1、BRITISH STANDARD BS2588-2: 1992 Portable sanitary pans for use in healthcare establishments Part2: Specification for reusable pans for commode chairsBS2588-2:1992 This British Standard, having been prepared under the directionof the Health Care Standards Policy Committee, waspublished under the auth
2、orityof the Standards Boardand comes into effect on 28February1992 BSI 08-1999 The following BSI references relate to the work on this standard: Committee reference HCC/21 Draft for comment91/51368DC ISBN 0 580 20437 5 Committees responsible for this British Standard The preparation of this British
3、Standard was entrusted by the Health Care Standards Policy Committee (HCC/-) to Technical Committee HCC/21, upon which the following bodies were represented: Association of Clinical Pathologists Association of Sterilizer and Disinfector Equipment Manufacturers British Glass Manufacturers Confederati
4、on British Laboratory Ware Association British Plastics Federation Central Sterilising Club Department of Health Healthcare Sanitary Systems Association Hospital Infection Society Independent Healthcare Association Infection Control Nurses Association Institute of Hospital Engineering Institute of S
5、terile Services Management Joint Committee of Professional Nursing, Midwifery and Health Visiting Associations (England) National Health Services National Health Service Regional Engineers Association Queens Nursing Institute Royal College of Midwives Royal College of Nursing Royal College of Pathol
6、ogists Royal College of Surgeons of Edinburgh Scottish Health Services Amendments issued since publication Amd. No. Date CommentsBS2588-2:1992 BSI 08-1999 i Contents Page Committees responsible Inside front cover Foreword ii 1 Scope 1 2 Definitions 1 3 Classification of commode pans 1 4 Materials 1
7、5 Surface finish 1 6 Construction 3 7 Performance 4 8 Lid 4 9 Marking 4 Appendix A Information to be supplied by the purchaser 6 Appendix B Rim test (for type1 commode pans only) 6 Appendix C Strength and stability tests for commode pans 6 Appendix D Temperature stability test 7 Figure 1 Schematic d
8、iagram of the test arrangements 7 Table 1 Test methods and requirements for plastics materials 2 Table 2 Test methods and requirements for the durability of the paint coatings on metal 3 Table 3 Overall dimensions of commode pans 4 Publication(s) referred to Inside back coverBS2588-2:1992 ii BSI 08-
9、1999 Foreword This Part of BS2588 has been prepared under the direction of the Health Care Standards Policy Committee The first edition of BS2588, which was published in 1955, was prepared at the request of the Hospital Equipment Standards Advisory Committee of the British Standards Institution. In
10、that edition, only the adult size Perfection 1)type of bed pan was specified. When considering the revision of BS2588:1955, it was confirmed that the design criteria for bed pans were not wholly applicable to the portable sanitary pans to be used with commode chairs. Accordingly, it was agreed that
11、the new edition of BS2588 should be prepared in two Parts with Part1 specifying the requirements for bed pans, and this Part (Part2) specifying two types of portable pan for use in commode chairs. Type1 pans are designed with a lip which rests on supporting bearers in the commode chair. Type2 pans a
12、re designed with the base supported by a level surface at between100mm and150mm beneath the commode seat. The sizes of the pans are compatible with the dimensions specified for WC seats specified in BS1254, and with bed pan washer disinfectors specified in BS2745. NOTEAlthough this specification has
13、 not been drafted to cover portable commode pans for use with mobile sanitary chairs complying with BS4751 which have been fitted with a suitable cradle or support frame, the commode pans are capable of use with such chairs. Also a pan specified in this Part of BS2588 may be used as a bed pan but it
14、 should also comply with the requirements of Part1. Two grades of bed pan are specified. Grade A pans, which are capable of withstanding heat sterilization at134 C, are specified for those who need a sterilizable pan; grade B pans, which will withstand heat disinfection at100 C, are satisfactory for
15、 most purposes. This Part of BS2588 specifies performance and marking requirements for reusable pans for commode chairs. It also specifies the surface finish as the quality of finish is of particular importance from the standpoint of ease of cleaning and disinfection and of resistance to corrosion.
