FORD ESB-M2G239-A-2014 ADHESIVE VINYL BASED - LOW AND HIGH TEMPERATURE CURE SEMI-STRUCTURAL TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2002 09 11 Revised Updated and renumbered 1980 05 02 Released AL1-6000-27 Printed copies are uncontrolled Page 1 of 3 Copyright 2002, Ford Global Technologies, Inc. ADHESIVE, VINYL BASED - LOW AND HIGH TEMPER

2、ATURE CURE, ESB-M2G239-A SEMI-STRUCTURAL 1. SCOPEThe material defined by this specification is a pumpable, one-component, heat curing modified vinylresin base, structural adhesive.2. APPLICATIONThis specification was released originally for material used for structural bonding of metal-to-metalbody

3、components such as the inner and outer panels (hem flange) of hoods, doors, etc. Thismaterial is oil tolerant and can be applied over oily steel and oily Zincrometal. Optimal adhesionstrengths are achieved at 0.008 - 0.010 in (0.20 - 0.25 mm) bondline thicknesses. Recommendedmaterial cure schedules

4、are 8 min at 135 C metal temperature minimum and 30 min at 205 C metal temperature maximum.3. REQUIREMENTS3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COLOR G

5、ray 3.3 VISCOSITY (FLTM BV 103-01, 0.104 in (2.64 mm) orifice, 80 psi (550 kPa) air pressure) 3.3.1 As Received 20 - 60 s 3.3.2 Aged, 72 h at 32 +/- 1 C, max 100 s 3.4 SOLIDS, min 99 % (ASTM D 2834, except heat at 102 +/- 3 C for 3 h in a mechanical convection oven) 3.5 WEIGHT PER VOLUME (ASTM D 816

6、) The weight tolerance for any one supplier shall be +/- 0.2 lb/gal (0.02 kg/L) based on the recorded weight of his original approved production sample. NOT TO BE USED FOR NEW DESIGN2014 12 08 N Status No replacement named L. Sinclair, NAENGINEERING MATERIAL SPECIFICATION ESB-M2G239-A Page 2 of 3 Co

7、pyright 2002, Ford Global Technologies, Inc. 3.6 SHEAR ADHESION STRENGTH (Cured platen press) (ASTM D 1002, 1/2 in (13 mm) length overlap, 0.008 - 0.010 in (0.20 - 0.25 mm) bondline thickness, 1 in (25 mm)/min pull rate, substrates per para 4.3, cure in platen press with 30 psi (0.21 MPa) max hydrau

8、lic pressure, material cure temperatures per para 4.4) 3.6.1 Normal (test at temperatures specified), min 3.6.1.1 23 +/- 2 C 400 psi (2.8 MPa) 3.6.1.2 82 +/- 3 C 60 psi (0.4 MPa) 3.6.1.3 -29 +/- 1 C 400 psi (2.8 MPa) 3.6.2 Aged (test at 23 +/- 2 C), min 400 psi (2.8 MPa) 3.6.2.1 2 weeks at 88 +/- 3

9、C 3.6.2.2 2 weeks at 38 +/- 1 C, 95 - 100% R. H. 3.6.2.3 2 weeks salt spray per ASTM B 117 3.7 COLD ADHESION No cracking or adhesion (FLTM BV 101-02, Procedure “E“, 0.020 in failure (0.51 mm) material thickness, substrates per para 4.3, material cure temperatures per para 4.4) 3.8 QUALITY The materi

10、al shall be a smooth homogeneous mixture, free from foreign materials and properties detrimental to normal production operations. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification 4.1 MECHANICAL CONVECTIO

11、N OVEN The mechanical oven(s) used to cure the material shall be capable of obtaining 205 C metal temperature on body steel (0.035 in (0.89 mm) within 8 - 10 min. 4.2 PLATEN PRESS A hydraulic press, Pasadena Hydraulics Inc., Model PWOS220, or equivalent, is required to compress and heat cure materia

12、ls to the proper material thickness. 4.3 SUBSTRATES 4.3.1 CRLC steel: 0.035 in (0.89 mm) thickness - surface precoated with M-99C47-A Mineral Oil at an application of approximately 0.2 cm3/ft2 (2.2 cm3/m2). ENGINEERING MATERIAL SPECIFICATION ESB-M2G239-A Page 3 of 3 Copyright 2002, Ford Global Techn

13、ologies, Inc. 4.3.2 Steel-sheet, zinc rich primer coated (ESB-M1A217): 0.035 in (0.89 mm) thickness surface precoated with M-99C47-A Mineral Oil at an application of approximately 0.2 cm3/ft2 (2.2 cm3/m2). 4.4 MATERIAL CURE SCHEDULES 4.4.1 Minimum: 135 C metal temperature for 8 min. 4.4.2 Maximum: 2

14、05 C metal temperature for 30 min. 4.5 STORAGE STABILITY The material shall be stored at temperatures below 27 C away from all sources of heat and sunlight. Heat greatly accelerates aging. Under these storage conditions, the minimum shelf life of the material shall be 3 months. When these materials

15、are stored at temperatures below 23 C, they shall be conditioned at room temperature prior to application. Adequate conditioning permits the material to obtain its optimum application properties. 4.6 WEIGHT PER VOLUME Materials conforming to this specification range from 10.5 - 12.5 lb/gal (1.25 -1.

16、49 kg/L). 4.7 TOXICITY Material may be expected to cause strong eye irritation and skin irritation on contact. Chemical goggles and impervious gloves should be worn when handling or mixing material. Material may also cause sensitization in some individuals exposed to high concentrations. The followi

17、ng precautions should appear on the label and be observed by all employes: Warning: Contains Epoxy Resins and Amine Hardner. May cause skin irritation. May cause allergic reaction. Avoid skin contact. In case of eye contact, flush eyes with water for 15 minutes and get immediate medical attention. For skin contact, wash immediately with mild soap and water. No special material labeling is required to comply with the Hazardous Materials Transportation Act.