vapor retarder systems, adhering fleece-backedsingle-ply roof membranes, and adhering insulation boardsused in various types of roof systems. The specification isintended for general classification purposes only, and does notimply restrictions on roofing system design, such as the slopeat which thi

4、s asphalt may be used.1.2 These products have lower application temperaturescompared to products specified by Specification D312/D312M.1.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents;

5、therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this st

6、andard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D5/D5M Test Method for Penetration of Bituminous Mate-rialsD36/D36M Test Method for Softening Point of Bitumen(Ring-and-Ball

7、 Apparatus)D92 Test Method for Flash and Fire Points by ClevelandOpen Cup TesterD113 Test Method for Ductility of Bituminous Materials(Withdrawn 2016)3D140/D140M Practice for Sampling Asphalt MaterialsD312/D312M Specification for Asphalt Used in RoofingD1079 Terminology Relating to Roofing and Water

8、proofingD2042 Test Method for Solubility of Asphalt Materials inTrichloroethyleneD3461 Test Method for Softening Point of Asphalt and Pitch(Mettler Cup-and-Ball Method)D4402/D4402M Test Method for Viscosity Determination ofAsphalt at Elevated Temperatures Using a RotationalViscometerD7553 Test Metho

9、d for Solubility of Asphalt Materials inN-Propyl Bromide3. Terminology3.1 For definitions of terms used in this specification, referto Terminology D1079.3.2 Definitions:3.2.1 high melt-point synthetic wax, nsynthetic wax with amelt point greater than 90C, for example polyethylene wax,oxidized polyet

10、hylene wax, Fischer-Tropsch wax, and ethylenebis stearamide wax.3.2.2 lightly oxidized asphalt, nhaving a softening pointand penetration range as defined in Table 1.3.2.3 wax-modified asphalt (WM), na product made bymodifying a lightly oxidized asphalt with a high melt-pointsynthetic wax.4. Material

11、s and Manufacture4.1 The base asphalt shall be prepared from lightly oxidizedpetroleum asphalt.4.2 The wax-modified asphalt shall incorporate one or morehigh melt-point synthetic waxes in order to meet the require-ments of this specification.5. Physical Properties5.1 The products shall be homogeneou

12、s and free of water.1This specification is under the jurisdiction of ASTM Committee D08 onRoofing and Waterproofing and is the direct responsibility of Subcommittee D08.03on Surfacing and Bituminous Materials for Membrane Waterproofing and Built-upRoofing.Current edition approved July 1, 2016. Publi

13、shed July 2016. DOI: 10.1520/D8051_D8051M-16.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approv

14、ed version of this historical standard is referenced onwww.astm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15.2 The products of each type shall conform to the physicalproperties prescribed in Table 1.6. Sampling and Test Metho

15、ds6.1 Sample the material and determine the properties enu-merated in this specification in accordance with the followingmethods:6.1.1 SamplingPractice D140/D140M.6.1.2 Softening PointSee Test Methods D36/D36M orD3461. In cases where a disagreement exists between thepurchaser and the seller, Test Me

16、thod D36/D36M shall be usedas the referee method.6.1.3 Flash PointTest Method D92.6.1.4 PenetrationTest Method D5/D5M.6.1.5 DuctilityTest Method D113.6.1.6 SolubilityTest Method D2042 or Test MethodD7553. In cases where a disagreement exists between thepurchaser and the seller, Test Method D2042 sha

17、ll be used asthe referee method.6.1.7 EVTTest Method D4402/D4402M is used to deter-mine what temperatures result in the viscosity values thatdefine EVT for mopping and mechanical application.7. Inspection7.1 Inspection of the material shall be agreed upon betweenthe purchaser and the seller as part

18、of the purchase contract.8. Rejection and Rehearing8.1 Failure to conform to any of the requirements prescribedin this specification shall constitute grounds for rejection. Incase of rejection, the seller shall have the right to re-inspect therejected material and resubmit the lot after removal of t

19、hosepackages not conforming to the requirements.9. Packaging and Package Marking9.1 The asphalt product shall be suitably packaged (if notshipped in bulk) to permit acceptance by the carrier and toafford adequate protection from the normal hazards of handlingand shipment.9.2 Each container or bill o

20、f lading on bulk shipments shallbe plainly marked with the name of the manufacturer or seller,the ASTM designation, maximum kettle temperature of 246C475F and the lot specific equiviscous temperature (EVT) formop and for mechanical spreader application.10. Keywords10.1 asphalt; built-up roof; equivi

21、scous temperature; roof-ing; softening point; synthetic wax; wax-modified asphaltAPPENDIX(Nonmandatory Information)X1. APPLICATION GUIDE AND BENEFITSX1.1 For built-up membrane construction, asphalt should beapplied within the EVT application range for asphalt describedin Terminology D1079.X1.2 At no

22、 time should the kettle temperature exceed 246C475F.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rig

23、hts, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for

24、 revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing

25、 you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may

26、 be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers,

27、 MA 01923, Tel: (978) 646-2600; http:/ 1 Physical Requirements of Wax-Modified Asphalt for Usein RoofingPropertyMin MaxOxidized Base Asphalt before ModificationSoftening Point, C F 60 140 70 158Penetration at 25C 77F, dmm 20 30Final Product after ModificationSoftening Point, C F 99 210 110 230Flash Point, C F 260 500Penetration, dmmat 0C 32F 6at 25C 77F 12 30at 46C 115F 75Ductility at 25C 77F, cm 4Solubility % 95EVT, C Fat 125 cPs 193 380at 75 cPs 210 410D8051/D8051M 162