DIN 1164-12-2005 Special cement - Part 12 Composition specification and conformity evaluation for cement with higher quantity of organic constituents《特种水泥 第12部分 高含量有机成分水泥的组分、要求和合格评.pdf

1、June 2005DEUTSCHE NORM English price group 5No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 91.100.10!$Qt,“1468109w

2、ww.din.deDDIN 1164-12Special cement cement with a high quantity of organic constituentsZement mit besonderen Eigenschaften Teil 12: Zusammensetzung, Anforderungen und bereinstimmungsnachweis von Zementmit einem erhhten Anteil an organischen Bestandteilenwww.beuth.deDocument comprises 6 pagesIn case

3、of doubt, the German-language original should be consulted as the authoritative text.Translation by DIN-Sprachendienst.Part 12: Composition, requirements and conformity assessment forDIN 1164-12:2005-06 2 Contents Page Foreword2 1 Scope 2 2 Normative references 3 3 Terms and definitions .3 4 Cement

4、with a high quantity of organic constituents3 5 Constituents.3 6 Composition.4 7 Mechanical, physical, chemical and durability requirements.4 8 Standard designation 4 9 Conformity criteria.5 10 Delivery .5 11 Conformity assessment 5 11.1 General5 11.2 Granting and withdrawal of certificate of confor

5、mity 6 11.3 Marking .6 Tables Table 1 Colour coding for strength classes 5 Foreword The DIN 1164 series of standards consists of the following parts: Part 10: Composition, requirements and conformity assessment for common cement Part 11: Composition, requirements and conformity assessment for cement

6、 with a shortened setting time Part 12: Composition, requirements and conformity assessment for cement with a high quantity of organic constituents This standard deals with cement no longer covered in DIN 1164-1:1994-10. When EN 197-1 (for normal cement) was implemented as DIN EN 197-1:2001-02, ceme

7、nt with a high content of organic constituents was not included in the residual standard DIN 1164:2000-11. Part 12 has subsequently been developed to account for this. 1 Scope This standard is to be used in conjunction with DIN EN 197-1 for normal cement and DIN 1164-10 for special cement. It specif

8、ies requirements for the composition and manufacture, and for the mechanical, physical and chemical properties of special cement with a high content of organic constituents, and the procedures to be followed when checking such cement for its compliance with these requirements. DIN 1164-12:2005-06 3

9、2 Normative references The following referenced documents are indispensable for the application of this standard. For dated references, the edition referred to applies. For undated references, the latest edition of the publication referred to (including any amendments) applies. DIN 1164-10:2004-08,

10、Special cement Composition, requirements and conformity assessment for common cement DIN V 18998:2002-11, Determining the corrosive effect of modifiers as specified in DIN EN 934 DIN EN 196-1, Methods of testing cement Part 1: Determination of strength DIN EN 196-3, Methods of testing cement Part 3:

11、 Determination of setting time and soundness DIN EN 197-1:2004-08, Cement Part 1: Composition, specifications and conformity criteria for common cements DIN EN 197-2:2000-11, Cement Part 2: Conformity assessment DIN EN 459-2:2002-02, Building lime Part 2: Test methods DIN EN 934 series, Modifiers fo

12、r concrete, mortar and grout 3 Terms and definitions For the purposes of this standard, the terms and definitions in DIN 1164-10, DIN EN 197-1 and DIN EN 197-2 apply. 4 Cement with a high quantity of organic constituents Cement with a high quantity of organic constituents (HO type cement) shall meet

13、 the general requirements as specified both in clause 4 of DIN EN 197-1:2004-08 and in the present standard. 5 Constituents The constituents of cement conforming to this standard shall be as specified in 5.1 to 5.4 of DIN EN 197-1:2004-08. The content of additives shall not exceed 1 % (m/m). Where t

