ASTM F2206-2011 Standard Specification for Fabricated Fittings of Butt-Fused Polyethylene (PE) Plastic Pipe Fittings Sheet Stock Plate Stock or Block Stock《端面热熔聚乙烯塑料管 配件 片料 金属板料 或块.pdf

1、Designation: F2206 11An American National StandardStandard Specification forFabricated Fittings of Butt-Fused Polyethylene (PE) PlasticPipe, Fittings, Sheet Stock, Plate Stock, or Block Stock1This standard is issued under the fixed designation F2206; the number immediately following the designation

2、indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification establishes requir

3、ements for fabri-cated fittings intended for use with outside-diameter controlledpolyethylene pipe and tubing. These fittings are manufacturedby heat-fusion joining shape-modified polyethylene compo-nents prepared from pipe, molded fittings, sheet, or block.Included are requirements for materials, d

4、esign, workmanship,minimum dimensions, marking, test methods, and qualitycontrol.1.2 Pressure rating of the fabricated-fitting design is beyondthe scope of this standard and shall be established by the fittingmanufacturer. This specification includes requirements for bothelevated temperature pressur

5、e-tests and short-term pressuriza-tion tests to demonstrate a reasonable level of performance ofthe fabricated-fitting design at the pressure rating establishedby the fitting manufacturer.1.3 The pressure-tests requirements are specified by thefittingsequivalent (E) DR. The EDR specified is the DR o

6、f thepiping system for which the fabricated fitting is intended to bebutt-fused.1.4 The text of this standard references notes and footnoteswhich provide explanatory material. These notes and footnotes(excluding those in tables and figures) shall not be consideredas requirements of the standard.1.5

7、UnitsThe values stated in inch-pound units are to beregarded as standard. The values given in parentheses aremathematical conversions to SI units which are provided forinformation only and are not considered standard.1.6 The following safety hazards caveat pertains only to thetest methods portion, S

8、ection 9, of this specification. Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions pr

9、ior to use.2. Referenced Documents2.1 ASTM Standards:2D1600 Terminology for Abbreviated Terms Relating toPlasticsD2122 Test Method for Determining Dimensions of Ther-moplastic Pipe and FittingsD2513 Specification for Polyethylene (PE) Gas PressurePipe, Tubing, and FittingsD3035 Specification for Pol

10、yethylene (PE) Plastic Pipe(DR-PR) Based on Controlled Outside DiameterD3261 Specification for Butt Heat Fusion Polyethylene(PE) Plastic Fittings for Polyethylene (PE) Plastic Pipe andTubingF412 Terminology Relating to Plastic Piping SystemsF714 Specification for Polyethylene (PE) Plastic Pipe(SDR-P

11、R) Based on Outside DiameterF2619/F2619M Specification for High-Density Polyethyl-ene (PE) Line PipeF2880 Specification For Lap-Joint Type Flange Adaptersfor Polyethylene Pressure Pipe in Nominal Pipe Sizes 3/4in. to 65 in.2.2 Federal Standards:3Fed. Std. No. 123 Marking for Shipment (Civil Agencies

12、)OPS Part 192 Title 49, Code of Federal Regulations2.3 Military Standard:3MIL-STD-129 Marking for Shipment and Storage2.4 ANSI/NSF Standard:4ANSI/NSF 61 for Drinking Water System ComponentsHealth Effects2.5 Plastic Pipe Institute:5TR-4 Listing of Hydrostatic Design Basis (HDB), Hydro-static Design S

13、tress (HDS), Strength Design Basis (SDB),1This specification is under the jurisdiction of ASTM Committee F17 on PlasticPiping Systems and is the direct responsibility of Subcommittee F17.10 on Fittings.Current edition approved April 1, 2011. Published April 2011. Originallyapproved in 2002. Last pre

14、vious edition approved in 2010 as F2206 02(2010).DOI: 10.1520/F2206-11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe AST

15、M website.3Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-50984Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.5Available from Plastics Pipe Institu