16、It has been assumed in the drafting of this standard that the tests for assessing compliance will be carried out by those who are appropriately qualified or under the supervision of experienced personnel. If the quality of a product can be assured only by in-process control, the user of this standar
17、d may wish to consider product certification. Where in-process quality control is not appropriate the user of this standard may wish to consider assessed capability. Product certification. Users of this British Standard are advised to consider the desirability of third party certification for produc
18、t conformity with this BritishStandard based on testing and continuing surveillance, which may be coupled with assessment of a suppliers quality systems against the appropriate Part of BS5750. Enquiries as to the availability of third party certification schemes will be forwarded by BSI to the Assoc
19、iation of Certification Bodies. If a third party certification scheme does not already exist, users should consider approaching an appropriate body from the list of Association members. Assessed capability. Users of this British Standard are advised to consider the desirability of assessment and reg
20、istration of a suppliers quality systems against the appropriate Part of BS5750 by a third party certification body. 1) “Perfection” is a term widely recognized by the industry concerned to indicate a specific shape of bed pan.BS2588-2:1992 BSI 08-1999 iii A British Standard does not purport to incl
21、ude all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages
22、i toiv, pages1to8, an inside back cover and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover.iv blankBS2588-2:1992 BSI 08-1999 1 1 Scope This British Standard specifies
23、materials, construction and performance requirements for reusable sanitary pans intended for use with commode chairs. Grade A pans are designed to withstand heat sterilization at134 C; gradeB pans are capable of withstanding heat disinfection at100 C. NOTE 1Appendix A gives details of the informatio
24、n to be supplied by the purchaser to the manufacturer. NOTE 2The titles of the publications referred to in this standard are given on the inside back cover. 2 Definitions For the purposes of this British Standard the following definitions apply. 2.1 portable sanitary pan a receptacle or container de
25、signed to collect human waste and to enable its subsequent safe transport to a place for disposal of the waste 2.2 disinfection the process used to reduce the number of viable micro-organisms in a product but which may not necessarily inactivate some viruses and bacterial spores 2.3 sterilization th
26、e process used to render a product free from viable micro-organisms 2.4 commode chair a chair designed with a seat, with an aperture, under which may be fitted a portable sanitary pan 2.5 commode pan a portable sanitary pan designed for use in a commode chair 3 Classification of commode pans 3.1 Typ
27、es Commode pans shall be classified as follows: a) type1 for pans provided with a rim which is intended to rest on supporting bearers in the commode chair (e.g.with the seat raised or removed, the pan may be lowered onto the bearers or, with the seat in place, the pan may be slid horizontally on to
28、the bearers); b) type2 for pans intended to rest on a level surface beneath the seat of a commode chair (e.g.the pan may be slid horizontally beneath the aperture in the chair seat or the seat may be lowered over the pan). 3.2 Grades Commode pans and, if fitted, their lids shall be graded as follows
29、: a) gradeA for pans capable of withstanding heat sterilization at a minimum of134 C; b) gradeB for pans capable of withstanding heat disinfection at100 1 C. 4 Materials 4.1 Plastics materials Plastics materials used for the construction of any part of the commode pan shall comply with the requireme
30、nts given in Table 1. Expanded or cellular (foam) plastics materials shall not be used. 4.2 Stainless steel Stainless steel used for the construction of any part of the commode pan shall comply with grades304S15 or304S16 of BS1449-2. 4.3 Coated constructions Coating materials used for the constructi
31、on of any part of the commode pan shall comply with the requirements given in Table 2. (See also7.4.) NOTECoatings may be applied to any suitable metal substrate. 5 Surface finish NOTEAbrasives can significantly scratch some surfaces and the manufacturer should warn the user when a surface is especi
32、ally vulnerable and is to be cleaned with extra care. Seealso item c) in both 9.1 and 9.2. 5.1 The surface finish of the commode pan shall be smooth and all surfaces shall be free from any discontinuities or crevices with a radius of curvature of less than3mm. 5.2 In addition, the surface finish of
33、uncoated stainless steel shall comply with finish no.4 or finish no.8 of BS1449-2. BS2588-2:1992 2 BSI 08-1999 Table 1 Test methods and requirements for plastics materials Property Test method Number of samples Requirement Rockwell hardness BS2782-3:Method365C 3 No sample shall have a hardness numbe