14、he content of organic constituents in the dry cement exceeds 0,5 %, this is to be indicated on the bag or in the delivery note. Additives shall not have any corrosive effect on reinforcement. Only modifiers listed in Annex A of DIN V 18998:2002-11 shall normally be used. Otherwise proof of suitabili

15、ty of the modifiers shall be provided. NOTE This proof may take the form of a specific or general agrment. Where additives (except those used to control the setting behaviour of SE type cement) contain modifiers that are also used in admixtures for mortar, concrete or grout as in the DIN EN 934 seri

16、es and that tend to modify the cement properties, their type as in DIN V 18998 shall be indicated on the bag and/or delivery note. DIN 1164-12:2005-06 4 6 Composition The composition of cement with a high content of organic constituents shall be as specified in Table 1 of DIN EN 197-1:2004-08. 7 Mec

17、hanical, physical, chemical and durability requirements Cement with a high content of organic constituents shall meet the mechanical, physical, chemical and durability requirements specified in clause 7 of DIN EN 197-1:2004-08. Where cement contains highly liquefactive additives, these may cause cha

18、nges to the consistency of the cement paste or mortar produced, which in turn may entail certain modifications to the physical test methods described in DIN EN 196-1 and DIN EN 196-3, as follows. a) Strength testing as in DIN EN 196-1 When filling the mortar into the mould, the material may segregat

19、e or settle. To prevent this, 0,1 % to 0,2 % by mass of organic stabilizer1)(in relation to the cement) shall be added to the mortar, which is not to be compacted when in the mould. After filling, the mould shall first be covered with plastic film and then with a glass plate. NOTE If the flow diamet

20、er of the mortar exceeds 240 mm, the strength test as in DIN EN 196-1 will presumably have to be modified. The flow diameter shall be determined using the flow table as specified in DIN EN 459-2, but after lifting the mould, without any prior jolting of the table. b) Determining the standard consist

21、ence as in DIN EN 196-3 Testing shall be repeated with pastes containing different water contents until one is found to produce a distance between plunger and base plate of (6 1) mm. Since the addition of only a few drops of water may cause a marked change in the cement paste consistence, the latter

22、 cannot be determined to the specified accuracy. In this case, the tolerance on the above dimension (of 6 mm) may be enlarged to become 3 mm. 8 Standard designation Cement with a high content of organic constituents shall be designated at least by the symbol denoting the cement type (cf. Table 1 of

23、DIN EN 197-1:2004-08), the figure (32,5, 42,5 or 52,5) indicating the strength class and the code letter N or R denoting the early strength class of the cement (cf. 7.1 of DIN EN 197-1:2004-08). Any special property as specified in DIN 1164-10 shall be indicated by the appropriate code letter as sha

24、ll be the type of cement as in the present standard (HO). Any deviations in chloride content from Table 3 of DIN EN 197-1:2004-08 (cf. footnote f in that table) and deviations from the loss on ignition of fly ash as in 5.2.4.1, 2ndparagraph, of DIN EN 197-1:2004-08 (cf. 5.3.4.1, 3rdparagraph, of DIN

25、 EN 197-1:2004-08) shall be given after the standard designation. EXAMPLE 1 Designation of Portland limestone cement with a limestone (LL) content between 6 % and 20 % (CEM II/A-LL), of strength class 42,5 and with a high content of organic constituents (HO): Portland limestone cement DIN 1164 CEM I

26、I/A-LL 42,5 R HO 1) Information on sources of supply is obtainable from the Normenausschuss Bauwesen (Building and Civil Engineering Standards Committee), DIN, 10772 Berlin, Germany. DIN 1164-12:2005-06 5 EXAMPLE 2 Designation of type CEM I Portland cement of strength class 42,5, with a low alkali c

27、ontent (NA) and a high content of organic constituents (HO): Portland cement DIN 1164 CEM I 42,5 N NA/HO 9 Conformity criteria Compliance of cement with the requirements specified in this standard shall be continually checked on the basis of the results obtained from testing spot samples in accordan