16、te (PPI), 105 Decker Court, Suite 825,Irving, TX 75062, http:/www.plasticpipe.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Pressure Design Basis (PDB) and Minim

17、um RequiredStrength (MRS) for Thermoplastic Materials or Pipe.3. Terminology3.1 Definitions are in accordance with Terminology F412and abbreviations are in accordance with Terminology D1600,unless otherwise specified.3.2 Definitions:3.2.1 butt-fusion end(s), nthe butt end(s) of the fabricatedfitting

18、 intended for field fusion by the installer.3.2.2 fabricated fitting, na fitting constructed from manu-factured polyethylene components or materials.3.3 Abbreviations:3.3.1 DIPSductile iron pipe size.3.3.2 DRdimension ratio.3.3.3 EDRequivalent dimension ratio. The DR of the pipeto which the fitting

19、is to be joined.3.3.4 IPSiron pipe size.3.3.5 ODoutside diameter.4. Classification4.1 GeneralThis specification establishes requirementsfor fabricated fittings intended for butt-fusion joining topolyethylene pipe.4.1.1 Fabricated fitting components may be machined fromextruded polyethylene or molded

20、 polyethylene stock andheat-fused to form the final part.4.1.2 Fabricated fittings intended for use in the distributionof natural gas or other fuel gases shall also meet the require-ments of Specification D2513.5. Ordering Information5.1 When ordering fittings under this specification includethe fol

21、lowing information:5.1.1 Polyethylene compound (material designation or tradename).5.1.2 Style of fitting (3 piece tee, 5 segment 90 ell, etc.).5.1.3 Size:5.1.3.1 Nominal size of end connections.5.1.3.2 End configurations (for example, IPS or DIPS).5.1.3.3 System DR.6. Material6.1 Polyethylene mater

22、ials allowed for use in fittings pro-duced in accordance with this specification shall be in accor-dance with the manufacturers fabricated-fitting design speci-fications. In addition:6.1.1 Polyethylene pipe used in the production of fittings inaccordance with this specification shall meet the requir

23、ementsof Specification F714, D3035, F2619/F2619M or D2513.6.1.2 Molded PE fittings used in the production of fabri-cated fittings in accordance with this specification shall meetthe requirements of Specification D3261.6.1.3 Flange adaptors used in the production of fabricatedfittings in accordance w

24、ith this specification shall meet therequirements of Specification F2880.6.1.4 Sheet, block or plate stock used in the production offabricated fittings shall be produced from stress-rated polyeth-ylene compounds listed in PPIs TR-4.NOTE 1Manufacturers should use appropriate quality assurance pro-ced

25、ures to ensure that sheet, block and plate are free from voids,laminations, foreign inclusions, cracks, and other injurious defects.7. Requirements7.1 Dimension and TolerancesButt-fusion ends shall beproduced from fittings or pipe conforming to SpecificationD3261, or by machining block, sheet, plate

26、, or pipe to therequired dimensions.7.1.1 DiameterNominal outside-diameter of the butt-fusion end shall conform to the IPS or DIPS dimension at areaof fusion. Outer-diameter dimensions and tolerances at the areaof fusion shall be as shown in Table 1 or Table 2.7.1.2 Wall ThicknessThe minimum wall th

27、ickness of thebutt-fusion end shall be in accordance with Table 1 or Table 2when measured in accordance with Test Method D2122.Conditioning to standard temperature but not to standardhumidity is required.7.1.3 EccentricityThe wall thickness variability of thebutt-fusion end as measured and calculate

28、d in accordance withTest Method D2122, in any diametrical cross-section of thepipe shall not exceed 12 %.7.1.4 MeasurementsThese shall be made in accordancewith Test Method D2122 for roundable pipe.7.1.5 Laying LengthsLaying length dimensions shall bedefined by the manufacturer.7.1.6 Special SizesWh

29、ere existing system conditions orspecial local requirements make other diameters or dimensionratios necessary, other sizes or dimension ratios, or both, shallbe acceptable for engineered applications when mutuallyagreed upon by the customer and the manufacturer, if the fittingis manufactured from pl

