FORD ESB-M11P31-A-2013 ADHESION REQUIREMENT ADHESIVE FOR BONDING MOLDED WEATHERSTRIP TO GLASS IN MODULE WINDOW ASSEMBLY TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Release No. Release/Revision 2013 12 12 N Status No replacement named L. Sinclair, NA 1985 03 22 C9P1-DR531035 Released Controlled document at www.MATS Page 1 of 3 ADHESION REQUIREMENT, ADHESIVE FOR BONDING ESB-M11P31-A MOLD

2、ED WEATHERSTRIP TO GLASS IN MODULE WINDOW ASSEMBLY NOT TO BE USED FOR NEW DESIGN 1. SCOPE This specification defines the adhesion requirements for an adhesive or an adhesive system suitable for bonding molded weatherstrip to glass in module window assembly. 2. APPLICATION This specification was rele

3、ased originally for adhesives used to bond ESB-M2D284 polyvinyl chloride weatherstrip to plain and ESB-M99G109 ceramic coated glass. Compliance with this performance specification does not guarantee the adhesive will function for all potential applications on a vehicle. The specific assembly should

4、be evaluated to Design Engineering performance requirements. Materials meeting this performance specification are specified on the Corporate Approved Source List. 3. REQUIREMENTS 3.1 CONDITIONING All test values indicated herein are based on materials conditioned in a controlled atmosphere of 23 +/-

5、 2 C and 50 +/- 5 % relative humidity for 24 h prior to testing and tested under the same conditions unless otherwise stated herein. 3.2 PEEL ADHESION Average load specified or substrate breakage Subject bonded test assemblies to the following exposures: . Normal, min (Condition for 30 min at specif

6、ied temperature prior to test) 3.2.1 Test at 23 +/- 2 C 18 N 3.2.2 Test at 88 +/- 1 C 9 N 3.2.3 Test at -29 +/- 1 C 36 N ENGINEERING MATERIAL SPECIFICATION ESB-M11P31-A Page 2 of 3 . Environmental Aged, min 3.2.4 1000 h heat age at 88 +/- 1 C 18 N 3.2.5 1000 h humidity at 38 +/- 2 C and 18 N 95 - 10

7、0 % R.H. 3.2.6 1000 h water immersion described per 18 N FLTM BI 4-1 3.2.7 240 h salt spray described per ASTM B 117 18 N 3.2.8 500 h Weatherometer described per 18 N FLTM BO 1-1 3.2.9 10 thermal cycles: 18 N 4 h at 88 +/- 1 C, 4 h humidity (38 +/- 2 C and 95 - 100 % R.H), 16 h at -29 +/- 2 C 3.2.10

8、 1 year Florida exposure, 5 South DWI 18 N Test Method: . Mold a 6.4 mm width x 200 mm length x 3.2 mm thick material section to an adhesive primed 300 x 300 mm glass plate. Substrates are identified in para 5.1. . Condition test assemblies for 4 h minimum at 23 +/- 2 C prior to environmental exposu

9、re. . Subject three test assemblies to each environment listed above. . Allow test assemblies to condition 24 h minimum at 23 +/- 2 C after environmental exposure before peel test. . Conduct 180 peel test using a tensile tester at 25 mm/min pull rate. 3.3 MODULE WINDOW ASSEMBLY PERFORMANCE REQUIREME

10、NTS Parts assembled with adhesive shall meet all engineering requirements specified by ES-D7WB-6529600-AA. 3.4 FUNCTIONAL APPROVAL Materials being evaluated for initial approval to this specification shall be subjected to a production trial. Functional trial results should be available to design and

11、 materials engineering prior to material approval and release. 3.5 SUPPLIERS RESPONSIBILITY All materials supplied to this specification must be equivalent in all characteristics to the material upon which approval was originally granted. Prior to making any change in the properties, composition, EN

12、GINEERING MATERIAL SPECIFICATION ESB-M11P31-A Page 3 of 3 construction, color, processing or labeling of the material originally approved under this specification, whether or not such changes affect the materials ability to meet the specification requirements, the Supplier shall notify Purchasing, T

13、oxicology and the affected Materials Engineering activity of the proposed changes and obtain the written approval of the Materials Engineering activity. Test data, test samples and a new code identification are to be submitted with the request. Substance restrictions imposed by law, regulations or F

14、ord, apply to the materials addressed by this document. The restrictions are defined in Engineering Material Specification WSS-M99P9999-A1, unless a different suffix (e.g., A2 or A3) is specified on the engineering document for the application. 4. APPROVAL OF MATERIALS Materials defined by this spec

15、ification must have prior approval by the responsible Materials Engineering activity. Suppliers desiring approval of their materials shall first obtain an expression of interest from the affected Purchasing, Design and Materials Engineering activity. Upon request, the Supplier shall submit to the af

16、fected Materials Engineering activity its own laboratory report to the specification (test results, not nominal values), the material designation and code number, and test specimens for Ford evaluation. Upon approval, the material will be added to the Engineering Material Approved Source List. 5. GE

17、NERAL INFORMATION The material data included herein is for information only and is not a requirement for the supplier. 5.1 SUBSTRATES 5.1.1 ESB-M2D348 RIM Urethane - 5.1 mm nominal thickness. 5.1.2 ESB-M4D284 Polyvinyl Chloride - 5.1 mm nominal thickness. 5.1.3 Glass Plate: Use current production plain and ESB-M99G109 ceramic coated glass as specified by the Body and Chassis Engineering Office - 4 mm nominal thickness. 5.2 ADHESIVE Use current production adhesive primer as recommended by the module window assembly supplier.