34、r of less than R94 Shore hardness BS2782-3:Method365B 3 No sample shall have a hardness of less than73 when using a type A durometer Resistance to liquids BS3900-G5 using test method3: exposure time60min, no recovery period and using the following test liquids: a) ethanol94%(V/V) industrial methylat
35、ed spirits; b) acetone; c) glacial acetic acid,50% (V/V) in water; d) bleach(1% available chlorine); e) phenol,2%(m/m) in water. 3pieces cut from the commode pan, for each test liquid In comparison with an untested sample, there shall be no blistering, pitting, softening or discolorationBS2588-2:199
36、2 BSI 08-1999 3 Table 2 Test methods and requirements for the durability of the paint coatings on metal 6 Construction 6.1 Overall dimensions The commode pan shall have the overall dimensions given in Table 3. NOTEThese dimensions should enable the pan to fit into bed pan washer-disinfectors complyi
37、ng with BS2745 2) . (SeealsoA.4.) Property Test method Test panel Number of test panels Requirement Resistance to bending BS3900-E1 Type2apparatus, using a12mm mandrel Mild steel, 1.2mm thick 3 No coating shall show cracks or loss of adhesion visible with normal or corrected vision Resistance to scr
38、atch BS3900-E2 3000g load Mild steel, 1.2mm thick 3 No panel shall show bare metal Resistance to impact (falling weight) BS3900-E3 Indentationof3mm with coating facing upwards Mild steel, 1.2mm thick 3 No coating shall show loss of adhesion Resistance to cupping BS3900-E4 Indentationof3mm on coated
39、and uncoated sides Mild steel, 1.2mm thick 3 No coating shall show cracks or loss of adhesion visible with normal or corrected vision Resistance to cross-cuts BS3900-E6 Singlecuttingtool, manually operated, producing six cuts in each direction at2mm spacing Mild steel, 1.2mm thick 3 No coating shall
40、 exceed classification2 of BS3900-E6 Resistance to humidity BS3900-F9 Durationoftest96h; no interim examination, no recovery period Mild steel, 1.2mm thick, coated on one face only 3 No coating shall show a colour change or formation of rust Resistance to liquids BS3900-G5 Testmethod3:exposure time6
41、0min, no recovery period; no removal of coating after exposure; test area covered, using test liquids: a) ethanol 94%(V/V) industrial methylated spirits; b) acetone; c) glacial acetic acid,50%(V/V) in water; d) bleach(1% available chlorine); e) phenol,2%(m/m) in water. Mild steel, 1.2mm thick, coate
42、d on one face only 3 No coating shall show blistering, pitting, softening or bleaching 2) BS2745 is currently being revised.BS2588-2:1992 4 BSI 08-1999 Table 3 Overall dimensions of commode pans All surfaces shall be capable of being visually inspected without the aid of instruments or equipment. 6.
43、2 Capacity 6.2.1 Minimum capacity When placed on a firm horizontal surface, the pan shall be capable of containing not less than2500ml of water without overflowing from the pan, and without leakage. 6.2.2 Tilt capacity When the pan containing not less than1000ml of water is tilted at20 from the hori
44、zontal in any direction, there shall be no spillage. 6.3 Rim When tested as described in Appendix B, the heights of the rim of a type1pan shall not change by more than3%. 7 Performance 7.1 Strength When tested as described inC.2, no dimensions of the commode pan shall change by more than3%. 7.2 Stab
45、ility When tested as described inC.3, the commode pan shall be free-standing. 7.3 Drainage When the commode pan, containing not less than100ml water, is tipped with its longest axis at an angle of110 to the horizontal and with its minimum height at its lowest point, no more than5ml water shall be re
46、tained after2min. 7.4 Temperature stability When the commode pan is tested as described in Appendix D, no dimension shall have changed by more than5% and, if the pan is manufactured from coated materials (see4.3), the coating shall have remained intact and shall not have lifted from the substrate. 7
47、.5 Durability When the commode pan, in an essentially horizontal attitude and containing not less than750ml water at a temperature of between15 C and25 C, is dropped successively three times from a height of1500 50mm on to a concrete paving slab complying with BS7263-1, the pan shall neither split n
48、or be deformed by more than10mm in any dimension. 7.6 Resistance to ignition When the pan is tested in accordance with section4of BS5852:1990, it shall be resistant to ignition sources0 and1. 8 Lid 8.1 If requested by the purchaser, the commode pan shall be supplied with a loose-fitting lid, with a
49、handle, constructed from the same material as that of the pan. The surface finish of the lid except the edge of the rim shall comply with clause5. The edge of the rim shall have no burrs. 8.2 After the lid in an essentially vertical attitude has been dropped successively three times from a height of1500 50mm on to a concrete paving slab complying with BS7263-1, the lid shall still fit on the pan. 8.3 In at least one attitude with a major axis inclined at not less than70 to the horizontal, the lid shall retain not more than1.0ml of water