30、astic compounds meeting the materialrequirements of this specification, and the fitting performs inaccordance with the requirements in this specification. Fordiameters not shown in Table 1 or Table 2, the tolerance shallbe the same percentage as that shown in the correspondingtables for the next sma

31、ller listed size. Minimum wall thicknessat the butt-fusion end for these special sizes shall not be lessthan the minimum wall thickness specified for the pipe thefitting is designed to be used with.7.2 Physical RequirementsFabricated fittings using mitercut pipe stock shall be manufactured from pipe

32、 stock with awall thickness that is at least 22% greater than that of the pipeto which the fitting is to be joined. (For example: An EDR11fitting shall be made using DR9 pipe stock.)7.3 Pressure Test RequirementsDesign validation tests per7.3.1 and 7.3.2 shall be conducted on “test samples” that are

33、representative of:Each of three (3) size groupings - 12 in. (300 mm) and smaller,greater than 12 to less than 24 in. (300 to less than 600 mm), and24 in. (600 mm) and larger.Each style of fitting (for example, 4 segment 90 Elbow, StraightTee, etc.).A single EDR sample shall be considered as represen

34、tativeof all of the wall thickness produced in that size and stylegrouping. The EDR of the test fitting(s) shall be in the midrange of the wall thickness typically produced for that sizegrouping. Fitting styles are characterized as elbows, tees, wyes,crosses, reducing tees, reducing laterals, branch

35、 saddles, me-chanical joint adapters, and end caps.F2206 1127.3.1 Elevated Temperature Sustained Pressure TestThe“test sample” shall be three specimens. Each specimen shallhave a minimum distance of three pipe diameters between endclosure(s) and any miter joints in the fitting(s).7.3.2 Short-term Pr

36、essurization TestingQuick Burst ofNon-Failure testing shall be conducted. The “test sample” shallbe five specimens. Each specimen shall have a minimumdistance of three pipe diameters between end closure(s) andany miter joints in the fittings(s).8. Workmanship, Finish and Appearance8.1 The manufactur

37、e of these fittings shall be in accordancewith good commercial practice so as to produce fittingsmeeting the requirements of this specification. Fittings shall behomogeneous throughout and free of cracks, holes, foreigninclusions or other injurious defects. The fittings shall be asuniform as commerc

38、ially practicable in color, opacity, density,and other physical properties.8.2 The procedure used for the heat fusion in the fabricationprocess shall be written and qualified in accordance with therequirements of OPS 49 CFR Part 192.283 “Plastic Pipe:Qualifying Joining Procedures.”8.3 All personnel

39、engaged in the heat fusion process shall bequalified in accordance with the requirements of OPS 49 CFRPart 192.285 “Plastic Pipe: Qualifying Persons to MakeJoints.”9. Test Methods9.1 GeneralThe test methods in this specification apply tofittings for use with pipe and tubing for gas, water, and other

40、engineered piping systems.TABLE 1 IPS Sizing System: Butt-Fusion End Dimensions, in.SizeIPSAverageODAMinimum Wall ThicknessBversus DR7.3 9 9.3 11 13.5 15.5 17 21 26 32.52 2.38 . 0.26 . 0.22 0.18 . 0.14 . . .3 3.500 0.479 0.389 0.376 0.318 0.259 0.226 0.206 0.167 0.135 0.1084 4.500 0.616 0.500 0.484

41、0.409 0.333 0.290 0.265 0.214 0.173 0.1385 5.563 0.762 0.618 0.598 0.506 0.412 0.359 0.327 0.265 0.214 0.1716 6.625 0.908 0.736 0.712 0.602 0.491 0.427 0.390 0.315 0.255 0.2048 8.625 1.182 0.958 0.927 0.784 0.639 0.556 0.507 0.411 0.332 0.26510 10.750 1.473 1.194 1.156 0.977 0.796 0.694 0.632 0.512

42、0.413 0.33112 12.750 1.747 1.417 1.371 1.159 0.944 0.823 0.750 0.607 0.490 0.39214 14.000 1.918 1.556 1.505 1.273 1.037 0.903 0.824 0.667 0.538 0.43116 16.000 2.192 1.778 1.720 1.455 1.185 1.032 0.941 0.762 0.615 0.49218 18.000 2.466 2.000 1.935 1.636 1.333 1.161 1.059 0.857 0.692 0.55420 20.000 . .