28、ce with clause 9 of DIN EN 197-1:2004-08. 10 Delivery Delivery documents shall bear the following information: mark of conformity (see 11.3); number of certificate of conformity; mass, i.e. gross weight of bag (25 kg) or net weight of bulk cement. In addition, the delivery documents for bulk cement

29、shall include the following details: date and time of delivery; registration number of delivery vehicle; customer, order number and consignee. Bags for special cement and their inscriptions shall be colour coded in accordance with Table 1. Table 1 Colour coding for strength classes Strength class Ba

30、ckground colour Contrast colour (inscription) 32,5 N Black 32,5 R Light brown Red 42,5 N Black 42,5 R Green Red 52,5 N Black 52,5 R Red White 11 Conformity assessment 11.1 General Compliance of special cement with the requirements specified in this standard shall be checked in accordance with DIN EN

31、 197-2:2000-11 (excluding clause 8) and certified as specified in 11.2 and 11.3. DIN 1164-12:2005-06 6 11.2 Granting and withdrawal of certificate of conformity 11.2.1 The inspection body shall provide the certification body with the following documentation: a) a report on initial inspection (if any

32、; cf. subclause 5.5.5 of DIN EN 197-2:2000-11); b) a report giving at least the results of the third party inspection tests carried out on the first sample taken for initial testing (cf. subclause 5.6.3 of DIN EN 197-2:2000-11). 11.2.2 If the inspection report indicates that the requirements specifi

33、ed in 5.5 of DIN EN 197-2:2000-11 are met, and if the results mentioned in 11.2.1 b) meet the requirements specified in clauses 4 to 7 and the conformity criteria specified in clause 9, the certification body will issue a certificate of conformity. 11.2.3 Throughout the rest of the initial period, t

34、he results of third party inspection testing and of factory production control (including autocontrol testing) shall be assessed and reported to the certification body (cf. subclause 5.6.3 of DIN EN 197-2:2000-11). 11.2.4 If the assessment referred to in subclause 11.2.3 is satisfactory, the certifi

35、cate of conformity remains valid as long as the specifications of DIN EN 197-2:2000-11 or the production conditions are not changed (unless it is to be withdrawn for the reasons listed in clause 6 of DIN EN 197-2:2000-11). 11.2.5 If production of a particular cement type is discontinued, the manufac

36、turer shall notify the inspection and certification bodies as soon as the stock of cement is depleted. The relevant certificate of conformity shall then be withdrawn without delay. The certificate of conformity is also to be withdrawn if third party inspection can no longer be carried out. 11.2.6 Ce

37、ment of a specified type or strength class that is produced at the same factory, is inspected, and is covered by a certificate of conformity, but which deliberately has a significantly different composition, physical or chemical properties or strength within the specified limits, can be identified a

38、nd treated as a different type of cement. 11.3 Marking 11.3.1 Conformity of a special cement with this standard shall be declared in a certificate of conformity issued by the certification body and indicated by an inspection mark applied to the product by the manufacturer. 11.3.2 The certificate of

39、conformity shall include the information given in the Muster fr bereinstimmungs-zertifikate nach 24 b MBO (Specimen form for certificate of conformity under article 24 b of the German Model Building Code2). 11.3.3 As proof of conformity of a cement, bags or delivery notes shall bear the inspection m

40、ark3)in addition to the information specified in clause 10. This mark shall include the following details: a) name of manufacturer; b) number of DIN Standard (DIN 1164) forming the basis of the assessment of conformity, and standard designation; c) logo or identification of certification body. 2) Se

41、e the Mitteilungen des Deutschen Instituts fr Bautechnik (Proceedings of the German Institute of Building Technology), 1995: 4, p. 101; obtainable from Verlag Wilhelm Ernst & Sohn, Mhlenstr. 3334, 13187 Berlin, Germany. 3) See the Mitteilungen des Deutschen Instituts fr Bautechnik, 1994: 5, p. 172.