FORD ESB-M2D319-A-2006 POLYURETHANE FOAM ACOUSTICAL - 80 KG M3 TO BE USED WITH FORD WSS-M99P1111-A 《80 KG M3声学用聚氨酯泡沫 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 05 02 N-STATUS Replaced by WSS-M99P32-B A. Reaume 2004 09 23 Revised Para 3.0 inserted; para 3.1, 3.15, 3.16 & 4 deleted 1982 05 14 Released CEM1-CGM1-CR904248-2 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LL

2、C Page 1 of 3 POLYURETHANE FOAM, ACOUSTICAL - 80 kg/m3 ESB-M2D319-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a filled polyether urethane foam, with up to 25% (by weight) reground foam, cast to the desired configuration. 2. APPLICATION This specification wa

3、s released originally for material used in the upper cowl area of the 1983 Escort/Lynx molded dash absorber. The foam shall not be used in direct contact with metal temperatures exceeding 121 C. Metal contact temperatures or exposure temperatures that exceed 121 C shall employ sufficient insulation

4、to insure that the foam is exposed to less than 121 C. This material is not recommended for use in areas which are subjected to repeated load deflections. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. The test values listed herein are base

5、d on samples taken from parts. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COMPOSITION Reground Foam, max 25% by weight The reground foam shall consist of cu

6、ttings from 160 kg/m3foam approved to ESB-M2D297-A1 or ESB-M2D297-A2 and be uniformly distributed throughout the finished part. 3.3 CONSTRUCTION The cell structure of sheets and finished parts shall be free from large voids, unblown compound or hard spots. Samples of parts or sheets shall be equal t

7、o or better than samples on file at Materials and Corrosion Protection Engineering Department, Textile and Acoustic Engineering Section. 3.4 DENSITY 80 +/- 25% kg/m3(ASTM D 1564, with skin) 3.5 ASH CONTENT, max 4% (ASTM D 586) ENGINEERING MATERIAL SPECIFICATIONESB-M2D319-A Printed copies are uncontr

8、olled Copyright 2006, Ford Global Technologies, LLC Page 2 of 3 3.6 TENSILE STRENGTH, min 70 kPa (ASTM D 1564) 3.7 HEAT AGED TENSILE STRENGTH 60 kPa (ASTM D 1564, except age at 121 C +/- 2 C for 48 h), min 3.8 TEAR STRENGTH, min 6 N/cm (ASTM D 624, Die “C“) 3.9 COMPRESSION AND RECOVERY (FLTM BN 015-

9、02) Compression, max 70% Recovery, min 85% 3.10 MILDEW RESISTANCE - For Initial Qualification Only No visual evidence of mildew growth and no mildew odor after 7 days exposure in a humidity cabinet controlled to 100% relative humidity at 40 C. 3.11 AGED FLEXIBILITY No crumbling or embrittlement Test

10、 Method: A 51 x 152 x 12.7 mm specimen shall be subjected to the following cycling, then bent 180 around a 51 mm diameter mandrel: 7 h at 83 +/- 2 C in a mechanical convection oven followed by 16 h at -18 +/- 2 C in a cold chamber and flexing in cold chamber. 3.12 AGED WEIGHT LOSS, max 2.5% Test Met

11、hod: Weigh 100 x 100 x 25 mm sample to the nearest mg (W1). Place the sample in a convection oven maintained at 121 C +/- 2 C for 24 h. Remove the sample and reweigh to the nearest mg (W2). W1- W2% Weight Loss = - x 100 W13.13 FLAMMABILITY 3.13.1 In order to comply with Federal Motor Vehicle Safety

12、Standard No. 302, the materials, portions of components, and composites shall not burn, or transmit a flame across its surface, at a rate of more than 4 in (101 mm) per minute. To demonstrate compliance, the sample size and method of testing shall be in accordance with FLTM BN 024-02. ENGINEERING MA

13、TERIAL SPECIFICATIONESB-M2D319-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 3 of 3 3.13.2 Performance - Environmental Aging All materials, portions of components, and composites defined by this specification that have not been treated, modified or reformulated

14、 and exceed a maximum burn rate of 76 mm per minute as specified by the Flammability Lot Sampling Plan of FLTM BN 024-02, must be evaluated for permanency of the materials flame retardant properties per ESB-M25P3-A according to the accelerated environmental aging requirements applicable to the accel

15、erated environmental aging requirements applicable to the basic materials category of this particular specification. Any material, portions of components, and composites defined by this specification that have been treated, modified or reformulated to conform to Flammability Lot Sampling Plan of FLT

16、M BN 024-02, regardless of maximum burn rate, must be evaluated for both permanency of materials flame retardant properties and changes in mechanical, chemical and physical properties per ESB-M25P3-A applicable to the basic materials category of this particular specification. 3.13.3 Flammability Tes

17、t Program Materials, portions of components, and composites governed by this specification must also comply with the requirements of ES-D3AB-11014-AA. 3.14 ACOUSTICAL PERFORMANCE Suppliers approved to this specification must have their material functionally approved by the affected Car Product Development Group for acoustical performance. This approval must be obtained before Materials and Corrosion Protection Engineering Department approval will be given.