43、 . 2.222 2.151 1.818 1.481 1.290 1.176 0.952 0.769 0.61522 22.000 . . . 2.444 2.366 2.000 1.630 1.419 1.294 1.048 0.846 0.67724 24.000 . . . 2.667 2.581 2.182 1.778 1.548 1.412 1.143 0.923 0.73826 26.000 . . . . . . 2.796 2.364 1.926 1.677 1.529 1.238 1.000 0.80028 28.000 . . . . . . 3.011 2.545 2.0

44、74 1.806 1.647 1.333 1.077 0.86230 30.000 . . . . . . 3.226 2.727 2.222 1.935 1.765 1.429 1.154 0.92332 32.000 . . . . . . . . . 2.909 2.370 2.065 1.882 1.524 1.231 0.98534 34.000 . . . . . . . . . 3.091 2.519 2.194 2.000 1.619 1.308 1.04636 36.000 . . . . . . . . . 3.273 2.667 2.323 2.118 1.714 1.3

45、85 1.10842 42.000 . . . . . . . . . . . . . . . 2.710 2.471 2.000 1.615 1.29248 48.000 . . . . . . . . . . . . . . . 3.097 2.824 2.286 1.846 1.47754 54.000 . . . . . . . . . . . . . . . . . . 3.176 2.571 2.077 1.662ATolerance on OD is 6 0.45 %.BEccentricity of wall shall not exceed 12 %.TABLE 2 DIPS

46、 Sizing System: Butt-Fusion End Dimensions, in.SizeDIPSAverageODAMinimum Wall ThicknessBversus DR9 11 13.5 17 21 26 32.53 3.96 0.389 0.360 0.294 0.233 0.189 0.153 0.1224 4.80 0.500 0.437 0.356 0.283 0.229 0.185 0.1486 6.90 0.736 0.628 0.512 0.406 0.329 0.266 0.2138 9.05 0.958 0.823 0.670 0.533 0.431

47、 0.348 0.27910 11.10 1.194 1.009 0.823 0.653 0.529 0.427 0.34212 13.20 1.417 1.200 0.978 0.777 0.629 0.508 0.40714 15.30 1.556 1.391 1.134 0.900 0.729 0.589 0.47116 17.40 1.778 1.582 1.289 1.024 0.829 0.670 0.53618 19.50 2.000 1.773 1.445 1.147 0.929 0.750 0.60020 21.60 2.222 1.964 1.600 1.271 1.029

48、 0.831 0.66524 25.80 2.667 2.346 1.912 1.518 1.229 0.993 0.79430 32.00 . . . 2.909 2.371 1.883 1.524 1.231 0.98536 38.30 . . . 3.482 2.837 2.253 1.824 1.473 1.17942 44.50 . . . 4.046 3.297 2.618 2.119 1.712 1.37048 50.80 . . . 4.619 3.763 2.989 2.419 1.954 1.563ATolerance on OD is 6 0.45 %.BEccentri

49、city of wall shall not exceed 12 %.F2206 1139.2 ConditioningUnless otherwise specified, conditionthe specimens prior to test at 73.4 6 3.6F (23 6 2C) for notless than6hinairor1hinwater.9.3 Test ConditionsConduct the tests at the standardlaboratory temperature of 73.4 6 3.6F (23 6 2C) unlessotherwise specified.9.4 Dimensions and Tolerances:9.4.1 Outside DiameterMeasure the outside diameter ofthe fittings at the butt-fusion end in accordance with the WallThickness section of Test Method D2122 by use of circumfer-ential tape readable to the nea